Process for continuously regenerating ferric chloride solutions
Assignee: Tesla Koncernovy Podnik
•
Filing: 1981-10-27
•
Granted: 1983-08-02
•
Expires: 2001-10-27
Abstract
Abstract The continuous electrolytic regeneration of ferric chloride solutions used for etching metals is effected by transferring the partially exhausted solution to the anodic space of an electrolyzer where it is exposed to direct current. The etched metal is deposited on the cathode, and the Fe 2+ is oxidized to Fe 3+ in the anodic space. The latter is separated from the cathodic space through a diaphragm and the regenerated solution is recirculated to the etching bath.
Inventors
- 👤 Antonin Stehlik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:16
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/46
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
165 words
A process for continuously regenerating a partial exhausted ferric chloride solution used for the bath of etching metals comprising the steps of providing an electrolyzer separated into a vertical anode space and a vertical cathode space by an ion exchange diaphragm, locating an anode extending freely into said anode space and a cathode extending freely into said cathode space and simultaneously feeding at least a part of said exhausted solution from the etching bath to the top of said anode space exposing said exhausted solution to direct current between the anode and cathode at a temperature and at a current density for a time sufficient to permit the deposition of metal on the cathode and the oxidation of the Fe 2+ to Fe 3+ in the anode space, and withdrawing regenerated solution from the bottom of said anode space for return to said etching bath, the circulation of said solution being maintained at a rate such that no free chlorine is liberated from said solution.
Claim 2
Dependent Claim
165 words
A process for continuously regenerating a partial exhausted ferric chloride solution used for the bath of etching metals comprising the steps of providing an electrolyzer separated into a vertical anode space and a vertical cathode space by an ion exchange diaphragm, locating an anode extending freely into said anode space and a cathode extending freely into said cathode space and simultaneously feeding at least a part of said exhausted solution from the etching bath to the top of said anode space exposing said exhausted solution to direct current between the anode and cathode at a temperature and at a current density for a time sufficient to permit the deposition of metal on the cathode and the oxidation of the Fe 2+ to Fe 3+ in the anode space, and withdrawing regenerated solution from the bottom of said anode space for return to said etching bath, the circulation of said solution being maintained at a rate such that no free chlorine is liberated from said solution.
Claim 3
Dependent Claim
54 words
The process as claimed in claim 1 wherein the electrolyzer tank is divided into three compartments by two diaphragms so located as to limit the mixing of the anode solution with the cathode solution and to permit an intensive flow of the regenerated etching solution in the compartments between the diaphragms and the anodes.
Claim 4
Dependent Claim
53 words
A process as claimed in claim 1 including the step of circulating said solution and maintaining the density of the direct current at a level, such that the deposition on the cathode per unit time is substantially equal to the amount of metal supplied to the etching bath due to the etching process.
Claim 5
Dependent Claim
36 words
A process as claimed in claim 3 including the step of maintaining the temperature of the solution to be regenerated by controlling the speed of recirculation of the solution between the electrolyzer and the etching bath.
Claim 6
Dependent Claim
53 words
A process as claimed in claim 4, wherein the speed of circulation of the solution through the electrolyzer is regulated so that the temperature within the electrolyzer is maintained higher than the desired temperature of the etching bath and the heat energy in the electrolyzer is used for heating of the etching bath.
Claim 7
Dependent Claim
34 words
The process as claimed in claim 1 wherein the direct current intensity is so controlled that the ratio of Fe 3+ /Fe 2+ in the etching bath may be kept at a constant value.
Claim 8
Dependent Claim
35 words
The process as claimed in claim 1 whereing the current between anode and cathode is maintained at a density of from 20 to 60 A/dm 2 at a temperature of from 50° to 95° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-01 | 1987-01-31 | 1987-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-01 | 1991-01-31 | 1991-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-01 | 1995-01-31 | 1995-08-02 | $7700.00 | Window Closed / Lapsed |