Metal surface modification
Assignee: Combustion Engineering Inc
•
Filing: 1981-12-21
•
Granted: 1983-08-30
•
Expires: 2001-12-21
Abstract
Abstract Properties of the surface of low melting substrate parts including low melting, high conductivity reactive metal parts, are modified by forming an alloy casing thereon having the metal of the substrate as a first (matrix) component thereof together with a higher melting material as the second (reinforcing) component. The higher melting component is coated on the substrate, melted under laser heating, with gas shielding to avoid oxidation, and mixed with a melted portion of the substrate through convective circulation and the mixture is rapidly cooled to produce the alloy casing. Then the casing may be rescanned with the laser beam to rapidly melt and resolidify the casing with refined grain structure. Such grain refining may also be applied to uncoated substrates.
Inventors
- 👤 Daniel S. Gnanamuthu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:19
CPC Classifications
C; C23; C23C; C23C26/00; C23C26/02; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/28; B23K35/286; B23K35/30; B23K35/3053; B23K35/3093; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12458
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
214 words
Surface layer alloy casing production method comprising, coating a preselected area of a metal substrate with a metal layer, the substrate thickness being such to constitute a virtually infinite heat sink relative to the coating, the coating metal liquidus or melting point being at least 200° C. higher than that of the substrate, scanning said area with a laser beam at speed and power density which in conjunction with conductivity of the selected substrate material provides a rapid heatup including melting of the entire coating and a predetermined thickness of the subtrate corresponding to its share of the alloy casing in less than two seconds and rapid cool down and resolidification of the melt to produce a 99% of theoretical density alloy casing entirely incorporating said coated-on metal layer and said sustrate thickness which is melted, with particles of the coating material in a matrix of a eutectic of coating and substrate materials metallurgically diffusion bonded to the substrate, said particles of the original coating material being concentrated upwardly within said casing and preventing oxidation of the melt, the process being controlled to induce a substantial mixing of the entirely melted coating and melted substrate layer and a precipitation out of particles of the original coating material into said matrix before the matrix freezes.
Claim 2
Dependent Claim
214 words
Surface layer alloy casing production method comprising, coating a preselected area of a metal substrate with a metal layer, the substrate thickness being such to constitute a virtually infinite heat sink relative to the coating, the coating metal liquidus or melting point being at least 200° C. higher than that of the substrate, scanning said area with a laser beam at speed and power density which in conjunction with conductivity of the selected substrate material provides a rapid heatup including melting of the entire coating and a predetermined thickness of the subtrate corresponding to its share of the alloy casing in less than two seconds and rapid cool down and resolidification of the melt to produce a 99% of theoretical density alloy casing entirely incorporating said coated-on metal layer and said sustrate thickness which is melted, with particles of the coating material in a matrix of a eutectic of coating and substrate materials metallurgically diffusion bonded to the substrate, said particles of the original coating material being concentrated upwardly within said casing and preventing oxidation of the melt, the process being controlled to induce a substantial mixing of the entirely melted coating and melted substrate layer and a precipitation out of particles of the original coating material into said matrix before the matrix freezes.
Claim 3
Dependent Claim
26 words
Surface layer production method in accordance with claim 1 and further comprising control of conditions to produce a grain refined layer of substrate adjacent said casing.
Claim 4
Dependent Claim
55 words
Surface layer production method in accordance with claim 1 wherein the substrate is selected from the class consisting of metals and alloys which melt (or have a liquidus temperature) at 400°-800° C. and the coating is selected from the class consisting of metals and alloys which melt (or have a liquidus temperature) above 1000° C.
Claim 5
Dependent Claim
24 words
Surface layer production method in accordance with claim 3 wherein the substrate is selected from class consisting of aluminum and magnesium and their alloys.
Claim 6
Dependent Claim
49 words
Surface layer production method in accordance with claim 4 wherein the coating material is selected from the class consisting of elements and alloyed forms of silicon, iron, nickel cobalt, molybdenum, tungsten, chromium, vanadium, zirconium, hafnium, tantalum, columbium, titanium, boron, beryllium, palladium, rhodium, rhenium, iridium, platinum, copper, gold, manganese, osmium.
Claim 7
Dependent Claim
49 words
Surface layer production method in accordance with claim 1 wherein the coating material is selected from the class consisting of elements and alloyed forms of silicon, iron, nickel, cobalt, molybdenum, tungsten, chrominum, vanadium, zirconium, hafnium, tantalum, columbium, titanium, boron, beryllium, palladium, rhodium, rhenium, iridium, platinum, copper gold, manganese, osmium.
Claim 8
Dependent Claim
19 words
Surface layer production method in accordance with claim 6 wherein the substrate comprises aluminum and the coating comprises silicon.
Claim 9
Dependent Claim
19 words
Surface layer production method in accordance with claim 1 wherein the original coating has a thickness of 10-100 mils.
Claim 10
Dependent Claim
16 words
Surface layer production method in accordance with claim 1 wherein original coating is of consolidated form.
Claim 11
Dependent Claim
17 words
Surface layer production method in accordance with claim 1 wherein original coating is of loose powder form.
Claim 12
Dependent Claim
9 words
Product as made by the process of claim 1.
Claim 13
Dependent Claim
158 words
Surface layer production method comprising, coating a higher melting coating metal on a lower melting metal substrate and rapidly scanning a high power density laser beam under shielding gas environment on said coating to melt it entirely and a predetermined depth of the substrate to mix the melt and resolidify rapidly to produce an alloy casing entirely incorporating such melted coating and said melted substrate depth and comprised of precipitated particles of said coating in a matrix of an essentially eutectic mixture of coating and melted substrate, then subsequently rapidly rescanning a high power density laser beam over said casing to remelt and resolidify it even more rapidly thereby reducing the size of said particles by a factor of at least 10X, the process being controlled to induce a substantial mixing of the entirely melted coating and melted substrate layer and a precipitation out of particles of the original coating material into said matrix before the matrix freezes.
Claim 14
Dependent Claim
158 words
Surface layer production method comprising, coating a higher melting coating metal on a lower melting metal substrate and rapidly scanning a high power density laser beam under shielding gas environment on said coating to melt it entirely and a predetermined depth of the substrate to mix the melt and resolidify rapidly to produce an alloy casing entirely incorporating such melted coating and said melted substrate depth and comprised of precipitated particles of said coating in a matrix of an essentially eutectic mixture of coating and melted substrate, then subsequently rapidly rescanning a high power density laser beam over said casing to remelt and resolidify it even more rapidly thereby reducing the size of said particles by a factor of at least 10X, the process being controlled to induce a substantial mixing of the entirely melted coating and melted substrate layer and a precipitation out of particles of the original coating material into said matrix before the matrix freezes.
Claim 15
Dependent Claim
55 words
Surface layer production method in accordance with claim 12 wherein the substrate is selected from the class consisting of metals and alloys which melt (or have a liquidus temperature) at 400°-800° C. and the coating is selected from the class consisting of metals and alloys which melt (or have a liquidus temperature) above 1000° C.
Claim 16
Dependent Claim
25 words
Surface layer production method in accordance with claim 13 wherein the substrate is selected from the class consisting of aluminum and magnesium and their alloys.
Claim 17
Dependent Claim
14 words
Surface layer production method in accordance with claim 14 wherein the substrate comprises aluminum.
Claim 18
Dependent Claim
49 words
Surface layer production method in accordance with claim 15 wherein the coating material is selected from the class consisting of elements and alloyed forms of silicon, iron, nickel, cobalt, molybdenum, tungsten, chromium, vanadium, zirconium, hafnium, tantalum, columbium, titanium, boron, beryllium, palladium, rhodium, rhenium, iridium, platinum, copper, gold, manganese, osmium.
References Cited (Backward Citations)
US3117846A
Cited
US3637374A
Cited
US3594219A
Cited
US3935417A
Cited
US3961098A
Cited
US4015100A
Cited
DE2509190A1
Cited
US3991229A
Cited
US4125926A
Cited
US4059461A
Cited
US4122240A
Cited
US4157923A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-29 | 1987-02-28 | 1987-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-29 | 1991-02-28 | 1991-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-29 | 1995-02-28 | 1995-08-30 | $7700.00 | Window Closed / Lapsed |