Patent US4396422A successfully refreshed from Google Patents.
US4396422A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing iron and refractory material
Assignee: Individual
•
Filing: 1982-03-08
•
Granted: 1983-08-02
•
Expires: 2002-03-08
Abstract
Abstract There is disclosed a process for producing iron and refractory material for use as a raw material for a refractory brick and as an aggregate for a castable refractory product. A mixture of aluminum smelting residue and scale is introduced into a furnace. The mixture is melted in the furnace and a thermit reaction is generated. After the completion of the thermit reaction, a molten iron and a molten slag are cooled. Particularly the molten slag is gradually cooled. The slag is crushed to form the refractory material. Alternatively, in order to produce iron and alumina cement, quicklime and/or limestone are further introduced into the furnace. The molten slag is cooled rapidly to form a clinker. The clinker is crushed to a powder size to form the alumina cement.
Inventors
- 👤 Hiroshi Matsuno
- 👤 Hiroyuki Sasaki
- 👤 Hideaki Shibuya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 23:07
CPC Classifications
C; C21; C21B; C21B3/00; C21B3/04; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y02W; Y02W30/00; Y02W30/50; Y10; Y10S; Y10S75/00; Y10S75/958
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
151 words
A process for producing iron and a refractory material for use as a raw material for a refractory brick and as an aggregate for a castable refractory product, which process comprises the steps of: (a) introducing a mixture of aluminum smelting residue and scale into a furnace, said aluminum smelting residue being composed mainly of metallic aluminum and alumina, and said scale being composed mainly of iron oxide; (b) melting said mixture in the furnace and generating a thermit reaction between the metallic aluminum in said aluminum smelting residue and the iron oxide in said scale, so that said mixture is formed into molten iron and molten slag; (c) cooling said molten iron and said molten slag after the completion of said thermit reaction, said molten slag being gradually cooled to cause crystal growth therein; and (d) crushing said slag to particle size or powder size to form the refractory material.
Claim 2
Dependent Claim
151 words
A process for producing iron and a refractory material for use as a raw material for a refractory brick and as an aggregate for a castable refractory product, which process comprises the steps of: (a) introducing a mixture of aluminum smelting residue and scale into a furnace, said aluminum smelting residue being composed mainly of metallic aluminum and alumina, and said scale being composed mainly of iron oxide; (b) melting said mixture in the furnace and generating a thermit reaction between the metallic aluminum in said aluminum smelting residue and the iron oxide in said scale, so that said mixture is formed into molten iron and molten slag; (c) cooling said molten iron and said molten slag after the completion of said thermit reaction, said molten slag being gradually cooled to cause crystal growth therein; and (d) crushing said slag to particle size or powder size to form the refractory material.
Claim 3
Dependent Claim
14 words
A process according to claim 1, in which said aluminum smelting residue contains magnesia.
Claim 4
Dependent Claim
18 words
A process according to claim 1, in which a raw material containing magnesia is introduced into said furnace.
Claim 5
Dependent Claim
143 words
A process for producing iron and alumina cement as a refractory material, which process comprises the steps: (a) introducing a mixture of aluminum smelting residue and scale into a furnace, said aluminum smelting residue being composed mainly of metallic aluminum and alumina, and said scale being composed mainly of iron oxide; (b) introducing quicklime and/or limestone into said furnace; (c) melting the raw materials introduced into said furnace and generating a thermit reaction between the metallic aluminum in said aluminum smelting residue and the iron oxide in said scale, so that said raw materials are formed into molten iron and molten slag; (d) cooling said molten iron and said molten slag after the completion of said thermit reaction, said molten slag being rapidly cooled to form a clinker containing amorphous substance; and (e) crushing said clinker to powder to form the alumina cement.
Claim 6
Dependent Claim
143 words
A process for producing iron and alumina cement as a refractory material, which process comprises the steps: (a) introducing a mixture of aluminum smelting residue and scale into a furnace, said aluminum smelting residue being composed mainly of metallic aluminum and alumina, and said scale being composed mainly of iron oxide; (b) introducing quicklime and/or limestone into said furnace; (c) melting the raw materials introduced into said furnace and generating a thermit reaction between the metallic aluminum in said aluminum smelting residue and the iron oxide in said scale, so that said raw materials are formed into molten iron and molten slag; (d) cooling said molten iron and said molten slag after the completion of said thermit reaction, said molten slag being rapidly cooled to form a clinker containing amorphous substance; and (e) crushing said clinker to powder to form the alumina cement.
Claim 7
Dependent Claim
51 words
A process according to claim 4, in which while said molten slag is maintained at a temperature of above 1,650° C. after the completion of said thermit reaction, oxygen under pressure is blown into said molten slag to reduce the content of those substances which adversely affect the resultant alumina cement.
Claim 8
Dependent Claim
14 words
A process according to claim 4, in which said aluminum smelting residue contains silica.
Claim 9
Dependent Claim
18 words
A process according to claim 4, in which a raw material containing silica is introduced into said furnace.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-08-01 | 1987-01-31 | 1987-08-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-08-01 | 1991-01-31 | 1991-08-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-08-01 | 1995-01-31 | 1995-08-02 | $7700.00 | Window Closed / Lapsed |