Hydrophilic sulfonated polyolefin porous membrane and process for preparing the same
Assignee: Asahi Kasei Corp
•
Filing: 1980-10-06
•
Granted: 1983-10-11
•
Expires: 2000-10-06
Abstract
Abstract A sulfonated polyolefin porous membrane containing sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin and having a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ has been found to be excellent in water permeability, removal capability, water-permeability retention, mechanical strength and elongation, etc. The porous membrane of the present invention may advantageously be employed as a fine microfilter or the like. The porous membrane of the present invention may be easily prepared by treating with a sulfonating agent a polyolefin porous membrane preferably containing an inorganic filler which is subsequently extracted from the membrane.
Inventors
- 👤 Kazuo Matsuda
- 👤 Mitsuo Kohno
- 👤 Yoshinao Doi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:34
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0093; B01D69/00; B01D69/02; B01D69/08; B01D71/00; B01D71/06; B01D71/26
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
86 words
A water permeable porous membrane which consists essentially of a sulfonated polyolefin selected from the group consisting of sulfonated polyethylene, sulfonated polypropylene, sulfonated polybutene and mixtures thereof and sulfonated copolymers of two or more kinds of monomers selected from ethylene, propylene, butene, hexene and tetrafluoroethylene, said polyolefin contains sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin and has a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ.
Claim 2
Dependent Claim
86 words
A water permeable porous membrane which consists essentially of a sulfonated polyolefin selected from the group consisting of sulfonated polyethylene, sulfonated polypropylene, sulfonated polybutene and mixtures thereof and sulfonated copolymers of two or more kinds of monomers selected from ethylene, propylene, butene, hexene and tetrafluoroethylene, said polyolefin contains sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin and has a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ.
Claim 3
Dependent Claim
30 words
A porous membrane as claimed in claim 1, wherein said sulfonic groups are present substantially only in the outer surfaces of the membrane and the inner surfaces surrounding the pores.
Claim 4
Dependent Claim
135 words
A process for preparing a water permeable porous membrane having a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ, which comprises treating, with a sulfonating agent selected from the group consisting of fuming sulfuric acid, chlorosulfonic acid, 100% sulfuric acid and solutions of sulfur trioxide dissolved in a suitable solvent a porous membrane consisting essentially of an inorganic filler and a polyolefin selected from the group consisting of polyethylene, polypropylene, polybutene and mixtures thereof and copolymers of two or more kinds of monomers selected from ethylene, propylene, butene, hexene and tetrafluoroethylene, the treatment being carried out so that the resulting sulfonated polyolefin contains sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin, and extracting the inorganic filler.
Claim 5
Dependent Claim
135 words
A process for preparing a water permeable porous membrane having a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ, which comprises treating, with a sulfonating agent selected from the group consisting of fuming sulfuric acid, chlorosulfonic acid, 100% sulfuric acid and solutions of sulfur trioxide dissolved in a suitable solvent a porous membrane consisting essentially of an inorganic filler and a polyolefin selected from the group consisting of polyethylene, polypropylene, polybutene and mixtures thereof and copolymers of two or more kinds of monomers selected from ethylene, propylene, butene, hexene and tetrafluoroethylene, the treatment being carried out so that the resulting sulfonated polyolefin contains sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin, and extracting the inorganic filler.
Claim 6
Dependent Claim
126 words
A process for preparing a water permeable porous membrane having a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ, which comprises treating, with a sulfonating agent selected from the group consisting of fuming sulfuric acid, chlorosulfonic acid 100% sulfuric acid and solutions of sulfur trioxide dissolved in a suitable solvent, a porous membrane consisting essentially of a polyolefin selected from the group consisting of polyethylene, polypropylene, polybutene and mixtures thereof and copolymers of two or more kinds of monomers selected from ethylene, propylene, butene, hexene and tetrafluoroethylene, the treatment being carried out so that the resulting sulfonated polyolefin contains sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin.
Claim 7
Dependent Claim
126 words
A process for preparing a water permeable porous membrane having a porosity of 30 to 85% and an average pore diameter of 0.05 to 1μ, which comprises treating, with a sulfonating agent selected from the group consisting of fuming sulfuric acid, chlorosulfonic acid 100% sulfuric acid and solutions of sulfur trioxide dissolved in a suitable solvent, a porous membrane consisting essentially of a polyolefin selected from the group consisting of polyethylene, polypropylene, polybutene and mixtures thereof and copolymers of two or more kinds of monomers selected from ethylene, propylene, butene, hexene and tetrafluoroethylene, the treatment being carried out so that the resulting sulfonated polyolefin contains sulfonic groups in an amount, in terms of exchange capacity, of 0.05 to 1 milliequivalent per gram of the sulfonated polyolefin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |