Method for manufacturing aluminum alloy casting
Assignee: Mazda Motor Corp
•
Filing: 1982-02-09
•
Granted: 1983-10-25
•
Expires: 2002-02-09
Abstract
Abstract A method for the manufacture of an aluminum alloy casting comprises pouring a molten aluminum alloy into a mold having a sand core therein, removing a portion of the sands used to form the core from the casting after the solidification thereof, heating the casting and, simultaneously, removing the remaining portion of the sands from the casting, and machining the casting to complete an aluminum alloy article having an aperture or cavity or any other trace complemental to the core.
Inventors
- 👤 Teruo Nakanishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:08
CPC Classifications
B; B22; B22D; B22D21/00; B22D21/002; B22D21/007; B22D29/00; B22D29/001; B22D29/003; B22D31/00; B22D31/002
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
169 words
A method for manufacturing a casting of aluminum alloy by the use of a mold having therein a destructible core made of sands and a resin binder, said casting having defined therein at least one cavity complemental in shape to the core, which method comprises the steps of: pouring a molten aluminum alloy into the mold to form a casting therein; removing the casting from the mold together with the core after it has been solidified; destroying the core in the casting to such as to permit the removal of a portion of the sand used to form the core from the casting; heating the casting to burn out and weaken the bonding capability of the resin component contained in the remaining sand located inside the casting so as to facilitate a complete removal of the sand therefrom, said casting being during the heating step, simultaneously subjected to a solid solution treatment and quenching treatment of the casting; rapidly cooling the casting to quench it; and drying said casting.
Claim 2
Independent Claim
169 words
A method for manufacturing a casting of aluminum alloy by the use of a mold having therein a destructible core made of sands and a resin binder, said casting having defined therein at least one cavity complemental in shape to the core, which method comprises the steps of: pouring a molten aluminum alloy into the mold to form a casting therein; removing the casting from the mold together with the core after it has been solidified; destroying the core in the casting to such as to permit the removal of a portion of the sand used to form the core from the casting; heating the casting to burn out and weaken the bonding capability of the resin component contained in the remaining sand located inside the casting so as to facilitate a complete removal of the sand therefrom, said casting being during the heating step, simultaneously subjected to a solid solution treatment and quenching treatment of the casting; rapidly cooling the casting to quench it; and drying said casting.
Claim 3
Dependent Claim
16 words
A method as claimed in claim 1, wherein the resin binder is a urea resin binder.
Claim 4
Dependent Claim
24 words
A method as claimed in claim 1, wherein the pouring step is carried out by the use of a low pressure die casting technique.
Claim 5
Dependent Claim
26 words
A method as claimed in claim 1, wherein the heating is carried out at 485° C. for 4 hours and then quenched in a water bath.
Claim 6
Dependent Claim
23 words
A method as claimed in claim 1, 2, 3 or 4, wherein the casting is a cylinder head for an internal combustion engine.
Claim 7
Dependent Claim
35 words
A method as claimed in claim 1, wherein said removing step includes the separation of the casting from a gate of the mold through which the molten aluminum alloy has been poured into the mold.
Claim 8
Dependent Claim
30 words
A method as claimed in claim 1, which further comprises the step of removing any cast fins formed during the casting step from the casting subsequent to the drying step.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-24 | 1987-04-25 | 1987-10-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-24 | 1991-04-25 | 1991-10-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-24 | 1995-04-25 | 1995-10-25 | $7700.00 | Window Closed / Lapsed |