Abstract
Abstract A novel polymer is provided as the condensation reaction product of a non-aqueous mixture of a phenol and an aldehyde in a molar ratio of about 0.5 to 1 phenol to aldehyde, containing refractory fibers, such as carbon, graphite, silica, having an aspect and metal oxides and silicates, which fibers have an aspect ratio of about 10. The phenol is selected from metacresol, orthocresol, 3,5-dimethylphenol, resorcinol and substituted resorcinols, the preferred material being mostly resorcinol. The aldehyde is selected from furfural and mixtures of furfural and paraformaldehyde. The condensation polymerization reaction can be effected by adding an acid catalyst to the mixture or by employing a curing agent which provided a polyfunctional amine reactive with either or both the aldehyde and the phenol.
Inventors
- 👤 Lawrence E. McAllister
- 👤 Herbert Dietrich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 05:43
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; C08J9/14; C08J9/143; C08G; C08G8/00; C08G8/04; C08G8/06; C08G8/08; C08G8/20; C08G8/22; C08G8/24; C08J2361/00; C08J2361/04; C08J2361/06
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
116 words
Method of forming a flame retardant polymer resin, said method comprising the steps of: mixing an initially non-aqueous substantially unreacted solution of a phenol in a liquid aldehyde in molar ratio of about 0.5 to 1 phenol to aldehyde, said phenol being selected from the group consisting of metacresol, orthocresol, 3,5-dimethylphenol, resorcinol and substituted resorcinols, said aldehyde being selected from the group consisting of furfural and mixtures of furfural and paraformaldehyde; effecting condensation polymerization of said solution into said resin; and adding to said solution prior to polymerization, refractory fibers having an aspect ratio of greater than about 10, said fibers being selected from the group consisting of carbon, graphite, silica and metal oxides and silicates.
Claim 2
Dependent Claim
116 words
Method of forming a flame retardant polymer resin, said method comprising the steps of: mixing an initially non-aqueous substantially unreacted solution of a phenol in a liquid aldehyde in molar ratio of about 0.5 to 1 phenol to aldehyde, said phenol being selected from the group consisting of metacresol, orthocresol, 3,5-dimethylphenol, resorcinol and substituted resorcinols, said aldehyde being selected from the group consisting of furfural and mixtures of furfural and paraformaldehyde; effecting condensation polymerization of said solution into said resin; and adding to said solution prior to polymerization, refractory fibers having an aspect ratio of greater than about 10, said fibers being selected from the group consisting of carbon, graphite, silica and metal oxides and silicates.
Claim 3
Dependent Claim
48 words
Method of forming a resin according to claim 1 wherein furfural alcohol is substituted on the basis of one mole of said furfuryl alcohol being chemically equivalent to one mole of said phenol and one mole of said aldehydes, up to 50% by weight of the final product.
Claim 4
Dependent Claim
28 words
Method of forming a resin according to claim 1 wherein said condensation polymerization is effected by addition of an acid catalyst in sufficient amount to produce said polymerization.
Claim 5
Dependent Claim
30 words
Method of forming a resin according to claim 1 wherein said condensation polymerization is effected by addition of a polyfunctional amine curing agent in sufficient amount to produce said polymerization.
Claim 6
Dependent Claim
44 words
Method of forming a resin according to claim 1 wherein said condensation polymerization is effected by the addition of said solution of heat and a latent amine complex curing agent which undergoes thermal decomposition to release a polyfunctional amine upon addition of said heat.
Claim 7
Dependent Claim
32 words
Method of forming a resin according to claim 4 wherein said acid catalyst is selected from the group consisting of phosphoric acid, phosphorous acid, sulfuric acid, hydrochloric acid and organic acid phosphates.
Claim 8
Dependent Claim
21 words
Method of forming a resin according to claim 4 wherein said curing agent is selected from both aliphatic and aromatic amines.
Claim 9
Dependent Claim
18 words
Method of forming a resin according to claim 5 wherein said latent curing agent is an amine complex.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |