Aqueous sizing composition and glass fibers made therewith for reinforcing thermosetting polymers

Claim 2

An aqueous sizing composition for glass fibers to yield sized glass fiber strands useful in reinforcing thermosetting polymers, comprising: (a) poly(vinylacetate) silane copolymer, (b) epoxy polymer, (c) one or more glass fiber lubricants, (d) an organo silane coupling agent selected from the group consisting of amino-organo-silane coupling agents, lubricant modified amino-organo-silane coupling agents, epoxy-containing silane coupling agents and a mixture of two or more of these agents, (e) one or more nonionic surfactants, (f) polyethylene-containing polymer in an amount of 0 to about 25 weight percent of the solids of the aqueous sizing composition, (g) wax in an amount of about 0 to about 5 weight percent of the solids of the aqueous sizing composition where an amount of the polyethylene-containing polymer is present when the wax is absent and an amount of wax is present if the polyethylene-containing polymer is absent and when both are present, the weight ratio of the polyethylene-containing polymer to wax is in the range of about 25:1 to about 1:25, (h) organic hydrocarbon acid to give the composition a pH in the range of about 4 to about 9, and (i) water to give a total solids content in the range of about 1 to about 30 weight percent.

Claim 3

Aqueous sizing composition of claim 1, wherein the poly(vinylacetate) silane copolymer is a vinylacetate-organo-silane copolymer having an insolubility in styrene and a silane level of from about 1 to about 7 weight percent.

Claim 4

Aqueous sizing composition of claim 1 or 2, wherein the amount of the poly(vinylacetate) silane copolymer is in the range of about 1 to about 12 weight percent of the aqueous sizing composition.

Claim 5

Aqueous sizing composition of claim 1 or 2, wherein the amount of the poly(vinylacetate) silane copolymer is in the range of about 1 to about 12 weight percent of the aqueous sizing composition and the amount is always greater than the amount of the epoxy polymer.

Claim 6

Aqueous sizing composition of claim 1, wherein the epoxy polymer has a molecular weight in the range of about 170 to about 900.

Claim 7

Aqueous sizing composition of claim 1 or 5, wherein the amount of the epoxy polymer present is in the range of about 1 to about 60 weight percent of the solids of the aqueous sizing composition.

Claim 8

Aqueous sizing composition of claim 1 or 5, wherein the amount of the epoxy polymer is in the range of about 1 to about 50 weight percent of the solids of the aqueous sizing composition and the amount is always less than the amount of the poly(vinylacetate) silane copolymer.

Claim 9

Aqueous sizing composition of claim 1, wherein the polyethylene-containing polymer is selected from high density polyethylene, medium density polyethylene, low density polyethylene, ultra high molecular weight polyethylene, polyethylene-polypropylene copolymer and polyethylene-1-olefin copolymers wherein the polyethylene is present in the major amount.

Claim 10

Aqueous sizing composition of claim 1, wherein the wax has a melting point above about 50° C.

Claim 11

Aqueous sizing composition of claim 1, wherein the amino silane is gamma-aminopropyltriethoxysilane.

Claim 12

Aqueous sizing composition of claim 1, wherein the lubricant modified amino silane coupling agent is gamma-aminopropyltriethoxysilane.

Claim 13

Aqueous sizing composition of claim 1, wherein the epoxy-containing polymer is gamma-glycidylpropyltrimethoxysilane.

Claim 14

Aqueous sizing composition of claim 1, which includes about 0.1 to about 4 weight percent of the aqueous sizing composition of a vinyl-containing silane coupling agent.

Claim 15

Aqueous sizing composition of claim 13, wherein the vinyl-containing silane coupling agent is gamma-methylacryloxypropyltrimethoxysilane.

Claim 16

Aqueous sizing composition of claim 1, wherein the amount of the one or more silane coupling agents is in the range of about 0.1 to about 4 weight percent of the aqueous sizing composition.

Claim 17

Aqueous sizing composition of claim 1 wherein the organic hydrocarbon acid is acetic acid.

Claim 18

Aqueous sizing composition of claim 1, wherein the nonionic surfactant is an alkyl aryl polyether with an HLB of around 14.

Claim 19

Aqueous sizing composition of claim 1, wherein the wax is a microcrystalline wax with a melting point greater than 50° C.

Claim 20

Sized glass fiber strand containing the aqueous sizing composition of claim 1.

Claim 21

Dry chopped glass fiber strands having an LOI in the range of about 1.5 to 2.5 of the aqueous sizing composition of claim 1, wherein the dry chopped glass fiber strands were dried at a temperature and time that are sufficient to remove a substantial amount of the moisture from the sized strands.

Claim 22

Dry chopped glass fiber strands of claim 20 dried at a temperature of at least 240° F. (115° C.) at around 11 hours.

Claim 23

Thermosetting molding compound having the dry chopped glass fiber strands of claims 20 or 21 along with a thermosetting polymer, catalyst, thickener and monomer.

Claim 24

Molded article of the molding compound of claim 22.

Claim 25

Molding compound of claim 22 wherein the thermosetting polymer is selected from the group consisting of unsaturated polyester, unsaturated vinyl esters, epoxy polymers including 1,2-epoxy polymers, phenolic resins, alkyd resins, silicone resins and diallyl phthalate homopolymers, polyamides, urea and melamine containing resins and polyurethanes.

Claim 26

Aqueous sizing composition for glass fibers used in producing glass fiber strands for use in thermosetting molding compounds for production of reinforced thermoset articles, comprising: (a) poly(vinylacetate) silane copolymer which is insoluble in styrene and has a silane level of from about 1 to about 7 weight percent of the copolymer which is present in the aqueous sizing composition in an amount of about 40 to about 90 weight percent of the total solids of the aqueous sizing composition, (b) epoxy polymer having a molecular weight in the range of about 170 to about 900 present in an amount in the range of about 1 to about 60 weight percent of the solids of the aqueous sizing composition, (c) one or more alkyl aryl polyether nonionic surfactants with an HLB of around 14, (d) a mixture of organo silane coupling agents having a predominant amount of an epoxy-containing silane coupling agent and a minor amount of a lubricant modified amino-organo silane coupling agent, (e) pelargonic acid amide of tetraethylene pentamine in an amount in the range of about 0.05 to about 5 weight percent of the aqueous sizing composition, (f) high density polyethylene polymer present in an amount of about 2 to about 25 weight percent of the solids of the sizing composition, (g) a microcrystalline paraffinic wax with a melting point greater than 50° C. present in an amount of about 1 to about 5 weight percent of the solids of the aqueous sizing composition, and where the weight ratio of the polyethylene polymer to the wax is in the range of about 10:1 to about 1:10, (h) organic hydrocarbon acid to give the composition a pH in the range of about 4 to around 7, and (i) water to give a total solids content in the range of about 1 to about 30 weight percent.

Claim 27

Aqueous sizing composition for glass fibers used in producing glass fiber strands for use in thermosetting molding compounds for production of reinforced thermoset articles, comprising: (a) poly(vinylacetate) silane copolymer which is insoluble in styrene and has a silane level of from about 1 to about 7 weight percent of the copolymer which is present in the aqueous sizing composition in an amount of about 40 to about 90 weight percent of the total solids of the aqueous sizing composition, (b) epoxy polymer having a molecular weight in the range of about 170 to about 900 present in an amount in the range of about 1 to about 60 weight percent of the solids of the aqueous sizing composition, (c) one or more alkyl aryl polyether nonionic surfactants with an HLB of around 14, (d) a mixture of organo silane coupling agents having a predominant amount of an epoxy-containing silane coupling agent and a minor amount of a lubricant modified amino-organo silane coupling agent, (e) pelargonic acid amide of tetraethylene pentamine in an amount in the range of about 0.05 to about 5 weight percent of the aqueous sizing composition, (f) high density polyethylene polymer present in an amount of about 2 to about 25 weight percent of the solids of the sizing composition, (g) a microcrystalline paraffinic wax with a melting point greater than 50° C. present in an amount of about 1 to about 5 weight percent of the solids of the aqueous sizing composition, and where the weight ratio of the polyethylene polymer to the wax is in the range of about 10:1 to about 1:10, (h) organic hydrocarbon acid to give the composition a pH in the range of about 4 to around 7, and (i) water to give a total solids content in the range of about 1 to about 30 weight percent.

Claim 28

Aqueous sizing composition of claim 25, wherein the poly(vinylacetate) silane copolymer is a copolymer of vinylacetate and gamma-methacryloxypropyltrimethoxysilane and has about 2 percent silane.

Claim 29

Aqueous sizing composition of claim 25 or 26, wherein the amount of the poly(vinylacetate) silane copolymer is always greater than the amount of the epoxy polymer.

Claim 30

Aqueous sizing composition of claim 25, wherein the lubricant modified amino silane coupling agent is gamma-aminopropyltriethoxysilane.

Claim 31

Aqueous sizing composition of claim 25, wherein the epoxy-containing silane is gamma-glycidoxypropyltrimethoxysilane present in an amount in the range of about 0.1 to about 4 weight percent of the aqueous sizing composition.

Claim 32

Aqueous sizing composition of claim 25, wherein the ratio of the high density polyethylene polymer to microcrystalline wax is in the range of about 1:1 to about 10:1.

Claim 33

Aqueous sizing composition of claim 25, wherein the weight ratio of the vinylacetate-organo silane copolymer to the epoxy polymer is in the range of about 1:1 to about 1:1.

Claim 34

Sized glass fiber strands having a coating of the aqueous sizing composition of claim 25.

Claim 35

Sized glass fiber strands of claim 32, dry chopped with drying conditions of temperature at least about 240° F. (115° C.) for around 1 hours or any other time/temperature relationship giving equivalent drying.

Claim 36

Bulk molding compound having the dried chopped strands of claim 33.

Claim 37

An aqueous sizing composition for treating glass fibers useful in reinforcing thermoplastic polymers, comprising: a. poly(vinyl acetate) silane copolymer, b. epoxy polymer, c. polyethylene-containing polymer with limited branching, d. an organo silane coupling agent selected from the group consisting of amino-organo-silane coupling agents, lubricant modified amino-organic-silane coupling agents, epoxy-containing silane coupling agents and a mixture of two or more of these agents, and e. water in an amount to give a total solids for the composition in the range of 1 to about 30 weight percent.

Claim 38

An aqueous sizing composition for treating glass fibers useful in reinforcing thermoplastic polymers, comprising: a. poly(vinyl acetate) silane copolymer, b. epoxy polymer, c. polyethylene-containing polymer with limited branching, d. an organo silane coupling agent selected from the group consisting of amino-organo-silane coupling agents, lubricant modified amino-organic-silane coupling agents, epoxy-containing silane coupling agents and a mixture of two or more of these agents, and e. water in an amount to give a total solids for the composition in the range of 1 to about 30 weight percent.

Claim 39

Glass fibers sized with the aqueous treating composition of claim 35.