High solids coatings with enhanced flexibility and impact strength

Claim 2

A thermosetting coating composition exhibiting improved flexibility and impact strength and having excellent weatherability and comprising: (A) a modified hydroxy acrylic copolymer which is the stepwise reaction product of: (i) a copolymer bearing pendant hydroxyl groups and having a number average molecular weight (M n ) of between about 1000-5000, said copolymer being prepared from (a) between about 5 and about 40 weight percent of monoethylenically unsaturated hydroxy alkyl ester of the formula CH 2 ═CR 1 --COOR 2 wherein R 1 is H or an alkyl group and R 2 is a hydroxy alkyl group and (b) between about 95-60 weight percent of other monoethylenically unsaturated monomers; (ii) dicarboxylic acid anhydride comprising at least about 50 percent by weight of an alkyl hexahydrophthalic anhydride, wherein (i) and (ii) are reacted in an amount sufficient to esterify between about 30 and about 100 percent of said pendant hydroxyl groups of said copolymer thereby generating pendant carboxyl groups; and (iii) a monoepoxide functional monomer comprising at least about 90 percent by weight C 2 -C 10 monoepoxide functional monomers, wherein said monomer is reacted with said pendant carboxyl groups of the polymer reaction product of (i) and (ii) in an amount so as to provide at least about 1.0 equivalent of epoxide groups per equivalent of said pendant carboxyl groups to generate pendant hydroxyl groups; (B) an amine-aldehyde crosslinking agent; (C) 0-50 weight percent based on the total weight of (A), (B) (C) and (D) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150 and about 6000; and (D) solvent said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxyl functionality included in said composition either as a hydroxyl group on said modified hydroxy acrylic copolymer or as a hydroxyl group on said hydroxy functional additive.

Claim 3

A coating composition according to claim 1, wherein said monoethylenically unsaturated hydroxy alkyl ester comprises C 5 -C 7 hydroxy alkyl acrylates, C 6 -C 8 hydroxy alkyl methacrylates, or mixtures thereof.

Claim 4

A coating composition according to claim 2, wherein said other monoethylenically unsaturated monomers comprise acrylates, other vinyl monomer, or mixtures of said acrylates and other vinyl monomers.

Claim 5

A coating composition according to claim 1, wherein said alkyl group of said alkyl hexahydrophthalic anhydride comprises a lower alkyl group having up to about seven carbons.

Claim 6

A coating composition according to claim 1, wherein said dicarboxylic acid anhydride comprises at least 80 percent by weight of an alkyl hexahydrophthalic anhydride.

Claim 7

A coating composition according to claims 4 or 5, wherein said alkyl hexahydrophthalic anhydride is methyl hexahydrophthalic anhydride.

Claim 8

A coating composition according to claim 1, wherein up to 50 percent by weight of said dicarboxylic acid anhydride employed in the preparation of said copolymer comprises an anhydride selected from the group consisting of hexahydrophthalic anhydride, 2-dodecene-1-ylsuccinic anhydride, tetrahydrophthalic anhydride, methyl tetrahydrophthalic anhydride, camphoric anhydride, and mixtures of the above.

Claim 9

A coating composition according to claim 1, wherein said C 2 -C 10 monoepoxide functional monomers comprises a monomer selected from the group consisting of ethylene oxide, propylene oxide, epichlorohydrin, glycidol, 1,2-epoxy butane, 1,2 epoxy-1 butene, 1,2-epoxyethyl benzene, 1,2 epoxy-3-phenoxy propane, and mixtures of the above.

Claim 10

A coating composition according to claim 8, wherein said C 2 -C 10 monoepoxide functional monomer is a C 3 -C 7 monomer.

Claim 11

A coating composition according to claim 9, wherein said C 3 -C 7 monomer contains terminal epoxide functionality.

Claim 12

A coating composition according to claim 1, wherein said monoepoxide functional monomer other than said C 2 -C 10 monoepoxide monomer comprises a monomer selected from the group consisting of epoxidized fatty esters, 2,3-epoxypropyl octyl ether, 1,2-epoxy-3,3,3-trichloropropane, 1,2-epoxytetradecane, 1,2-epoxycyclodecane, exo-2,3-epoxynorbornane, 1,4-epoxy-cyclohexane, 1,2-epoxy-3-floropropane, and mixtures of the above.

Claim 13

A coating composition according to claim 1, wherein said amine-aldehyde crosslinking agent is selected from the group consisting of condensation products of formaldehyde with melamine, substituted melamine, urea, benzoquanamine and substituted benzoguanamine and mixtures of said condensation products and is included in an amount sufficient to provide between about 0.75 and about 3.75 equivalent of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in said composition, either as a hydroxyl group on said modified hydroxy acrylic copolymer or as a hydroxyl group on said hydroxy functional additive.

Claim 14

A coating composition according to claim 1, wherein said hydroxy functional additive is a polyol selected from the group consisting of (i) hydroxy functional polyesters, (ii) hydroxy functional polyethers, (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers formed from monoethylenically unsaturated monomers, one or more of which bears hydroxy functionality and which is included in said copolymer in amounts ranging from about 10 to about 50 weight percent of said copolymer, and (vi) mixtures of (i)-(v).

Claim 15

A coating composition according to claim 1, which further comprises up to 15 weight percent based on the total weight of the composition of a flow control additive.

Claim 16

A coating composition according to claim 1, wherein said dicarboxylic acid anhydride consists of methyl hexahydrophthalic anhydride and said monoepoxide functional monomer consists of a C 2 -C 10 monoepoxide functional monomer.

Claim 17

A modified hydroxy acrylic copolymer which is the stepwise reaction product of: (i) a copolymer bearing pendant hydroxyl groups having a number average molecular weight (M n ) of between about 1000-5000, said copolymer being prepared from (a) between about 5 and about 40 weight percent of monoethylenically unsaturated hydroxy alkyl ester having formula CH 2 ═CR 1 --COOR 2 wherein R 1 is H or an alkyl group and R 2 is a hydroxy alkyl group and (b) between about 95-60 weight percent of other monoethylenically unsaturated monomers; (ii) dicarboxylic acid anhydride comprising at least about 50 percent by weight of an alkyl hexahydrophthalic anhydride, wherein (i) and (ii) are reacted in an amount sufficient to esterify between about 30 and about 100 percent of said pendant hydroxyl groups of said copolymer thereby generating pendant carboxyl groups; and (iii) a monoepoxide functional monomer comprising at least about 90 percent by weight C 2 -C 10 monoepoxide functional monomers, wherein said monomer is reacted with said pendant carboxyl groups of the polymer reaction product of (i) and (ii) in an amount so as to provide at least about 1.0 equivalent of epoxide groups per equivalent of said pendant carboxyl groups to generate pendant hydroxyl groups.

Claim 18

A modified hydroxy acrylic copolymer which is the stepwise reaction product of: (i) a copolymer bearing pendant hydroxyl groups having a number average molecular weight (M n ) of between about 1000-5000, said copolymer being prepared from (a) between about 5 and about 40 weight percent of monoethylenically unsaturated hydroxy alkyl ester having formula CH 2 ═CR 1 --COOR 2 wherein R 1 is H or an alkyl group and R 2 is a hydroxy alkyl group and (b) between about 95-60 weight percent of other monoethylenically unsaturated monomers; (ii) dicarboxylic acid anhydride comprising at least about 50 percent by weight of an alkyl hexahydrophthalic anhydride, wherein (i) and (ii) are reacted in an amount sufficient to esterify between about 30 and about 100 percent of said pendant hydroxyl groups of said copolymer thereby generating pendant carboxyl groups; and (iii) a monoepoxide functional monomer comprising at least about 90 percent by weight C 2 -C 10 monoepoxide functional monomers, wherein said monomer is reacted with said pendant carboxyl groups of the polymer reaction product of (i) and (ii) in an amount so as to provide at least about 1.0 equivalent of epoxide groups per equivalent of said pendant carboxyl groups to generate pendant hydroxyl groups.

Claim 19

A modified hydroxy acrylic copolymer according to claim 16, wherein said monoethylenically unsaturated hydroxy alkyl ester comprises C 5 -C 7 hydroxy alkyl acrylates, C 6 -C 8 hydroxy alkyl methacrylates, or mixtures thereof.

Claim 20

A modified hydroxy acrylic copolymer according to claim 16, wherein said other monoethylenically unsaturated monomers comprise acrylates, other vinyl monomer, or mixtures of said acrylates and other vinyl monomers.

Claim 21

A modified hydroxy acrylic copolymer according to claim 16, wherein said alkyl group of said alkyl hexahydraphthalic anhydride comprises a lower alkyl group having up to about seven carbons.

Claim 22

A modified hydroxy acrylic copolymer according to claim 16, wherein said dicarboxylic acid anhydride comprises at least 80 percent by weight of an alkyl hexahydrophthalic anhydride.

Claim 23

A modified hydroxy acrylic copolymer according to claims 19 or 20, wherein said alkyl hexahydrophthalic anhydride is methyl hexahydrophthalic anhydride.

Claim 24

A modified hydroxy acrylic copolymer according to claim 16, wherein up to about 50 percent by weight of said dicarboxylic acid anhydride employed in the preparation of said copolymer comprises an anhydride selected from the group consisting of hexahydrophthalic anhydride, 2-dodecene-1-ylsuccinic anhydride, tetrahydrophthalic anhydride, methyl tetrahydrophthalic anhydride, camphoric anhydride, and mixtures of the above.

Claim 25

A modified hydroxy acrylic copolymer according to claim 16, wherein said C 2 -C 10 monoepoxide functional monomers comprises a monomer selected from the group consisting of ethylene oxide, propylene oxide, epichlorohydrin, glycidol, 1,2-epoxy butane, 1,2 epoxy-1-butene, 1,2-epoxyethyl benzene, 1,2-epoxy-3-phenoxy propane, and mixtures of the above.

Claim 26

A modified hydroxy acrylic copolymer according to claim 23, wherein said C 2 -C 10 nonoepoxide functional monomer is a C 3 -C 7 monomer.

Claim 27

A modified hydroxy acrylic copolymer according to claim 24, wherein said C 3 -C 7 monomer contains terminal epoxide functionality.

Claim 28

A modified hydroxy acrylic copolymer according to claim 16, wherein said monoepoxide functional monomer other than said C 2 -C 10 monoepoxide monomer comprises a monomer selected from the group consisting of epoxidized fatty esters, 2,3-epoxypropyloctyl ether, 1,2-epoxy-3,3,3-trichloropropane, 1,2-epoxytetradecane, 1,2-epoxycyclodecane, exo-2,3-epoxynorbornane, 1,4-epoxycyclohexane, 1,2-epoxy-3-fluoropropane and mixtures of the above.

Claim 29

A high solids thermosetting coating composition which contains greater than about 60 percent by weight of nonvolatile solids and which except for pigments and other nonreactive components, consists essentially of: (A) a modified hydroxy acrylic copolymer which is the stepwise reaction product of: (i) a copolymer bearing pendant hydroxyl groups and having a number average molecular weight (M n ) of between about 1000-5000, said copolymer being prepared from (a) between about 5 and about 40 weight percent of monoethylenically unsaturated hydroxy alkyl ester having the formula CH 2 ═CR 1 --COOR 2 wherein R 1 is H or an alkyl group and R 2 is a hydroxy alkyl group and (b) between about 95-60 weight percent of other monoethylenically unsaturated monomers; (ii) dicarboxylic acid anhydride comprising at least about 50 percent by weight of an alkyl hexahydrophthalic anhydride, wherein (i) and (ii) are reacted in an amount sufficient to esterify between about 30 and about 100 percent of said pendant hydroxyl groups of said copolymer thereby generating pendant carboxyl groups; and (iii) a monoepoxide functional monomer comprising at least about 90 percent by weight C 2 -C 10 monoepoxide functional monomers, wherein said monomer is reacted with said pendant carboxyl groups of the polymer reaction product of (i) and (ii) in an amount so as to provide at least about 1.0 equivalent of epoxide groups per equivalent of said pendant carboxyl groups to generate pendant hydroxyl groups; (B) an amine-aldehyde crosslinking agent; (C) 0-50 weight percent based on the total weight of (A), (B), (C), (D) and (E) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150 and about 6000, (D) solvent; and (E) up to 15 weight percent based on the total weight of (A), (B), (C), (D) and (E) of a flow control additive, said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen cross-linking functionality for each equivalent of hydroxyl functionality included in said composition either as a hydroxyl group on said modified hydroxy acrylic copolymer or as a hydroxyl group on said hydroxy functional additive.

Claim 30

A high solids thermosetting coating composition which contains greater than about 60 percent by weight of nonvolatile solids and which except for pigments and other nonreactive components, consists essentially of: (A) a modified hydroxy acrylic copolymer which is the stepwise reaction product of: (i) a copolymer bearing pendant hydroxyl groups and having a number average molecular weight (M n ) of between about 1000-5000, said copolymer being prepared from (a) between about 5 and about 40 weight percent of monoethylenically unsaturated hydroxy alkyl ester having the formula CH 2 ═CR 1 --COOR 2 wherein R 1 is H or an alkyl group and R 2 is a hydroxy alkyl group and (b) between about 95-60 weight percent of other monoethylenically unsaturated monomers; (ii) dicarboxylic acid anhydride comprising at least about 50 percent by weight of an alkyl hexahydrophthalic anhydride, wherein (i) and (ii) are reacted in an amount sufficient to esterify between about 30 and about 100 percent of said pendant hydroxyl groups of said copolymer thereby generating pendant carboxyl groups; and (iii) a monoepoxide functional monomer comprising at least about 90 percent by weight C 2 -C 10 monoepoxide functional monomers, wherein said monomer is reacted with said pendant carboxyl groups of the polymer reaction product of (i) and (ii) in an amount so as to provide at least about 1.0 equivalent of epoxide groups per equivalent of said pendant carboxyl groups to generate pendant hydroxyl groups; (B) an amine-aldehyde crosslinking agent; (C) 0-50 weight percent based on the total weight of (A), (B), (C), (D) and (E) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150 and about 6000, (D) solvent; and (E) up to 15 weight percent based on the total weight of (A), (B), (C), (D) and (E) of a flow control additive, said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen cross-linking functionality for each equivalent of hydroxyl functionality included in said composition either as a hydroxyl group on said modified hydroxy acrylic copolymer or as a hydroxyl group on said hydroxy functional additive.

Claim 31

A high solids coating composition according to claim 27, wherein said other monoethylenically unsaturated hydroxy alkyl ester is selected from the group consisting of C 5 -C 7 hydroxy alkyl acrylates, C 6 -C 8 hydroxy alkyl methacrylates, and mixtures thereof.

Claim 32

A high solids coating composition according to claim 28, wherein said other monoethylenically unsaturated monomers are selected from the group consisting of acrylates, other vinyl monomer, and mixtures of said acrylates and other vinyl monomers.

Claim 33

A high solids coating composition according to claim 27, wherein said alkyl group of said alkyl hexahydrophthalic anhydride comprises a lower alkyl group having up to about seven carbons.

Claim 34

A high solids coating composition according to claim 27, wherein said dicarboxylic acid anhydride comprises at least 80 percent by weight of an alkyl hexahydrophthalic anhydride.

Claim 35

A high solids coating composition according to claims 30 or 31, wherein said alkyl hexahydrophathalic anhydride is methyl hexahydrophthalic anhydride.

Claim 36

A high solids coating composition according to claim 27, wherein up to 50 percent by weight of said dicarboxylic acid anhydride employed in the preparation of said copolymer is selected from the group consisting of hexahydrophthalic anhydride, 2-dodecene-1-ylsuccinic anhydride, tetrahydrophthalic anhydride, methyl tetrahydrophthalic anhydride, camphoric anhydride, and mixtures of the above.

Claim 37

A high solids coating composition according to claim 27, wherein said C 2 -C 10 monoepoxide functional monomers are selected from the group consisting of ethylene oxide, propylene oxide, epichlorohydrin, glycidol, 1-2-epoxy butane, 1,2 epoxy-1 butene, 1,2-epoxyethyl benzene, 1,2 epoxy-3-phenoxy propane, or mixtures of the above.

Claim 38

A high solids coating composition according to claim 34, wherein said C 2 -C 10 monoepoxide functional monomer is a C 3 -C 7 monomer.

Claim 39

A high solids coating composition according to claim 35, wherein said C 3 -C 7 monomer contains terminal epoxide functionality.

Claim 40

A high solids coating composition according to claim 27 wherein said monoepoxide functional monomer other than said C 2 -C 10 monoepoxide monomer is selected from the group consisting of epoxidized fatty esters, 2,3-epoxypropyl octyl ether, 1,2-epoxy 3,3,3-trichloropropane, 1,2-epoxytetradecane, 1,2-epoxycyclodecane, exo-2,3-epoxynorbornane, 1,4-epoxycyclohexane, 1,2 epoxy-3-fluoropropane, or mixtures of the above.

Claim 41

A high solids coating composition according to claim 27, wherein said amine-aldehyde crosslinking agent is selected from the group consisting of condensation products of formaldehyde with melamine, substituted melamine, urea, benzoquanamine and substituted benzoguanamine and mixtures of said condensation products and is included in an amount sufficient to provide between about 0.75 and about 3.75 equivalent of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in said composition either as a hydroxyl group on said modified hydroxy acrylic copolymer or as a hydroxyl group on said hydroxy functional additive.

Claim 42

A high solids coating composition according to claim 27, wherein said hydroxy functional additive is a polyol selected from the group consisting of (i) hydroxy functional polyesters, (ii) hydroxy functional polyethers, (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers formed from monoethylenically unsaturated monomers, one or more of which bears hydroxy functionality and which is included in said copolymer in amounts ranging from about 10 to about 50 weight percent of said copolymer, and (vi) mixtures of (i)-(v).

Claim 43

A high solids coating composition according to claim 27, wherein said dicarboxylic acid anhydride consists of methyl hexahydrophthalic anhydride and said monoepoxide functional monomer consists of a C 2 -C 10 monoepoxide functional monomer.