Zone purification of silicon in a reactive plasma
Assignee: Electricite de France SA
•
Filing: 1981-07-28
•
Granted: 1983-08-16
•
Expires: 2001-07-28
Abstract
Abstract Boron is removed from silicon by zone melting purification. A jet of hot plasma obtained by high frequency excitation is directed on a zone of a bar of silicon to be purified. The plasma is formed from a mixture of a plasma-producing gas, such as argon, and an amount of oxygen which is sufficiently low to avoid oxidization of silicon.
Inventors
- 👤 Jacques Amouroux
- 👤 Daniel Morvan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:02
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/02; C30B29/06; C30B13/00; C30B13/16; C30B13/22
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
86 words
A process for zone melting purification of silicon, comprising the steps of melting a zone of a bar of silicon to be purified by directing a jet of hot plasma obtained by high frequency excitation onto said zone and moving the jet and bar with respect to each other so as to cause the melted zone to travel along the bar, wherein the plasma is formed from a mixture of a plasma-producing gas and a sufficiently small amount of oxygen to avoid substantial oxidation of silicon.
Claim 2
Dependent Claim
86 words
A process for zone melting purification of silicon, comprising the steps of melting a zone of a bar of silicon to be purified by directing a jet of hot plasma obtained by high frequency excitation onto said zone and moving the jet and bar with respect to each other so as to cause the melted zone to travel along the bar, wherein the plasma is formed from a mixture of a plasma-producing gas and a sufficiently small amount of oxygen to avoid substantial oxidation of silicon.
Claim 3
Dependent Claim
33 words
A process according to claim 1 for boron removal, wherein the oxygen percentage of the plasma is adjusted to a value between 100 times and 300 times the boron percentage in said silicium.
Claim 4
Dependent Claim
22 words
A process according to claim 1, wherein the oxygen percentage of the plasma is adjusted to a value between 0.005% and 0.1%.
Claim 5
Dependent Claim
20 words
A process according to claim 1 or 2, wherein the plasma is created by a purely inductive process without electrodes.
Claim 6
Dependent Claim
31 words
A process according to claim 1, further comprising the steps of cleaning the ingot with acid to remove any boron compounds drawn to the surface of the ingot by zone melting.
Claim 7
Dependent Claim
21 words
A process according to claim 1, wherein hydrogen is added to the plasma-producing gas and to the oxygen in the plasma.
Claim 8
Dependent Claim
29 words
A process according to claim 1, further comprising the step of processing the ingot with a plasma containing no oxygen to eliminate defects after treatment with plasma containing oxygen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-15 | 1987-02-14 | 1987-08-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-15 | 1991-02-14 | 1991-08-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-15 | 1995-02-14 | 1995-08-16 | $7700.00 | Window Closed / Lapsed |