Chemical vapor deposition of vanadium oxide coatings
Assignee: PPG Industries Inc
•
Filing: 1982-02-01
•
Granted: 1983-07-12
•
Expires: 2002-02-01
Abstract
Abstract A method is disclosed for the chemical vapor deposition of vanadium oxide film on glass substrates, as well as a thermochromic VO 2 film for the variable transmittance of solar energy and a conductive V 2 O 3 film, both formed by chemical vapor deposition employing liquid vanadium compounds.
Inventors
- 👤 Charles B. Greenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:20
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/405; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C03C17/34; C03C17/3411; C03C17/3417; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/218; C03C2218/00; C03C2218/10; C03C2218/15; C03C2218/152; C03C2218/30; C03C2218/32; C03C2218/324
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
64 words
A method for the chemical vapor deposition of vanadium oxide films comprising the steps of: a. heating a glass substrate to a sufficient temperature to convert a vanadium compound to vanadium oxide; b. vaporizing a liquid vanadium compound; c. contacting a surface of said heated glass substrate with the vapor of said vanadium compound to deposit a vanadium oxide film on the glass surface.
Claim 2
Independent Claim
64 words
A method for the chemical vapor deposition of vanadium oxide films comprising the steps of: a. heating a glass substrate to a sufficient temperature to convert a vanadium compound to vanadium oxide; b. vaporizing a liquid vanadium compound; c. contacting a surface of said heated glass substrate with the vapor of said vanadium compound to deposit a vanadium oxide film on the glass surface.
Claim 3
Dependent Claim
13 words
The method according to claim 1, wherein the vanadium compound is vanadium i-propylate.
Claim 4
Dependent Claim
30 words
The method according to claim 2, wherein the vanadium compound and the glass substrate are exposed to an oxidizing atmosphere, and a film containing V 2 O 5 is formed.
Claim 5
Dependent Claim
32 words
The method according to claim 3, wherein the V 2 O 5 coated glass is further exposed to a reducing atmosphere to reduce the V 2 O 5 to VO 2 .
Claim 6
Dependent Claim
37 words
The method according to claim 1, wherein the glass substrate is coated with a primer layer selected from the group consisting of tin oxide, silicon, and titanium oxide prior to the chemical vapor deposition of vanadium oxide.
Claim 7
Dependent Claim
28 words
The method according to claim 5, wherein the vaporized vanadium i-propylate contacts the glass surface in a nonoxidizing atmosphere and a thermochromic film containing VO 2 is formed.
Claim 8
Dependent Claim
13 words
The method according to claim 1, wherein the organovanadium compound is vanadium n-propylate.
Claim 9
Dependent Claim
30 words
The method according to claim 7, wherein the vanadium oxide coated glass is exposed to a nonoxidizing atmosphere and an electrically conductive film containing V 2 O 3 is formed.
Claim 10
Dependent Claim
22 words
The method according to claim 1, wherein the vanadium oxide film is deposited to a thickness of about 100 to 1,500 Angstroms.
Claim 11
Independent Claim
92 words
A method for depositing a vanadium oxide film comprising the steps of: a. heating a glass substrate to a temperature of at least about 350° C.; b. vaporizing vanadium i-propylate; c. conveying the vaporized vanadium i-propylate in a stream of nonoxidizing gas to the substrate; d. contacting a surface of said heated glass substrate with the vaporized vanadium i-propylate in a nonoxidizing atmosphere to deposit thereupon a vanadium oxide film; and e. cooling the vanadium oxide coated glass in a reducing gas atmosphere to obtain a thermochromic film containing VO 2 .
Claim 12
Independent Claim
92 words
A method for depositing a vanadium oxide film comprising the steps of: a. heating a glass substrate to a temperature of at least about 350° C.; b. vaporizing vanadium i-propylate; c. conveying the vaporized vanadium i-propylate in a stream of nonoxidizing gas to the substrate; d. contacting a surface of said heated glass substrate with the vaporized vanadium i-propylate in a nonoxidizing atmosphere to deposit thereupon a vanadium oxide film; and e. cooling the vanadium oxide coated glass in a reducing gas atmosphere to obtain a thermochromic film containing VO 2 .
Claim 13
Independent Claim
83 words
A method for depositing a vanadium oxide film comprising the steps of: a. heating a glass substrate to a temperature of at least about 300° C.; b. vaporizing vanadium i-propylate; c. conveying the vaporized vanadium i-propylate in a stream of inert gas to the substrate; d. contacting a surface of the substrate with the vaporized vanadium i-propylate to form a vanadium oxide film; and e. cooling the vanadium oxide coated glass in air to obtain a film containing V 2 O 5 .
Claim 14
Independent Claim
83 words
A method for depositing a vanadium oxide film comprising the steps of: a. heating a glass substrate to a temperature of at least about 300° C.; b. vaporizing vanadium i-propylate; c. conveying the vaporized vanadium i-propylate in a stream of inert gas to the substrate; d. contacting a surface of the substrate with the vaporized vanadium i-propylate to form a vanadium oxide film; and e. cooling the vanadium oxide coated glass in air to obtain a film containing V 2 O 5 .
Claim 15
Dependent Claim
21 words
The method according to claim 11, wherein the V 2 O 5 is reduced to VO 2 in a reducing atmosphere.
Claim 16
Dependent Claim
13 words
The method according to claim 12, wherein the reducing atmosphere comprises forming gas.
Claim 17
Dependent Claim
15 words
The method according to claim 13, wherein the reducing atmosphere further comprises an aromatic hydrocarbon.
Claim 18
Independent Claim
93 words
A method for making a conductive coated glass article comprising the steps of: a. heating a glass substrate to a temperature of at least about 400° C.; b. vaporizing vanadium n-propylate; c. conveying said vaporized vanadium n-propylate to said substrate in a stream of nitrogen; d. contacting a surface of said heated glass substrate with the vaporized vanadium n-propylate to deposit thereupon a film containing V 2 O 3 ; and e. cooling the coated glass article in an atmosphere insufficiently oxidizing to convert the V 2 O 3 to VO 2 .
Claim 19
Independent Claim
93 words
A method for making a conductive coated glass article comprising the steps of: a. heating a glass substrate to a temperature of at least about 400° C.; b. vaporizing vanadium n-propylate; c. conveying said vaporized vanadium n-propylate to said substrate in a stream of nitrogen; d. contacting a surface of said heated glass substrate with the vaporized vanadium n-propylate to deposit thereupon a film containing V 2 O 3 ; and e. cooling the coated glass article in an atmosphere insufficiently oxidizing to convert the V 2 O 3 to VO 2 .
Claim 20
Dependent Claim
19 words
The method according to claim 15, wherein the V 2 O 3 coated glass is cooled in forming gas.
Claim 21
Dependent Claim
35 words
The method according to claim 15, wherein the film containing V 2 O 3 is deposited to a thickness of about 200 to 1,500 Angstroms and has a resistivity less than 1,000 ohms per square.
References Cited (Backward Citations)
US3483110A
Cited
US4307942A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-11 | 1987-01-10 | 1987-07-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-11 | 1991-01-10 | 1991-07-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-11 | 1995-01-10 | 1995-07-12 | $7700.00 | Window Closed / Lapsed |