Catalyst and process
Assignee: Phillips Petroleum Co
•
Filing: 1981-12-09
•
Granted: 1983-10-18
•
Expires: 2001-12-09
Abstract
Abstract A high surface area catalyst component or support is produced by swelling a magnesium halide, e.g., MgCl 2 , with a secondary or tertiary alcohol, adding a hydrocarbon diluent, and removing some or substantially all of the free or unreacted alcohol. In one preferred embodiment, the alcoholate product is contacted with a halogenated tetravalent titanium compound, e.g., TiCl 4 , to form a first catalyst component (A) which can be combined with a cocatalyst component (B) comprising a metallic hydride or an organometallic compound, e.g., an organoaluminum compound to form a catalyst system active for olefin polymerization.
Inventors
- 👤 Richard E. Dietz
- 👤 Melvin B. Welch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:55
CPC Classifications
C; C08; C08F; C08F10/00; Y; Y10; Y10S; Y10S526/00; Y10S526/904
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
147 words
A catalyst characterized by the product obtained by (a) reacting finely divided particulate MgX 2 where X is Br, Cl or I with an excess of a secondary or tertiary alcohol under conditions which cause swelling of the particulate magnesium dihalide and forms an alcoholate of increased surface area and a final surface area ranging from about 75 to 150 m 2 /g, (b) removing excess or unreacted alcohol from the product formed in (a) under conditions sufficient to reduce the alcohol present to less than 2 moles per mole magnesium dihalide, (c) contacting the finely divided alcoholate product substantially freed of unreacted alcohol obtained in (b) with a tetravalent halogenated titanium compound to form a catalyst component (A), and (d) a cocatalyst component B comprising a metallic hydride or organometallic compound wherein said metal is selected from Groups IA, IIA, and IIIA of the Periodic Table.
Claim 2
Dependent Claim
147 words
A catalyst characterized by the product obtained by (a) reacting finely divided particulate MgX 2 where X is Br, Cl or I with an excess of a secondary or tertiary alcohol under conditions which cause swelling of the particulate magnesium dihalide and forms an alcoholate of increased surface area and a final surface area ranging from about 75 to 150 m 2 /g, (b) removing excess or unreacted alcohol from the product formed in (a) under conditions sufficient to reduce the alcohol present to less than 2 moles per mole magnesium dihalide, (c) contacting the finely divided alcoholate product substantially freed of unreacted alcohol obtained in (b) with a tetravalent halogenated titanium compound to form a catalyst component (A), and (d) a cocatalyst component B comprising a metallic hydride or organometallic compound wherein said metal is selected from Groups IA, IIA, and IIIA of the Periodic Table.
Claim 3
Dependent Claim
40 words
A catalyst according to claim 1 wherein the magnesium dihalide is magnesium dichloride, the alcohol has the formula ROH wherein R is an alkyl group containing from 3 to about 10 carbon atoms, and the titanium compound is titanium tetrachloride.
Claim 4
Dependent Claim
13 words
A catalyst according to claim 2 wherein the cocatalyst is a trihydrocarbylaluminum compound.
Claim 5
Dependent Claim
14 words
A catalyst according to claim 3 wherein the trihydrocarbylaluminum compound is triethylaluminum or triisobutylaluminum.
Claim 6
Dependent Claim
13 words
A catalyst according to claim 2 wherein the alcohol is 2-propanol or tert-butanol.
Claim 7
Dependent Claim
69 words
A catalyst according to claim 1 wherein (a) is carried out in the presence of a hydrocarbon diluent with a mole ratio of hydrocarbon to alcohol ranging from about 25:1 to about 0.02:1 and with the moles of alcohol to magnesium dihalide employed ranging from about 2:1 to about 50:1 and further wherein the product of (a) has a surface area of at least about 75 m 2 /g.
Claim 8
Dependent Claim
18 words
A catalyst according to claim 1 wherein the magnesium dihalide is milled prior to reacting with the alcohol.
Claim 9
Dependent Claim
13 words
A catalyst according to claim 2 which additionally contains a particulate solid diluent.
Claim 10
Dependent Claim
75 words
A catalyst according to claim 1 obtained by (a) reacting MgCl 2 with isopropanol or tert-butanol in a hydrocarbon diluent, (b) distilling some or substantially all of the excess or unreacted alcohol from the product formed in (a) to leave a slurry of particulate magnesium dichloride alcoholate in the hydrocarbon, (c) contacting the slurry product of (b) with a hydrocarbon solution of TiCl 4 , and (d) combining the product formed in (c) with triethylaluminum.
Claim 11
Independent Claim
170 words
A method of preparing a catalyst comprising (a) swelling a MgX 2 wherein X is Br, Cl or I with an excess of a secondary or tertiary alcohol in a hydrocarbon diluent under conditions which cause swelling of the particulate magnesium chloride and produces an alcoholate of increased surface area and a final surface area ranging from about 75 to 150 m 2 /g, (b) removing excess or unreacted alcohol from the alcoholate thus produced under conditions sufficient to reduce the alcohol present to less than 2 moles per mole magnesium dihalide and leave a slurry of particulate magnesium dihalide alcoholate in the hydrocarbon diluent, (c) contacting the alcoholate substantially freed of alcohol remaining in (c) with a tetravalent halogenated titanium compound, (d) washing the product obtained in (c) with an inert solvent to remove unreacted titanium compound, and (e) combining a cocatalyst component comprising a metallic hydride or organometallic compound wherein said metal is selected from Groups IA, IIA and IIIA of the Periodic Table with product of (d).
Claim 12
Independent Claim
170 words
A method of preparing a catalyst comprising (a) swelling a MgX 2 wherein X is Br, Cl or I with an excess of a secondary or tertiary alcohol in a hydrocarbon diluent under conditions which cause swelling of the particulate magnesium chloride and produces an alcoholate of increased surface area and a final surface area ranging from about 75 to 150 m 2 /g, (b) removing excess or unreacted alcohol from the alcoholate thus produced under conditions sufficient to reduce the alcohol present to less than 2 moles per mole magnesium dihalide and leave a slurry of particulate magnesium dihalide alcoholate in the hydrocarbon diluent, (c) contacting the alcoholate substantially freed of alcohol remaining in (c) with a tetravalent halogenated titanium compound, (d) washing the product obtained in (c) with an inert solvent to remove unreacted titanium compound, and (e) combining a cocatalyst component comprising a metallic hydride or organometallic compound wherein said metal is selected from Groups IA, IIA and IIIA of the Periodic Table with product of (d).
Claim 13
Dependent Claim
73 words
A method according to claim 10 wherein step (a) is carried out with a mole ratio of hydrocarbon to alcohol in the range of about 25:1 to about 0.02:1 and at a temperature ranging from about room temperature (20° C.) to the reflux temperature, the excess alcohol in (b) is removed by fractional distillation and the contacting in (c) is carried out by refluxing with said titanium compound in an inert hydrocarbon solvent.
Claim 14
Dependent Claim
52 words
A method according to claim 10 wherein step (a) is carried out by reacting MgCl 2 with isopropanol or tert-butanol in a hydrocarbon diluent, said alcoholate in (c) is contacted with TiCl 4 in the presence of a hydrocarbon diluent, and the washing in (d) is carried out with a hydrocarbon diluent.
Claim 15
Dependent Claim
19 words
A catalyst prepared according to claim 10 wherein the washed product in (c) is combined with a solid diluent.
Claim 16
Dependent Claim
34 words
A catalyst prepared according to claim 10 wherein the magnesium halide is MgCl 2 , said alcohol is isopropanol or tert-butanol, said titanium compound is TiCl 4 , and said cocatalyst is trialkylaluminum compound.
Claim 17
Dependent Claim
13 words
A catalyst prepared according to claim 14 wherein said trialkylaluminum compound is triethylaluminum.
References Cited (Backward Citations)
US3129256A
Cited
US3642746A
Cited
US3644318A
Cited
US3789036A
Cited
US4156063A
Cited
US4013823A
Cited
US3953414A
Cited
US3859231A
Cited
US4006101A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-17 | 1987-04-18 | 1987-10-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-17 | 1991-04-18 | 1991-10-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-17 | 1995-04-18 | 1995-10-18 | $7700.00 | Window Closed / Lapsed |