Abstract
Abstract A process for the manufacture of a polyurethane prepolymer adhesive by a catalyst initiated reaction of polyol and isocyanate copolymers is performed under room temperature conditions, and in convenient quantities for application, storage, and transportation purposes. Compounding includes alternatives of catalyst and co-catalyst combinations, and additives, including a reaction inhibitor, plasticizer, delayed reaction catalyst and surfactant.
Inventors
- 👤 James A. Hammond
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:46
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/089; C08G18/16; C09; C09J; C09J175/00; C09J175/04; C08G2170/00; C08G2170/60
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
161 words
A process for manufacturing a polyurethane prepolymer adhesive under room temperature conditions comprising the steps of: (a) introducing a predetermined amount of at least one polyol reactant into a reaction vessel; (b) mixing a predetermined amount of least one isocyanate reactant into the reaction vessel to give a uniform resin mixture sufficient to give an excess active isocyanate content in the polyurethane prepolymer adhesive of approximately 5% to 20% by weight; (c) adding a predetermined amount of catalyst to initiate reaction of the reactants in the reaction vessel, with vigorous stirring to give a uniform mixture, said predetermined amount of catalyst being sufficient to allow the reaction to substantially reach completion within 2 to 8 hours; (d) isolating the mixed contents in the reaction vessel from ambient conditions to prevent contamination of the contents by ambient moisture; and (e) mixing the reactants during the reaction in the reaction vessel until the reaction substantially subsides, whereby the polyurethane prepolymer adhesive is formed.
Claim 2
Dependent Claim
161 words
A process for manufacturing a polyurethane prepolymer adhesive under room temperature conditions comprising the steps of: (a) introducing a predetermined amount of at least one polyol reactant into a reaction vessel; (b) mixing a predetermined amount of least one isocyanate reactant into the reaction vessel to give a uniform resin mixture sufficient to give an excess active isocyanate content in the polyurethane prepolymer adhesive of approximately 5% to 20% by weight; (c) adding a predetermined amount of catalyst to initiate reaction of the reactants in the reaction vessel, with vigorous stirring to give a uniform mixture, said predetermined amount of catalyst being sufficient to allow the reaction to substantially reach completion within 2 to 8 hours; (d) isolating the mixed contents in the reaction vessel from ambient conditions to prevent contamination of the contents by ambient moisture; and (e) mixing the reactants during the reaction in the reaction vessel until the reaction substantially subsides, whereby the polyurethane prepolymer adhesive is formed.
Claim 3
Dependent Claim
19 words
The process according to claim 1 further comprising the step of mixing into the polyol-isocyanate mixture a fire retardant.
Claim 4
Dependent Claim
20 words
The process according to claim 1 further comprising the step of mixing into the polyurethane prepolymer adhesive a reaction inhibitor.
Claim 5
Dependent Claim
19 words
The process according to claim 1 further comprising the step of mixing into the polyurethane prepolymer adhesive a plasticizer.
Claim 6
Dependent Claim
30 words
The process according to claim 1 further comprising the step of mixing into the polyol-isocyanate mixture a predetermined amount of a plasticizer, said predetermined amount ranging from 0-50%, by weight.
Claim 7
Dependent Claim
31 words
The process according to claim 1 further comprising the step of mixing into the polyurethane prepolymer adhesive a predetermined amount of a plasticizer, said predetermined amount ranging from 0-5%, by weight.
Claim 8
Dependent Claim
17 words
The process according to claim 6 wherein the delayed action catalyst is a hydroxylated quaternary ammonium carbonate.
Claim 9
Dependent Claim
31 words
The process according to claim 6 further comprising the step of mixing into a polyurethane prepolymer adhesive a predetermined amount of a surfactant, said predetermined amount ranging from 0-10%, by weight.
Claim 10
Dependent Claim
23 words
The process according to claim 1 further comprising the step of mixing into the polyurethane prepolymer adhesive a predetermined amount of a surfactant.
Claim 11
Dependent Claim
29 words
The process according to claim 8 or claim 9 wherein the surfactant is selected from the group consisting of polysiloxane polyoxyalkylene block copolymer surfactants and polyol derive organic surfactants.
Claim 12
Dependent Claim
110 words
The process according to claim 1 wherein the amount of catalyst is predetermined by a method comprising the steps of: (a) removing a 150 gram sample of the unreacted resin mixture from the reaction vessel; (b) adding an estimated amount of catalyst to the sample in a suitable vessel; (c) adjusting the estimated amount of catalyst to cause a temperature rise of the sample of 5 to 10 degrees F. within 5 to 10 minutes from the time of addition of catalyst to the sample; and (d) measuring the added amount of catalyst for the reaction vessel proportional to the amount of the sample which was determined in step (c).
Claim 13
Dependent Claim
30 words
The process according to claim 1 further comprising the step of mixing into the polyol reactant a predetermined amount of a co-catalyst, said predetermined amount ranging from 0-10%, by weight.
Claim 14
Dependent Claim
29 words
The process according to claim 1 wherein the excess active isocyanate content in the polyurethane prepolymer adhesive is in the range of approximately 5 to 20 percent by weight.
Claim 15
Dependent Claim
30 words
The process according to claim 1 wherein the step of isolating the mixed contents in the reaction vessel includes purging the contents of the reaction vessel with dry nonreactive gases.
Claim 16
Dependent Claim
33 words
The process according to claim 1 wherein the reaction vessel is a drum, and the step of mixing the reactants during the reaction is performed with a means for continuously rolling the drum.
Claim 17
Dependent Claim
25 words
The process according to claim 1 wherein the step of mixing the reactants during the reaction is performed by a means for stirring the reactants.
Claim 18
Dependent Claim
14 words
The process according to claim 3 wherein the reaction inhibitor comprises a Lewis acid.
Claim 19
Dependent Claim
14 words
The process according to claim 4 wherein the plasticizer comprises a light petroleum oil.
Claim 20
Dependent Claim
13 words
The process according to claim 1 wherein the catalyst is an organometallic compound.
Claim 21
Dependent Claim
25 words
The process according to claim 1 wherein the excess active isocyanate content in the polyurethane prepolymer adhesive is approximately 8 to 11.5 percent by weight.
Claim 22
Dependent Claim
25 words
The process according to claim 3 wherein the reaction inhibitor additive is selected from the group consisting of benzoyl chloride, acetyl chloride, and acetic anhydride.
Claim 23
Dependent Claim
21 words
The process according to claim 12 wherein the co-catalyst is treated with a drying agent to withdraw water from the co-catalyst.
Claim 24
Dependent Claim
23 words
The process according to claim 1 wherein the catalyst is selected from a group consisting of dibutyl tin dilaurate and di(phenylmercuric) dodecenyl succinate.
Claim 25
Dependent Claim
44 words
The process according to claim 1 further comprising the step of adding a predetermined amount of at least one co-catalyst to the polyol reactant, wherein the co-catalyst is a Lewis base selected from the group consisting of triethylenediamine, dimethyl ethanolamine, and N,N,N',N'-tetrakis (2-hydroxypropyl) ethylenediamine.
Claim 26
Dependent Claim
30 words
The process according to claim 1 wherein the polyol reactant is selected from the group consisting of dipropylene glycol, polypropylene glycol, polyethylene glycol, polybutadiene glycol, polyethylene triol and polypropylene triol.
Claim 27
Dependent Claim
34 words
The process according to claim 1 wherein the isocyanate reactant is selected from the group consisting of diphenylmethane diisocyanate; polymethylene polyphenylisocyanate; 2, 4 toluene diisocyanate; 2, 6 toluene diisocyanate; hexamethylene diisocyanate and isophorone diisocyanate.
Claim 28
Dependent Claim
35 words
The process according to claim 17 wherein the Lewis acid reaction inhibitor is selected from a group consisting of benzoyl chloride, acetyl chloride, and acetic anhydride, and the plasticizer comprises a light petroleum aromatic oil.
Claim 29
Dependent Claim
11 words
A polyurethane prepolymer adhesive manufactured by the process of claim 1.
Claim 30
Dependent Claim
11 words
A polyurethane prepolymer adhesive manufactured by the process of claim 6.
Claim 31
Dependent Claim
30 words
The process according to claim 1 wherein said predetermined amount of catalyst is added after said polyol reactant and said isocyanate reactant are mixed to give said uniform resin mixture.
References Cited (Backward Citations)
US2650212A
Cited
US2692873A
Cited
US2801648A
Cited
US3196026A
Cited
US3814736A
Cited
US3993652A
Cited
US3919173A
Cited
US3980594A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-25 | 1987-01-24 | 1987-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-25 | 1991-01-24 | 1991-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-25 | 1995-01-24 | 1995-07-26 | $7700.00 | Window Closed / Lapsed |