Patent US4394455A successfully refreshed from Google Patents.
US4394455A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Spinel slip casting composition and articles
Assignee: Dow Chemical Co
•
Filing: 1981-08-31
•
Granted: 1983-07-19
•
Expires: 2001-08-31
Abstract
Abstract A spinel containing slip-casting composition, a method for preparing the spinel slip-casting composition and a method for casting the slip into usable forms are described. The spinel employed to prepare the castable slips is a pre-calcined spinel prepared in the manner of copending application Ser. No. 184,189, filed Sept. 4, 1980, which is ball-milled with water, then mixed with a deflocculant at pH 9 or below and optionally with a molding aid. The slurry or "slip" is cast into a mold porous to water until the desired thickness of solid has been obtained and the excess "slip" decanted or otherwise withdrawn from the mold i.e., drain cast method or the "slip" is solid cast and dried to produce a green solid casting. The green shape is retained in the mold until it gains green strength, 1 hour to 5 days, and thereafter placed in an oven wherein it is fired to above about 1400 DEG C. for from 1 to 20 hours until it has reached its maximum density of between about 55 and 99 percent of theoretical. Also disclosed are mixtures of pre-fired spinels with calcined spinels of various heat histories to yield more durable green forms. In addition there is disclosed slips prepared from mixtures of different spinel compositions.
Inventors
- 👤 Dale M. Bertelsman
- 👤 William M. Eckert
- 👤 Stanley J. Morrow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:03
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/44; C04B35/443; C01; C01F; C01F7/00; C01F7/02; C01F7/16; C01F7/162; C01F7/78; C01G; C01G37/00; C01G37/006; C01P; C01P2002/00; C01P2002/30; C01P2002/32; C01P2002/50; C01P2002/52; C01P2002/54; C01P2006/00; C01P2006/10; C01P2006/16; C01P2006/80; C01P2006/82
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
61 words
A casting composition comprising (A) 10 to about 60 percent by weight of a powder of a spinel prepared by coprecipitation of metal hydroxides or metal compound convertable to the metal hydroxides, dried and calcined to between about 400° and 1400° C.; and (B) the balance water and a sufficient deflocculating agent to form a substantially stable dispersion of the powder.
Claim 2
Dependent Claim
61 words
A casting composition comprising (A) 10 to about 60 percent by weight of a powder of a spinel prepared by coprecipitation of metal hydroxides or metal compound convertable to the metal hydroxides, dried and calcined to between about 400° and 1400° C.; and (B) the balance water and a sufficient deflocculating agent to form a substantially stable dispersion of the powder.
Claim 3
Dependent Claim
91 words
A casting composition comprising (A) 10 to about 60 percent by weight of a spinel powder (1) at least 10 percent of which is a coprecipitate precursor calcined at a temperature greater than 900° and up to 1400° C.; (2) up to 90 percent of a 1500° C. and above fired precalcined coprecipitate precursor; and (3) the balance, if any, of a coprecipitate precursor calcined at a temperature of from 400° to 900° C.; and (B) the balance being water and sufficient deflocculant to form a stable dispersion of the powders.
Claim 4
Dependent Claim
91 words
A casting composition comprising (A) 10 to about 60 percent by weight of a spinel powder (1) at least 10 percent of which is a coprecipitate precursor calcined at a temperature greater than 900° and up to 1400° C.; (2) up to 90 percent of a 1500° C. and above fired precalcined coprecipitate precursor; and (3) the balance, if any, of a coprecipitate precursor calcined at a temperature of from 400° to 900° C.; and (B) the balance being water and sufficient deflocculant to form a stable dispersion of the powders.
Claim 5
Dependent Claim
70 words
A slip casting composition comprising (A) 0 to 25 weight percent of a spinel powder fired to about 1500° C.; (B) 10 to 50 weight percent of a spinel powder calcined to between about 900° and 1400° C.; (C) 25 to 90 percent by weight of water; (D) 0.2 to 4 percent by weight of a mold aid; and (E) 0.1 to 4 percent by weight of a deflocculating agent.
Claim 6
Dependent Claim
70 words
A slip casting composition comprising (A) 0 to 25 weight percent of a spinel powder fired to about 1500° C.; (B) 10 to 50 weight percent of a spinel powder calcined to between about 900° and 1400° C.; (C) 25 to 90 percent by weight of water; (D) 0.2 to 4 percent by weight of a mold aid; and (E) 0.1 to 4 percent by weight of a deflocculating agent.
Claim 7
Dependent Claim
18 words
The composition of claim 1, 2 or 3 wherein said spinel is a MgAl 2 O 4 spinel.
Claim 8
Dependent Claim
18 words
The composition of claim 4 wherein said mold aid is an alginate and said deflocculant is a polyelectrolyte.
Claim 9
Dependent Claim
20 words
The composition of claim 1, 2 or 3 wherein said spinel is a Mg(Al x Cr 2-x )O 4 spinel.
Claim 10
Dependent Claim
25 words
Furnaceware prepared by slip casting the composition of claim 4 and firing the so cast shape at above 1500° C. for one to twenty hours.
Claim 11
Dependent Claim
25 words
Furnaceware prepared by slip casting the composition of claim 5 and firing the so cast shape at above 1500° C. for one to twenty hours.
Claim 12
Dependent Claim
25 words
Furnaceware prepared by slip casting the composition of claim 6 and firing the so cast shape at above 1500° C. for one to twenty hours.
Claim 13
Dependent Claim
31 words
Solid shapes prepared by solid casting a slurry of the composition of claim 4 and firing the dried shape so cast to above 1500° C. for from one to twenty hours.
Claim 14
Dependent Claim
31 words
Solid shapes prepared by solid casting a slurry of the composition of claim 5 and firing the dried shape so cast to above 1500° C. for from one to twenty hours.
Claim 15
Dependent Claim
31 words
Solid shapes prepared by solid casting a slurry of the composition of claim 6 and firing the dried shape so cast to above 1500° C. for from one to twenty hours.
Claim 16
Dependent Claim
92 words
The casting composition of claim 1, wherein at least 10 weight percent of spinel powder is a coprecipitate precursor calcined at a temperature of from 900° C. to 1400° C.; up to 90 weight percent of the precalcined coprecipitate precursor is sintered at a temperature above 1500° C.; and the balance, if any, is a magnesium/aluminum coprecipitate comprised of a layered crystallite having the structure ##STR1## and at least one segregated phase of the formula AlO(OH) and/or Al(OH) 3 wherein the overall stoichiometry of the precipitate is MgAl 2 (OH) 8 .
References Cited (Backward Citations)
GB697231A
Cited
US2618566A
Cited
US2805167A
Cited
US3530209A
Cited
US3516839A
Cited
US3531308A
Cited
US3544266A
Cited
US3567472A
Cited
SU449021A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-18 | 1987-01-17 | 1987-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-18 | 1991-01-17 | 1991-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-18 | 1995-01-17 | 1995-07-19 | $7700.00 | Window Closed / Lapsed |