Process for the continuous manufacture of sheeting from thermoplastic synthetic resins
Assignee: HT Troplast AG
•
Filing: 1981-08-18
•
Granted: 1983-08-02
•
Expires: 2001-08-18
Abstract
Abstract A process for the continuous manufacture of sheeting from thermoplastic synthetic resins includes the steps of applying thermoplastic synthetic resin, in the form of particles, such as shreds, crumbs, cuttings, pieces, chips, or the like, continuously as a sheet-like layer of raw material to a moving support; passing the raw material layer through a heating zone to thereby preheat the material layer to a temperature approximately in the range from 100° to 140° C.; pressing the preheated material layer continuously over its full area during travel through a treatment zone so that, in a first phase, the raw material layer is compacted and welded under the effect of a pressure of from about 10 to 60 kp/cm 2 and at the same time the material layer is heated to a temperature in the range from about 160° to 220° C; and, in a second, directly following phase, while maintaining said pressure, cooling the material layer and simultaneously pressing the layer to the thickness dimension predetermined by the amount of raw material layer applied to the moving support.
Inventors
- 👤 Hans Brinkmann
- 👤 Bernhard Kraemer
- 👤 Herbert Schulte
- 👤 Uwe Sommermeyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 07:43
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/50; B29C70/504; B29C70/506; B29B; B29B13/00; B29C43/00; B29C43/22; B29C43/228; B29B17/00; B29B17/0026; B29B17/0042; B29C43/32; B29C43/44; B29C43/48; B29C2043/483; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2105/0854; B29K2105/25; B29K2105/251; B29L; B29L2007/00; B29L2007/002; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/62; Y10; Y10S; Y10S425/00; Y10S425/046
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
177 words
A process for the continuous manufacture of a sheet from thermoplastic synthetic resins, especially a sheet suitable as covering material for use in the construction field, which comprises applying thermoplastic synthetic resin, in the form of particles on a continuously moving support to form a sheet-like layer of raw material consisting of said particles on said moving support; transporting the raw material layer through a heating zone to thereby preheat the raw material layer to an elevated temperature; pressing the preheated raw material layer continuously over its full area while traveling through a pressing treatment zone having two treatment phases, in the first treatment phase, the layer of raw material is compacted under the effect of the pressing pressure and the particles are heated to a welding temperature to form a thermoplastic sheet comprised of said welded particles and, in the second, directly succeeding treatment phase, the sheet is cooled and is simultaneously pressed under the same pressing pressure applied in the first treatment phase and thereafter removing the sheet of welded particles from said moving support.
Claim 2
Dependent Claim
177 words
A process for the continuous manufacture of a sheet from thermoplastic synthetic resins, especially a sheet suitable as covering material for use in the construction field, which comprises applying thermoplastic synthetic resin, in the form of particles on a continuously moving support to form a sheet-like layer of raw material consisting of said particles on said moving support; transporting the raw material layer through a heating zone to thereby preheat the raw material layer to an elevated temperature; pressing the preheated raw material layer continuously over its full area while traveling through a pressing treatment zone having two treatment phases, in the first treatment phase, the layer of raw material is compacted under the effect of the pressing pressure and the particles are heated to a welding temperature to form a thermoplastic sheet comprised of said welded particles and, in the second, directly succeeding treatment phase, the sheet is cooled and is simultaneously pressed under the same pressing pressure applied in the first treatment phase and thereafter removing the sheet of welded particles from said moving support.
Claim 3
Dependent Claim
27 words
A process according to claim 1, wherein the sheet is cooled to a temperature approximately in the range from 120° to 140° C. and is thereafter embossed.
Claim 4
Dependent Claim
27 words
A process according to claim 1, wherein the sheet is cooled to a temperature approximately in the range from 50° to 80° C. and is thereafter split.
Claim 5
Dependent Claim
31 words
A process according to one of claims 1-3, wherein the particles are applied in a to-and-fro motion transversely across the moving support up to a desired thickness of the material layer.
Claim 6
Dependent Claim
23 words
A process according to claim 1, wherein particles of said material are utilized having the same or a different composition of the material.
Claim 7
Dependent Claim
34 words
A process according to claim 1, wherein at least a portion of the particles is provided with a colored and/or conductive encasing, on the basis of coloring agents, carbon black pastes, or metal pastes.
Claim 8
Dependent Claim
56 words
A process according to claim 1, wherein the particles are applied, to form the layer of raw material, onto a supporting sheet or a textile supporting sheet of fleeces, mats, fabrics, meshworks of mineral and/or synthetic resin fibers, including fibers, polyester fibers or polyamide fibers, and are pressed into a composite sheet in the treatment zone.
Claim 9
Dependent Claim
31 words
A process according to claim 1, wherein the particles comprise a vinyl chloride polymer and/or copolymer of vinyl chloride, which contains plasticizers, as well as optionally additional auxiliary agents and fillers.
Claim 10
Dependent Claim
21 words
A process according to claim 1, wherein the particles comprise thermoplastic synthetic resin partially including acrylates, polyesters or ethylene vinyl acetate.
Claim 11
Dependent Claim
22 words
A process according to claim 1, wherein the particles are made of crosslinkable thermoplastic synthetic resins, such as ethylene-propylene copolymers, ethylene-propylene terpolymers.
Claim 12
Dependent Claim
36 words
A process according to claim 10, wherein after pressing and welding the particles together into the sheet, crosslinking of the synthetic resin is carried out either within the treatment zone or after leaving the treatment zone.
Claim 13
Dependent Claim
22 words
A process according to claim 1, wherein a sheet is produced having a thickness from 1.5 mm to at least 10 mm.
Claim 14
Dependent Claim
94 words
A process according to claim 1, wherein the particles forming the layer of raw material are applied to an endlessly revolving bottom belt providing said moving support and are preheated thereon, and thereafter the topside of the layer of raw material is covered with an endlessly revolving top belt and the resulting covered layer is drawn continuously through a double ram press formed around said top belt and said bottom belt, said press being heated in an inlet zone providing said first treatment phase and cooled in an outlet zone providing second treatment phase.
Claim 15
Dependent Claim
25 words
A process according to claim 13, wherein the raw material layer is supported along the sides by concomitantly revolving belts while traveling through the press.
Claim 16
Dependent Claim
19 words
A process according to claim 1, wherein a sheet is produced having a thickness from 4 to 8 mm.
Claim 17
Dependent Claim
20 words
A process according to claim 1, wherein the processing (travelling) speed is from 0.5 m/min. to at least 2.0 m/min.
Claim 18
Dependent Claim
33 words
A process according to claim 1, wherein the heating of the material layer in the treatment zone is effected by electrical resistant heating means, which are heated up to 160° to 220° C.
Claim 19
Dependent Claim
39 words
A process according to claim 1, wherein the cooling of the material layer in the treatment zone is effected by cooling water of a temperature of 20° to 100° C., flowing within channels in the vibrating press metal plates.
Claim 20
Dependent Claim
40 words
A process according to claim 1, wherein the treatment zone is formed by a double ram vibrating press which includes a pair of endless conveyor belts that engage the upper and lower surfaces of the sheet formed within said press.
Claim 21
Dependent Claim
75 words
A process according to claim 1, wherein the layer of raw materials is preheated to a temperature approximately in the range of from 100° to 140° C., the layer of raw material is subjected to a pressing pressure in the range of from about 10 to 60 kp/cm 2 and is heated to a temperature in the range of from about 160° to 220° C. in the first treatment phase of said pressing treatment zone.
References Cited (Backward Citations)
US3012901A
Cited
DE1479090A1
Cited
US3399426A
Cited
US3488411A
Cited
US3617590A
Cited
DE1679822B1
Cited
DE1928405A1
Cited
US3607999A
Cited
US3754065A
Cited
US4239715A
Cited
US3883624A
Cited
DE2319254B2
Cited
US4238176A
Cited
US4189291A
Cited
US4254068A
Cited
US4363771A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-01 | 1987-01-31 | 1987-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-01 | 1991-01-31 | 1991-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-01 | 1995-01-31 | 1995-08-02 | $7700.00 | Window Closed / Lapsed |