Coating and primer formulation on the basis of a copolymer of tetrafluoroethylene and a perfluoro-(alkylvinyl) ether, and use thereof
Assignee: Hoechst AG
•
Filing: 1981-09-10
•
Granted: 1983-07-26
•
Expires: 2001-09-10
Abstract
Abstract Coating formulations having improved adhesion are described which are especially suitable as primer for top coats of fluorocarbon polymers, which comprise (a) a copolymer of tetrafluoroethylene units, units of a perfluoroalkylvinyl ether and optionally units of hexafluoropropylene or vinylidene fluoride, (b) optionally dispersed polytetrafluoroethylene particles in addition, (c) a mixture of lithium hydroxide and suspended fine-particle pyrogenic SiO 2 , and (d) water as liquid carrier. The coating formulations are applied according to known methods to substrates such as metals, glass or ceramic surfaces. They may be used as single-layer systems without top coat, or as primer, the top coat being applicable immediately after a short-time drying only. Application fields are the coating of household equipment or technical apparatus, where a high-grade adhesion onto the substrate, combined with anti-adhesive properties and a smooth surface are obtained.
Inventors
- 👤 Gerhard Gebauer
- 👤 Franz Mayer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:12
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/08; B05D5/083; C; C09; C09D; C09D127/00; C09D127/02; C09D127/12; C09D127/18; B05D2401/00; B05D2401/20; C08; C08L; C08L2205/00; C08L2205/02; C08L27/00; C08L27/02; C08L27/12; C08L27/18; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/3154; Y10T428/31544
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
209 words
A method for improving the coating of a substrate with a fluoropolymer which comprises applying a primer composition and subsequently without an intermediate heat treatment for sintering applying a topcoat of a tetrafluoroethylene homopolymer or copolymer wherein the improvement comprises applying a primer composition consisting essentially of (a) from 100 to 20 weight %, relative to the total polymer solids of the components (a) and (b), of a copolymer of copolymerized tetrafluoroethylene units; from 0.5 to 11 weight % of copolymerized units of a perfluoro(alkylvinyl) ether of the formula CF 2 ═CF--OR, in which R is a perfluoroalkyl radical having from 1 to 10 carbon atoms; and from 0 to 12 weight % of copolymerized units of hexafluoropropylene or vinylidene fluoride, each relative to the total weight of the copolymer; (b) from 0 to 80 weight %, relative to the total polymer solids of components (a) and (b), of dispersed polytetrafluoroethylene particles having a mean grain size of from 0.05 to 30 μm; (c) from 10 to 70 weight % of the weight sum of (a) plus (b) plus (c) of lithium hydroxide and suspended, fine-particle SiO 2 produced by thermal treatment; the molar ratio LiOH: SiO 2 being from 1:0.5 to 1:30; and (d) water as liquid carrier.
Claim 2
Independent Claim
209 words
A method for improving the coating of a substrate with a fluoropolymer which comprises applying a primer composition and subsequently without an intermediate heat treatment for sintering applying a topcoat of a tetrafluoroethylene homopolymer or copolymer wherein the improvement comprises applying a primer composition consisting essentially of (a) from 100 to 20 weight %, relative to the total polymer solids of the components (a) and (b), of a copolymer of copolymerized tetrafluoroethylene units; from 0.5 to 11 weight % of copolymerized units of a perfluoro(alkylvinyl) ether of the formula CF 2 ═CF--OR, in which R is a perfluoroalkyl radical having from 1 to 10 carbon atoms; and from 0 to 12 weight % of copolymerized units of hexafluoropropylene or vinylidene fluoride, each relative to the total weight of the copolymer; (b) from 0 to 80 weight %, relative to the total polymer solids of components (a) and (b), of dispersed polytetrafluoroethylene particles having a mean grain size of from 0.05 to 30 μm; (c) from 10 to 70 weight % of the weight sum of (a) plus (b) plus (c) of lithium hydroxide and suspended, fine-particle SiO 2 produced by thermal treatment; the molar ratio LiOH: SiO 2 being from 1:0.5 to 1:30; and (d) water as liquid carrier.
Claim 3
Dependent Claim
44 words
The method of claim 1, wherein the component (a) of the primer composition in the copolymer contains from 0.4 to 6.5 weight % of copolymerized units of hexafluoropropylene and 1.5 to 6.0 weight % of copolymerized units of perfluoro(n-propylvinyl) ether and copolymerized tetrafluoroethylene units.
Claim 4
Dependent Claim
26 words
The method of claim 1, wherein the weight sum of components (a), (b) and (c) of the primer composition is from 12 to 60 weight percent.
Claim 5
Dependent Claim
15 words
The method of claim 1, wherein the primer composition contains in addition pigments and fillers.
References Cited (Backward Citations)
US3694392A
Cited
US4252859A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-25 | 1987-01-24 | 1987-07-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-25 | 1991-01-24 | 1991-07-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-25 | 1995-01-24 | 1995-07-26 | $7700.00 | Window Closed / Lapsed |