Aromatic imide polymer laminate material and method for producing the same
Assignee: Ube Corp
•
Filing: 1982-04-20
•
Granted: 1983-10-25
•
Expires: 2002-04-20
Abstract
Abstract An aromatic imide polymer laminate material comprising at least one aromatic imide polymer film consisting essentially of at least one aromatic imide polymer which comprises at least 80 molar % of at least one type of recurring unit of the formula (I): <IMAGE> (I) wherein R represents a divalent aromatic radical; and at least one metallic foil which is superimposed on and directly bonded to said aromatic imide polymer film, which laminate material is produced by heat-pressing said aromatic imide polymer film superimposed on said metallic foil at 250 DEG to 600 DEG C. under a pressure of 1 to 2,000 kg/cm2 without applying a bonding agent between the polymer film and the metallic foil.
Inventors
- 👤 Yoshikazu Sasaki
- 👤 Hiroshi Inoue
- 👤 Tadashi Miura
- 👤 Kazuo Kumamoto
- 👤 Sumio Toudou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:12
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0346; B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B32B15/18; B32B15/20; B32B27/00; B32B27/28; B32B27/281; B32B2307/00; B32B2307/30; B32B2307/306; B32B2307/3065; B32B2379/00; B32B2379/08; B32B2457/00; B32B2457/08; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/266; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31721
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
121 words
An aromatic imide polymer laminate material comprising at least one aromatic imide polymer film consisting essentially of at least one aromatic imide polymer which comprises at least 80 molar % of at least one type of recurring unit of the formula (1): ##STR8## wherein R represents a divalent aromatic radical said polymer being characterized by a logarithmic viscosity of from 0.2 to 7 determined in a concentration of 0.5 g per 100 ml of p-chlorophenol at a temperature of 50° C., and a glass transition temperature of from 250° to 400° C.; and at least one metallic foil which is superimposed on and directly bonded to said aromatic imide polymer film without the presence of a bonding agent layer formed therebetween.
Claim 2
Dependent Claim
121 words
An aromatic imide polymer laminate material comprising at least one aromatic imide polymer film consisting essentially of at least one aromatic imide polymer which comprises at least 80 molar % of at least one type of recurring unit of the formula (1): ##STR8## wherein R represents a divalent aromatic radical said polymer being characterized by a logarithmic viscosity of from 0.2 to 7 determined in a concentration of 0.5 g per 100 ml of p-chlorophenol at a temperature of 50° C., and a glass transition temperature of from 250° to 400° C.; and at least one metallic foil which is superimposed on and directly bonded to said aromatic imide polymer film without the presence of a bonding agent layer formed therebetween.
Claim 3
Dependent Claim
27 words
The laminate material as claimed in claim 1, wherein the thickness of said aromatic imide polymer film is in the range of from 10 to 200 microns.
Claim 4
Dependent Claim
25 words
The laminate sheet as claimed in claim 1, wherein the thickness of said metallic foil is in the range of from 1 to 500 microns.
Claim 5
Dependent Claim
41 words
The laminate material as claimed in claim 1, wherein said metallic foil consists of a member selected from the group consisting of copper, tungsten, nickel, chromium, iron, silver, aluminium, lead, tin, and alloys containing one or more of the above-mentioned metals.
Claim 6
Dependent Claim
26 words
The laminate material as claimed in claim 1, which is composed of one aromatic imide polymer film and one metallic foil directly bonded to each other.
Claim 7
Dependent Claim
32 words
The laminate material as claimed in claim 1, which is composed of one aromatic imide polymer film and two metallic foils directly bonded to both surfaces of said aromatic imide polymer film.
Claim 8
Dependent Claim
56 words
The laminate material as claimed in claim 1, wherein said aromatic imide polymer exhibits a logarithmic viscosity of from 0.3 to 5, determined in a concentration of 0.5 g per 100 ml of a solvent consisting of p-chlorophenol at a temperature of 50° C., and a glass transition temperature of from 270° C. to 350° C.
Claim 9
Independent Claim
161 words
A method for producing an aromatic imide polymer laminate material comprising the steps of: superimposing at least one aromatic imide polymer film consisting essentially of at least one aromatic imide polymer which comprises at least 80 molar % of at least one type of recurring unit of the formula (1): ##STR9## wherein R represents a divalent aromatic radical said polymer being characterized by a logarithmic viscosity of from 0.2 to 7 determined in a concentration of 0.5 g per 100 ml of p-chlorophenol at a temperature of 50° C., and a glass transition temperature of from 250° to 400° C., and at least one metallic foil directly onto each other to provide a precursory laminate material; and heat-pressing said precursory laminate material at a temperature of from 250° to 600° C. under a pressure of from 1 to 2,000 kg/cm 2 to directly bond said aromatic imide polymer film and said metallic foil to each other without using a bonding agent.
Claim 10
Independent Claim
161 words
A method for producing an aromatic imide polymer laminate material comprising the steps of: superimposing at least one aromatic imide polymer film consisting essentially of at least one aromatic imide polymer which comprises at least 80 molar % of at least one type of recurring unit of the formula (1): ##STR9## wherein R represents a divalent aromatic radical said polymer being characterized by a logarithmic viscosity of from 0.2 to 7 determined in a concentration of 0.5 g per 100 ml of p-chlorophenol at a temperature of 50° C., and a glass transition temperature of from 250° to 400° C., and at least one metallic foil directly onto each other to provide a precursory laminate material; and heat-pressing said precursory laminate material at a temperature of from 250° to 600° C. under a pressure of from 1 to 2,000 kg/cm 2 to directly bond said aromatic imide polymer film and said metallic foil to each other without using a bonding agent.
Claim 11
Dependent Claim
36 words
The method as claimed in claim 8, wherein said heat-pressing procedure is carried out at a temperature which is higher than the glass transition temperature of said aromatic imide polymer but not higher than 550° C.
Claim 12
Dependent Claim
29 words
The method as claimed in claim 8, wherein said heat-pressing procedure is carried out in an inert gas atmosphere and/or under a reduced pressure of 50 mmHg or less.
Claim 13
Dependent Claim
35 words
The method as claimed in claim 8, wherein before said heat-pressing procedure is carried out, said aromatic imide polymer film and/or said metallic foil is preheated at a temperature of from 200° to 400° C.
Claim 14
Dependent Claim
55 words
The process as claimed in claim 8, wherein said aromatic imide polymer exhibits a logarithmic viscosity of from 0.3 to 5, determined in a concentration of 0.5 g per 100 mil of a solvent consisting of p-chlorophenol at a temperature of 50° C., and a glass transition temperature of from 270° C. to 350° C.
Claim 15
Dependent Claim
13 words
An aromatic imide polymer laminate material made by the method of claim 8.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-24 | 1987-04-25 | 1987-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-24 | 1991-04-25 | 1991-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-24 | 1995-04-25 | 1995-10-25 | $7700.00 | Window Closed / Lapsed |