Method for manufacturing a fine-patterned thick film conductor structure
Assignee: Asahi Kasei Corp
•
Filing: 1981-11-20
•
Granted: 1983-08-30
•
Expires: 2001-11-20
Abstract
Abstract A method for manufacturing a fine-patterned thick film conductor structure free from ununiformity in film thickness comprises steps of forming resist on a thin metal plate at areas other than land areas, electroplating the thin metal plate using the thin metal plate as a cathode electrode to form conductors having a circuit density of no less than three lines/mm and a thickness of 15-200 μm, bonding the electroplated thin metal plate to an insulative substrate with the thin metal plate side facing up and etching the thin metal plate. The fine-patterned conductors are suited for use in small-sized coils, high density connectors and high density wirings. Further disclosed is a method for manufacturing a fine-patterned thick film printed circuit board free from side protrusion comprising steps of forming resist on a thin metal plate at areas other than land areas, electroplating the thin metal plate to a thickness of 0.3-10 μm at a current density of 0.05-2 A/dm 2 , electroplating the thin metal plate to a desired final thickness at a current density of 3-20 A/dm 2 , and removing all or the areas other than the land areas of the thin metal plate.
Inventors
- 👤 Kaoru Ohmura
- 👤 Ryohei Koyama
- 👤 Takeo Kimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:10
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/20; H05K3/205; H05K2203/00; H05K2203/01; H05K2203/0147; H05K2203/0152; H05K2203/03; H05K2203/0376; H05K2203/07; H05K2203/0703; H05K2203/0726; H05K3/38; H05K3/386
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
124 words
A method for manufacturing a fine-patterned thick film conductor structure comprising the steps of: (a) forming a resist on a thin metal plate at areas other than land areas and electroplating said land areas using said thin metal plate as a cathode electrode to form conductors having a circuit density of no less than 3 lines/mm and a film thickness of 15-200 μm, the cathode current density in the electroplating to said thin metal plate being between 0.05 and 2 A/dm 2 until the film thickness reaches 0.3-10 μm, and thereafter increasing to 3-50 A/dm 2 ; (b) bonding said electroplated thin metal plate to an insulative substrate with the thin metal plate side facing up, and (c) etching away said thin metal plate.
Claim 2
Independent Claim
124 words
A method for manufacturing a fine-patterned thick film conductor structure comprising the steps of: (a) forming a resist on a thin metal plate at areas other than land areas and electroplating said land areas using said thin metal plate as a cathode electrode to form conductors having a circuit density of no less than 3 lines/mm and a film thickness of 15-200 μm, the cathode current density in the electroplating to said thin metal plate being between 0.05 and 2 A/dm 2 until the film thickness reaches 0.3-10 μm, and thereafter increasing to 3-50 A/dm 2 ; (b) bonding said electroplated thin metal plate to an insulative substrate with the thin metal plate side facing up, and (c) etching away said thin metal plate.
Claim 3
Dependent Claim
49 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1 wherein said electroplated thin metal plates are bonded on both sides of said insulative substrate with the thin metal plate side facing up so that the conductor patterns of said plates face to each other.
Claim 4
Dependent Claim
57 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1 or 2 further comprising the step of electroplating the exposed conductors after said thin metal plate has been etched to form conductor layers having a thickness of 15-200 μm whereby a substantial thickness of the conductors is attained without thickening the plated conductors.
Claim 5
Dependent Claim
64 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 2 further comprising the step of drilling through-holes at through-hole connection areas of the conductor pattern on said insulative substrate after said thin metal plates on both sides of said insulative substrate have been etched, and electroplating the exposed conductors to form conductor layers thereon having a thickness of 15-200 μm.
Claim 6
Dependent Claim
42 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 4 wherein a cathode current density in the electroplating to the exposed conductors after the etching of said thin metal plate is between 3 and 50 A/dm 2 .
Claim 7
Dependent Claim
35 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1, 2 or 4 wherein said thin metal film is selected from aluminum, tin and zinc having a thickness of 1-500 μm.
Claim 8
Dependent Claim
22 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1, 2 or 4 wherein said conductor is copper.
Claim 9
Dependent Claim
31 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1, 2 or 4 wherein said insulative substrate is a polymer film having a thickness of 5-200 μm.
Claim 10
Dependent Claim
42 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 3 wherein a cathode current density in the electroplating to the exposed conductors after the etching of said thin metal plate is between 3 and 50 A/dm 2 .
Claim 11
Dependent Claim
32 words
A method for manufacturing a fine-patterned thick film conductor strcuture according to claim 3 wherein siad thin metal film is selected from aluminum, tin and zinc having a thickness of 1-500 μm.
Claim 12
Dependent Claim
19 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 3 wherein said conductor is copper.
Claim 13
Dependent Claim
28 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 3 wherein said insulative substrate is a polymer film having a thickness of 5-200 μm.
Claim 14
Dependent Claim
32 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1 wherein said tin metal film is selected from aluminum, tin and zinc having a thickness of 1-500 μm.
Claim 15
Dependent Claim
32 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 5 wherein said thin metal film is selected from aluminum, tin and zinc having a thickness of 1-500 μm.
Claim 16
Dependent Claim
19 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1 wherein said conductor is copper.
Claim 17
Dependent Claim
19 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 5 wherein said conductor is copper.
Claim 18
Dependent Claim
19 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 6 wherein said conductor is copper.
Claim 19
Dependent Claim
42 words
A method for manufacturing a fine-patterned thick film conductor structure according to claim 1 wherein a ratio of plated film thickness to line-to-line spacing is no smaller than 1.4 at a cathode current density of no smaller than 3 A/dm 2 .
Claim 20
Independent Claim
94 words
A method for manufacturing a fine-patterned thick film printed circuit board comprising the steps of: (a) forming a resist on a thin metal plate at areas other than land areas; (b) electroplating said thin metal plate to a thickness of 0.3-10 μm at a current density of 0.05-2 A/dm 2 ; (c) electroplating said thin metal plate to a desired film thickness at a current density of 3-20 A/dm 2 to form conductors on said land areas; and (d) removing all of the areas other than the land areas of said thin metal plate.
Claim 21
Independent Claim
94 words
A method for manufacturing a fine-patterned thick film printed circuit board comprising the steps of: (a) forming a resist on a thin metal plate at areas other than land areas; (b) electroplating said thin metal plate to a thickness of 0.3-10 μm at a current density of 0.05-2 A/dm 2 ; (c) electroplating said thin metal plate to a desired film thickness at a current density of 3-20 A/dm 2 to form conductors on said land areas; and (d) removing all of the areas other than the land areas of said thin metal plate.
Claim 22
Dependent Claim
42 words
A method for manufacturing a fine-patterned thick printed circuit board according to claim 19 wherein a ratio of plated film thickness to line-to-line spacing is no smaller than 1.4 at a cathode current density of no smaller than 3 A/dm 2 .
Claim 23
Dependent Claim
40 words
A method for manufacturing a fine-patterned thick film printed circuit board according to claim 19 further comprising a step of bonding said thin metal plate to an insulative substrate after said steps (a) to (c) and before said step (d).
References Cited (Backward Citations)
US2447541A
Cited
US2874085A
Cited
US2984595A
Cited
US3152938A
Cited
US3024151A
Cited
US3414487A
Cited
GB1258856A
Cited
US3704207A
Cited
US3990926A
Cited
US4159222A
Cited
GB2066583A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-29 | 1987-02-28 | 1987-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-29 | 1991-02-28 | 1991-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-29 | 1995-02-28 | 1995-08-30 | $7700.00 | Window Closed / Lapsed |