Abstract
Abstract A solar cell is provided which utilizes a semicrystalline semiconductor starting material. The solar cell has a metallic layer deposited over the grain boundaries between adjacent active grain areas of the material to collect the current generated in the grain areas. The metallic layer also shields the grain boundaries from illumination, thereby passivating the boundaries.
Inventors
- 👤 Sanjeev R. Chitre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:40
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/10; H10F77/16; H10F77/162; H10F77/164; H10F77/1642; H10F77/20; H10F77/206; H10F77/211; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/546; Y10; Y10S; Y10S205/00; Y10S205/923
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
99 words
A solar cell comprising: a semicrystalline structure having a plurality of grain areas of differing crystalline orientation and grain boundaries separating the differing grain areas; a p-n junction formed in the semicrystalline structure; and a conductive metallic region formed at the grain boundaries (a) for collecting generated carriers from the structure before the carriers recombine at the grain boundaries, and (b) for shielding the grain boundaries from light thereby to further passivate the grain boundaries, said metallic region being formed by anodic etching at the grain boundaries and cathodic displacement of atoms at the grain boundaries with metallic atoms.
Claim 2
Dependent Claim
99 words
A solar cell comprising: a semicrystalline structure having a plurality of grain areas of differing crystalline orientation and grain boundaries separating the differing grain areas; a p-n junction formed in the semicrystalline structure; and a conductive metallic region formed at the grain boundaries (a) for collecting generated carriers from the structure before the carriers recombine at the grain boundaries, and (b) for shielding the grain boundaries from light thereby to further passivate the grain boundaries, said metallic region being formed by anodic etching at the grain boundaries and cathodic displacement of atoms at the grain boundaries with metallic atoms.
Claim 3
Dependent Claim
25 words
The cell of claim 2 wherein the metallic region is formed by treating the grain boundaries with a solution of copper nitrate and ammonium fluoride.
Claim 4
Dependent Claim
26 words
The cell of claim 1 wherein there is deposited on said metallic region a relatively thicker metal layer to form a lower resistance current conducting path.
Claim 5
Dependent Claim
17 words
The cell of claim 3 wherein said relatively thicker metallic layer is electrodeposited on the metallic region.
Claim 6
Dependent Claim
15 words
The cell of claim 1 wherein said anodic etching is an anisotropic anodic etching process.
Claim 7
Dependent Claim
30 words
The cell of claim 5 wherein said anodic etching process is carried out with a solution of a suitably low reduction potential metal ion and a crystalline element removing anion.
Claim 8
Dependent Claim
113 words
A solar cell comprising: a semicrystalline structure having a plurality of grain areas of differing crystalline orientation and grain boundaries separating the differing grain areas; a p-n junction formed in the semicrystalline structure; and a conductive metallic region formed at the grain boundaries (a) for collecting generated carriers from the structure before the carriers recombine in the grain boundaries, and (b) for shielding the grain boundaries from light thereby to further passivate the grain boundaries; and a plurality of conductive pads distributed over the surface of the structure and electrically connected to the metallic region at the grain boundaries, and a bus electrically interconnecting the plurality of pads to collect the generated current.
Claim 9
Dependent Claim
113 words
A solar cell comprising: a semicrystalline structure having a plurality of grain areas of differing crystalline orientation and grain boundaries separating the differing grain areas; a p-n junction formed in the semicrystalline structure; and a conductive metallic region formed at the grain boundaries (a) for collecting generated carriers from the structure before the carriers recombine in the grain boundaries, and (b) for shielding the grain boundaries from light thereby to further passivate the grain boundaries; and a plurality of conductive pads distributed over the surface of the structure and electrically connected to the metallic region at the grain boundaries, and a bus electrically interconnecting the plurality of pads to collect the generated current.
Claim 10
Dependent Claim
54 words
The cell of claims 1 or 7 which further comprises a relatively thicker metallic layer deposited on said metal region to further facilitate collection of carriers before the carriers recombine in the boundaries and to further shield the boundaries and prevent the illumination of the boundaries thereby to further inhibit recombination in the boundaries.
Claim 11
Independent Claim
98 words
A method of fabricating a solar cell utilizing a semicrystalline starting material having a plurality of grain areas of differing crystalline orientation separated by grain boundaries, said method comprising the steps of: doping the starting material with impurities to thereby form a p-n junction in the material; and providing a metallic region along the grain boundaries of the starting material to provide a conduction network to collect the generated current by anisotropic anodic etching at the grain boundaries and cathodic displacement of atoms at the the grain boundaries with metallic atoms, thereby also reducing recombination in the boundaries.
Claim 12
Independent Claim
98 words
A method of fabricating a solar cell utilizing a semicrystalline starting material having a plurality of grain areas of differing crystalline orientation separated by grain boundaries, said method comprising the steps of: doping the starting material with impurities to thereby form a p-n junction in the material; and providing a metallic region along the grain boundaries of the starting material to provide a conduction network to collect the generated current by anisotropic anodic etching at the grain boundaries and cathodic displacement of atoms at the the grain boundaries with metallic atoms, thereby also reducing recombination in the boundaries.
Claim 13
Dependent Claim
27 words
The method of claim 9 wherein the anodic etching and cathodic displacing steps comprise immersing the material in an aqueous solution of copper nitrate and ammonium fluoride.
Claim 14
Dependent Claim
51 words
The method of claim 9 wherein a relatively thicker metallic layer is deposited on said metallic region to further facilitate collection of carriers before the carriers recombine in the boundaries and to further shield the boundaries and prevent the illumination of the boundaries thereby to further inhibit recombination in the boundaries.
Claim 15
Dependent Claim
11 words
The method of claim 11 further comprising sintering the metallic layer.
Claim 16
Dependent Claim
28 words
The method of claim 11 further comprising placing conductive pads on the metallic layer and interconnecting the pads with a bus to facilitate the collection of generated current.
Claim 17
Dependent Claim
48 words
The method of claim 11 further comprising applying a transparent protective coating onto the light receiving surface of the material, screening conductive pads onto the protective coating; sintering the pads through the coating to make electrical contact with the metallic layer; and interconnecting the pads with a bus.
Claim 18
Dependent Claim
32 words
The method of claim 9 wherein said anisotropic etching and replacement process is carried out with a solution of a suitably low reduction potential metal ion and a crystalline element removing anion.
Claim 19
Dependent Claim
14 words
The method of claim 15 wherein said solution comprises copper nitrate and ammonium fluoride.
Claim 20
Dependent Claim
16 words
The method of claim 15 or 16 wherein said semicrystalline structure is a silicon semicrystalline structure.
Claim 21
Dependent Claim
171 words
A solar cell comprising: a wafer of semicrystalline silicon having a plurality of grain areas of differing crystalline orientation and etched grain boundaries separating the differing grain areas; a p-n junction diffused into the silicon wafer; a region of metal in the etched boundaries which has displaced silicon atoms in the boundaries to form a metallization pattern following the grain boundaries; and a thicker layer of metal deposited over the metallic region to form a metallization pattern following the grain boundaries to (a) collect generated carriers from the grain areas before the carriers recombine in the boundaries and (b) to shield the boundaries from illumination thereby to further inhibit carrier recombination in the boundaries; a light transparent layer forming a protective coating over the light-receiving side of the wafer; a plurality of conductive pads disposed on the coating and sintered through the coating making electrical contact with the layer of deposited metal; and a bus interconnecting the pads to conduct the current of carriers collected by the metallic region and layer.
Claim 22
Dependent Claim
171 words
A solar cell comprising: a wafer of semicrystalline silicon having a plurality of grain areas of differing crystalline orientation and etched grain boundaries separating the differing grain areas; a p-n junction diffused into the silicon wafer; a region of metal in the etched boundaries which has displaced silicon atoms in the boundaries to form a metallization pattern following the grain boundaries; and a thicker layer of metal deposited over the metallic region to form a metallization pattern following the grain boundaries to (a) collect generated carriers from the grain areas before the carriers recombine in the boundaries and (b) to shield the boundaries from illumination thereby to further inhibit carrier recombination in the boundaries; a light transparent layer forming a protective coating over the light-receiving side of the wafer; a plurality of conductive pads disposed on the coating and sintered through the coating making electrical contact with the layer of deposited metal; and a bus interconnecting the pads to conduct the current of carriers collected by the metallic region and layer.
Claim 23
Independent Claim
201 words
A method of fabricating a solar cell utilizing a wafer of semicrystalline silicon having a plurality of grain areas of differing crystalline orientation separated by grain boundaries, said method comprising the steps of; etching the wafer with sodium hydroxide to remove any damage from the wafer; doping the wafer with POCl 3 on one side of the wafer and with aluminum on the other side to diffuse a p-n junction into the wafer; immersing the wafer in an aqueous solution of copper nitrate and ammonium fluoride to anisotropically etch and displace atoms of each boundary to form a first layer of copper in the grain boundaries; electroplating a second layer of metal onto the first layer of copper to cover the grain boundaries to provide a current collection network around the periphery of each of the grain areas and to shield the grain boundaries from illumination; depositing a coating of silicon nitride on the wafer to protect the wafer and metallic layers; screening conductive pads onto the silicon nitride coating; sintering the pads through the coating to make electrical contact with the metallic layer covering the grain boundaries; and interconnecting the pads with a bus wire to collect the generated current.
Claim 24
Independent Claim
201 words
A method of fabricating a solar cell utilizing a wafer of semicrystalline silicon having a plurality of grain areas of differing crystalline orientation separated by grain boundaries, said method comprising the steps of; etching the wafer with sodium hydroxide to remove any damage from the wafer; doping the wafer with POCl 3 on one side of the wafer and with aluminum on the other side to diffuse a p-n junction into the wafer; immersing the wafer in an aqueous solution of copper nitrate and ammonium fluoride to anisotropically etch and displace atoms of each boundary to form a first layer of copper in the grain boundaries; electroplating a second layer of metal onto the first layer of copper to cover the grain boundaries to provide a current collection network around the periphery of each of the grain areas and to shield the grain boundaries from illumination; depositing a coating of silicon nitride on the wafer to protect the wafer and metallic layers; screening conductive pads onto the silicon nitride coating; sintering the pads through the coating to make electrical contact with the metallic layer covering the grain boundaries; and interconnecting the pads with a bus wire to collect the generated current.
Claim 25
Independent Claim
63 words
A method of fabricating a solar cell utilizing semicrystalline starting material having a plurality of grain areas of differing crystalline orientation separated by grain boundaries, said method comprising the steps of: doping the starting material with impurities to thereby form p-n junctions in the grain areas; preferentially etching the starting material at the grain boundaries and selectively providing metal at the etched areas.
Claim 26
Independent Claim
63 words
A method of fabricating a solar cell utilizing semicrystalline starting material having a plurality of grain areas of differing crystalline orientation separated by grain boundaries, said method comprising the steps of: doping the starting material with impurities to thereby form p-n junctions in the grain areas; preferentially etching the starting material at the grain boundaries and selectively providing metal at the etched areas.
Claim 27
Independent Claim
86 words
A method of fabricating a photovoltaic solar panel comprising: providing an extensive layer of polycrystalline semiconductor material, the grains in said material having one statistically predominant orientation, forming p-n junctions within a substantial proportion of the grains of said layer material, etching said polycrystalline layer with an etchant that preferentially etches the grain orientations facing the grain boundaries of said layer, and selectively providing metallization over said preferentially etched boundaries, said metallization acting as a conductor for current collection from the p-n junctions of said grains.
Claim 28
Independent Claim
86 words
A method of fabricating a photovoltaic solar panel comprising: providing an extensive layer of polycrystalline semiconductor material, the grains in said material having one statistically predominant orientation, forming p-n junctions within a substantial proportion of the grains of said layer material, etching said polycrystalline layer with an etchant that preferentially etches the grain orientations facing the grain boundaries of said layer, and selectively providing metallization over said preferentially etched boundaries, said metallization acting as a conductor for current collection from the p-n junctions of said grains.
Claim 29
Dependent Claim
21 words
The method of claim 21 in which said etchant also contains metal ions which combine with ununited bonds on boundary-adjacent grains.
References Cited (Backward Citations)
US2588254A
Cited
US4320168A
Cited
US4171997A
Cited
US4197141A
Cited
US4249957A
Cited
US4366338A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-29 | 1987-02-28 | 1987-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-29 | 1991-02-28 | 1991-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-29 | 1995-02-28 | 1995-08-30 | $7700.00 | Window Closed / Lapsed |