Process for the manufacture of a mixture of polycarbonates and styrene-containing polymers, use of the mixture and molded parts thereof
Assignee: BASF SE
•
Filing: 1982-02-18
•
Granted: 1983-10-11
•
Expires: 2002-02-18
Abstract
Abstract The invention relates to a process for the manufacture of a mixture of a polycarbonate and a styrene-containing polymer whereby the polycarbonate present in solution is initially brought into contact with a precipitating agent. The solvent and the precipitating agent are subsequently separated from the precipitated solid material to prepare a polycarbonate having residual moisture of more than 1 and less than 50 percent by weight relative to the polycarbonate, and where the resultant product with a residual moisture is mixed with the styrene-containing polymer at temperatures above the softening range of the components removing volatile components. The claimed mixtures are suitable for the manufacture of molded parts for cars, bottles and appliances.
Inventors
- 👤 Franz Brandstetter
- 👤 Franz Haaf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:09
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/005; C08L; C08L69/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
121 words
A process for the manufacture of a mixture of a polycarbonate and a styrene containing polymer comprises (a) contacting a dissolved polycarbonate with a precipitating agent and subsequently removing the solvent and the precipitating agent from the precipitated solid material to prepare a polycarbonate having a residual moisture, and (b) mixing the polycarbonate having the residual moisture and styrene-containing polymer melt at a temperature above the softening range of the polycarbonate and styrene-containing polymer wherein the polycarbonate having the residual moisture contains more than 1 and less than 50 percent by weight residual moisture, relative to the weight of polycarbonate, and wherein the mixing of the polycarbonate having the residual moisture and the styrene-containing polymer is accomplished while removing volatile ingredients.
Claim 2
Dependent Claim
121 words
A process for the manufacture of a mixture of a polycarbonate and a styrene containing polymer comprises (a) contacting a dissolved polycarbonate with a precipitating agent and subsequently removing the solvent and the precipitating agent from the precipitated solid material to prepare a polycarbonate having a residual moisture, and (b) mixing the polycarbonate having the residual moisture and styrene-containing polymer melt at a temperature above the softening range of the polycarbonate and styrene-containing polymer wherein the polycarbonate having the residual moisture contains more than 1 and less than 50 percent by weight residual moisture, relative to the weight of polycarbonate, and wherein the mixing of the polycarbonate having the residual moisture and the styrene-containing polymer is accomplished while removing volatile ingredients.
Claim 3
Dependent Claim
30 words
The process of claim 1 wherein the residual moisture of the polycarbonate is between 15 percent by weight and 40 percent by weight, relative to the weight of the polycarbonate.
Claim 4
Dependent Claim
61 words
The process of claim 1 wherein the styrene-containing polymer is an acrylonitrile-butadiene-styrene copolymer having a polybutadiene content of 25 percent by weight and a rigid component of 55 percent by weight having a ratio of styrene/acrylonitrile of 5/65 and a viscosity number of 55 milliliters/gram, having an average particle size d 50 value of the flexible component of approximately 0.35 microns.
Claim 5
Dependent Claim
116 words
The process of claim 1 wherein the styrene-containing polymer is an acrylonitrile-butadiene-styrene copolymer having a polybutadiene content of 25 percent by weight and a rigid component of 55 percent by weight wherein the rigid commponent consists of a mixture of about 50 percent by weight of a copolymer of α-methylstyrene/acrylonitrile having an acrylonitrile content of 30 percent by weight relative to the copolymer, having a viscosity number of 50 milliliters/gram and about 50 percent by weight of a copolymer of styrene/acrylonitrile having an acrylonitrile content of 35 percent by weight relative to the copolymer and a viscosity number of 67 milliliters/gram, having an average particle size d 50 of the flexible component of approximately 0.35 microns.
Claim 6
Dependent Claim
80 words
The process of claim 1 wherein the styrene-containing polymer is an acrylic ester-modified styrene-acrylonitrile terpolymer with a rubber content of 25 percent by weight with the rubber having been produced by emulsion polymerization of butylacrylate in the presence of 2 percent by weight of the acrylate of tricyclodecenyl alcohol with a rigid component of 50 percent by weight, with a rigid component representing a copolymer, which contains 35 percent by weight of acrylonitrile and has a viscosity number of 70.
Claim 7
Dependent Claim
30 words
The process of claim 1 wherein the styrene-containing polymer is a polystyrene having an average particle size of the flexible component of 2 to 3 microns and produced in solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |