Ambient temperature application of indicia to elastomer substrates

Claim 2

A process for applying an amine curable prepolymer or polymer to a substrate, comprising the steps of: applying a treating agent to the surface of a cured elastomer substrate, said treating agent selected from the group consisting of an N-halohydantoin, an N-haloamide, and an N-haloimide applying a curable indicia to said treated substrate along a limited portion of said substrate, said indicia containing an amine curable polymer or prepolymer, a polar solvent, and an amine curing agent, and curing said indicia at ambient temperatures.

Claim 3

A process according to claim 1, wherein said indicia is made by mixing said amine curable polymer or prepolymer, said polar solvent, and said amine curing agent, said amine curable polymer or prepolymer selected from the group consisting of (a) epoxy resins; (b) halogen-containing hydrocarbon polymers; (c) chlorosulfonated polymers; (d) polymers containing acid halide groups such as ##STR5## and haloformate groups such as ##STR6## (e) polymers containing anhydride groups which, on reaction with said diamines, yield amide-acid linkages; (f) organopolysiloxanes; and (g) urethane polymers or prepolymers; wherein said polar solvent is selected from a compound having dipole moments in excess of 0.4 debye in which there are no more than a total of 8 CH 3 --, CH 2 , or tertiary carbon radicals per polar group contained in said compound, and (b) benzene and biphenyl; and wherein said elastomer substrate is made from monomers selected from the group consisting of (a) dienes containing from 4 to 12 carbon atoms, copolymers thereof, and interpolymers thereof; (b) natural rubber; (c) vinyl substituted aromatic compounds having from 8 to 15 carbon atoms and diene compounds having from 4 to 12 carbon atoms; (d) isobutylene and isoprene; (e) butadiene and acrylonitrile; and (f) chloroprene, and (g) combinations thereof.

Claim 4

A process according to claim 2, wherein said indicia is in liquid form before cure.

Claim 5

A process according to claim 3, wherein said polar compound ranges from about 2 to about 40 parts per 100 parts of said prepolymer or polymer and is selected from the group consisting of esters, ketones, ethers, halogenated hydrocarbons, tertiary amines, nitrile paraffins, fully substituted amides, sulfones, sulfoxides, and sulfides.

Claim 6

A process according to claim 4, wherein said elastomer substrate is selected from the group consisting of said elastomers made from said conjugated dienes, elastomers made from said conjugated dienes and said vinyl substituted aromatics, and said natural rubber; said elastomers made from said conjugated dienes being made from monomers, selected from the group consisting of butadiene, isoprene, pentadiene, hexadiene, heptadiene, octadiene, 2,3-dimethyl-1,3-butadiene and 2,3-dimethyl-1,3-pentadiene; said amine curable polymer or prepolymer is said urethane polymer or prepolymer containing isocyanate end groups; and said polar solvent selected from the group consisting of dimethylformamide, tetrahydrofuran, cyclohexanone, ethyl acetate, methyl ethyl ketone, and acetone.

Claim 7

A process according to claim 5, wherein said elastomer substrate is selected from the group consisting of polybutadiene, natural rubber, and styrene-butadiene rubber, and wherein said ambient temperature cure is from about 15° C. to about 50° C., and wherein said indicia is formed in a mold, and said mold is applied to said treated elastomer substrate so that said indicia adheres to said treated substrate when said mold is removed.

Claim 8

A process according to claim 6, wherein said treating agent is selected from the group consisting of 1,3-dichloro-5,5-dimethyl hydantoin; 1,3-dibromo-5,5-dimethyl hydantoin; 1,3-dichloro-5-methyl-5-isobutyl hydantoin; 1,3-dichloro-5-methyl-5-hexyl hydantoin; N-bromoacetamide; tetrachloroglycoluril; and N-bromosuccinimide.

Claim 9

A process according to claim 6, wherein said treating agent is selected from the group consisting of monochloroisocyanuric acid, dichloroisocyanuric acid, trichloroisocyanuric acid, and combinations thereof.

Claim 10

A process according to claims 2, 3, 4, 5, 6, 7, or 8 wherein said amine curing agent is selected from the group consisting of (a) 4,4'-methylene bis (2-chloroaniline), (b) a complex of 4,4'-methylene dianiline and a salt, said salt being selected from the group consisting of sodium chloride, sodium bromide, sodium iodide, sodium nitrite, lithium chloride, lithium bromide, lithium iodide, lithium nitrite, and sodium cyanide, (c) a complex of racemic 2,3-di-4(aminophenyl)butane with a salt, said salt selected from the group consisting of sodium chloride, sodium bromide, sodium iodide, potassium chloride, potassium bromide, potassium iodide, cesium chloride, cesium bromide, and cesium iodide, the ratio of said dianiline or said butane to said salt in said complex being 3 moles to 1 mole, the equivalent amount of said curing agent based upon said prepolymer or polymer ranging from about 0.85 to about 105.

Claim 11

A process according to claims 2, 3, 4, 5, 6, 7, or 8, wherein said elastomer substrate is a tire.

Claim 12

A process according to claims 2, 3, 4, 5, 6, 7, or 8, wherein said elastomer substrate is a conveyor belt.

Claim 13

A process according to claims 2, 3, 4, 5, 6, 7, or 8, wherein said elastomer substrate is a hose.

Claim 14

A process according to claims 2, 3, 4, 5, 6, 7, or 8, including the step of applying said liquid indicia to said substrate in situ.

Claim 15

A process for repairing an elastomer substrate having a cut or gouge therein, comprising the steps of: applying a treating agent to the cut or gouge of the elastomer substrate, said treating agent selected from the group consisting of N-halohydantoins, N-haloamides, and N-haloimides; obtaining an amine curable prepolymer or polymer; obtaining a polar or polarizable solvent selected from (a) compounds having dipole moments in excess of 0.4 debye in which there are no more than a total of 8 CH 3 --, CH 2 , or tertiary carbon radicals per polar group contained in said compound, and (b) benzene and biphenyl; obtaining an amine curing agent; mixing said amine curable polymer and prepolymer, said amine curing agent, and said polar solvent, and forming a liquid mixture; applying said liquid mixture to said treated elastomer substrate and curing said liquid mixture at ambient temperature so that a strong bond is obtained whereby said article is repaired.

Claim 16

A process for repairing an elastomer substrate having a cut or gouge therein, comprising the steps of: applying a treating agent to the cut or gouge of the elastomer substrate, said treating agent selected from the group consisting of N-halohydantoins, N-haloamides, and N-haloimides; obtaining an amine curable prepolymer or polymer; obtaining a polar or polarizable solvent selected from (a) compounds having dipole moments in excess of 0.4 debye in which there are no more than a total of 8 CH 3 --, CH 2 , or tertiary carbon radicals per polar group contained in said compound, and (b) benzene and biphenyl; obtaining an amine curing agent; mixing said amine curable polymer and prepolymer, said amine curing agent, and said polar solvent, and forming a liquid mixture; applying said liquid mixture to said treated elastomer substrate and curing said liquid mixture at ambient temperature so that a strong bond is obtained whereby said article is repaired.

Claim 17

A process according to claim 14, wherein said elastomer substrate is made from monomers selected from the group consisting of (a) dienes containing from 4 to 12 carbon atoms, copolymers thereof, and interpolymers thereof; (b) natural rubber; (c) vinyl substituted aromatic compounds having from 8 to 15 carbon atoms and diene compounds having from 4 to 12 carbon atoms; (d) isobutylene and isoprene; (f) butadiene and acrylonitrile; and (g) chloroprene; said prepolymer or polymer selected from the group consisting of (a) epoxy resins; (b) halogen-containing hydrocarbon polymers; (c) chlorosulfonated polymers; (d) polymers containing acid halide groups such as ##STR7## and haloformate groups such as ##STR8## (e) polymers containing anhydride groups which, on reaction with diamines, yield amide-acid linkages; (f) organopolysiloxanes; and (g) urethane polymers or prepolymers; said polar compound ranging from about 2 to about 40 parts per 100 parts of prepolymer, and being selected from the group consisting of esters, ketones, ethers, halogenated hydrocarbons, tertiary amines, nitroparaffins, fully substituted amides, sulfones, sulfoxides, and sulfides.

Claim 18

A process according to claim 15, wherein said elastomer substrate is selected from the group consisting of said elastomers made from said conjugated dienes, elastomers made from said conjugated dienes and said vinyl substituted aromatics, and said natural rubber; said elastomers made from said conjugated dienes being made from monomers selected from the group consisting of butadiene, isoprene, pentadiene, hexadiene, heptadiene, octadiene, 2,3-dimethylbutadiene and 2,3-dimethyl-1,3-pentadiene; said amine curable polymer or prepolymer is said urethane polymer or prepolymer containing isocyanate end groups; said curing agent being said complex of 4,4'-methylene dianiline and a salt; and said polar solvent selected from the group consisting of dimethylformamide, tetrahydrofuran, cyclohexanone, ethyl acetate, methyl ethyl ketone, and acetone.

Claim 19

A process according to claim 16, wherein said curing agent is made from the salt of lithium chloride or sodium chloride, and wherein said elastomer substrate is selected from the group consisting of polybutadiene, natural rubber, and styrene-butadiene rubber.

Claim 20

A process according to claim 14, 15, 16, or 17, wherein said treating agent is selected from the group consisting of 1,3-dichloro-5,5-dimethyl hydantoin; 1,3-dibromo-5,5-dimethyl hydantoin; 1,3-dibromo-5,5-dimethyl hydantoin; 1,3-dichloro-5-methyl-5-isobutyl hydantoin; 1,3-dichloro-5-methyl-5-hexyl hydantoin; N-bromoacetamide; tetrachloroglycoluril; and N-bromosuccinimide.

Claim 21

A process according to claim 14, 15, 16, or 17, wherein said treating agent is selected from the group consisting of monochloroisocyanuric acid, dichloroisocyanuric acid, trichloroisocyanuric acid, and combinations thereof.

Claim 22

A process according to claim 14, 15, 16, or 17, wherein said liquid mixture is formed and applied in situ.

Claim 23

A process according to claim 14, 15, 16, or 17, wherein said substrate is a tire, and whereby said tire is repaired.