ZnS:Mn Thin-film electroluminescent element with memory function
Assignee: Sharp Corp
•
Filing: 1977-05-18
•
Granted: 1983-07-19
•
Expires: 1997-05-18
Abstract
Abstract A ZnS thin-film electroluminescent element which exhibits the hysteresis phenomenon within the light emission versus applied voltage characteristics, the electric current versus applied alternating voltage characteristics, or the electric current phase versus applied alternating voltage characteristics. The ZnS element comprises a ZnS EL thin-film including Mn serving as a luminescent center with a concentration of 0.05-5.0 wt. %, and a pair of dielectric layers made of rare earth oxides or oxides groups of III, IV and V of the Periodic Table. The EL thin-film is sandwiched between the pair of the dielectric layers. The ZnS EL thin-film is made by applying the electron-beam heating evaporation technology to a ZnS pellet.
Inventors
- 👤 Mikio Takeda
- 👤 Yoshinobu Kakihara
- 👤 Masaru Yoshida
- 👤 Yukihiko Nakata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:32
CPC Classifications
H; H05; H05B; H05B33/00; H05B33/12; H05B33/14; C; C09; C09K; C09K11/00; C09K11/08; C09K11/57; C09K11/572; C09K11/574
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
129 words
A ZnS:Mn thin-film electroluminescent element containing a hysteresis memory function which comprises a ZnS:Mn thin-film electroluminescent layer containing ZnS polycrystalline grains having a diameter of 0.05 to 0.2μ and containing Mn in a concentration of 0.05 to 5.0 weight percent, said Mn serving as a luminescent center, said electroluminescent layer being sandwiched between a pair of dielectric layers, at least one of the dielectric layers being made of Y 2 O 3 , and first and second electrodes provided on the respective dielectric layers, said ZnS:Mn electroluminescent layer having a thickness of 0.4-2.0μ and a dielectric constant at 1 KHz of about 10 to 22, a loss tangent at 1 KHz of about 1 to 4×10 3 , and a breakdown strength of about 3 to 4×10 6 V/cm.
Claim 2
Dependent Claim
129 words
A ZnS:Mn thin-film electroluminescent element containing a hysteresis memory function which comprises a ZnS:Mn thin-film electroluminescent layer containing ZnS polycrystalline grains having a diameter of 0.05 to 0.2μ and containing Mn in a concentration of 0.05 to 5.0 weight percent, said Mn serving as a luminescent center, said electroluminescent layer being sandwiched between a pair of dielectric layers, at least one of the dielectric layers being made of Y 2 O 3 , and first and second electrodes provided on the respective dielectric layers, said ZnS:Mn electroluminescent layer having a thickness of 0.4-2.0μ and a dielectric constant at 1 KHz of about 10 to 22, a loss tangent at 1 KHz of about 1 to 4×10 3 , and a breakdown strength of about 3 to 4×10 6 V/cm.
Claim 3
Dependent Claim
127 words
A ZnS:Mn thin-film electroluminescent element containing a hysteresis memory function which comprises a ZnS:Mn thin-film electroluminescent layer containing ZnS polycrystalline grains having a diameter of 0.05 to 0.2μ and containing Mn in a concentration of 0.05 to 5.0 weight percent, said Mn serving as a luminescent center, said electroluminescent layer being sandwiched between a pair of dielectric layers, at least one of the dielectric layers being made of ZrO 2 , and first and second electrodes provided on the respective dielectric layers, said ZnS:Mn electroluminescent layer having a thickness of 0.4-2.0μ and a dielectric constant at 1 KHz of about 10 to 22, a loss tangent at 1 KHz of about 1 to 4×10 3 , and a breakdown strength of about 3 to 4×10 6 V/cm.
Claim 4
Dependent Claim
127 words
A ZnS:Mn thin-film electroluminescent element containing a hysteresis memory function which comprises a ZnS:Mn thin-film electroluminescent layer containing ZnS polycrystalline grains having a diameter of 0.05 to 0.2μ and containing Mn in a concentration of 0.05 to 5.0 weight percent, said Mn serving as a luminescent center, said electroluminescent layer being sandwiched between a pair of dielectric layers, at least one of the dielectric layers being made of ZrO 2 , and first and second electrodes provided on the respective dielectric layers, said ZnS:Mn electroluminescent layer having a thickness of 0.4-2.0μ and a dielectric constant at 1 KHz of about 10 to 22, a loss tangent at 1 KHz of about 1 to 4×10 3 , and a breakdown strength of about 3 to 4×10 6 V/cm.
Claim 5
Dependent Claim
129 words
A ZnS:MN thin-film electroluminescent element containing a hysteresis memory function which comprises a ZnS:Mn thin-film electroluminescent layer containing ZnS polycrystalline grains having a diameter of 0.05 to 0.2μ and containing Mn in a concentration of 0.05 to 5.0 weight percent, said Mn serving as a luminescent center, said electroluminescent layer being sandwiched between a pair of dielectric layers, at least one of the dielectric layers being made of Dy 2 O 3 , and first and second electrodes provided on the respective dielectric layers, said ZnS:Mn electroluminescent layer having a thickness of 0.4-2.0μ and a dielectric constant at 1 KHz of about 10 to 22, a loss tangent at 1 KHz of about 1 to 4×10 3 , and a breakdown strength of about 3 to 4×10 6 V/cm.
Claim 6
Dependent Claim
129 words
A ZnS:MN thin-film electroluminescent element containing a hysteresis memory function which comprises a ZnS:Mn thin-film electroluminescent layer containing ZnS polycrystalline grains having a diameter of 0.05 to 0.2μ and containing Mn in a concentration of 0.05 to 5.0 weight percent, said Mn serving as a luminescent center, said electroluminescent layer being sandwiched between a pair of dielectric layers, at least one of the dielectric layers being made of Dy 2 O 3 , and first and second electrodes provided on the respective dielectric layers, said ZnS:Mn electroluminescent layer having a thickness of 0.4-2.0μ and a dielectric constant at 1 KHz of about 10 to 22, a loss tangent at 1 KHz of about 1 to 4×10 3 , and a breakdown strength of about 3 to 4×10 6 V/cm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-18 | 1987-01-17 | 1987-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-18 | 1991-01-17 | 1991-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-18 | 1995-01-17 | 1995-07-19 | $7700.00 | Window Closed / Lapsed |