Color stable chelated titanate compositions

Claim 1

An elastomeric composition comprising (i) a hydroxyl endblocked polydiorganosiloxane, (ii) a silane or mixture of silanes having an average of from 2.01 to 4 inclusive alkoxy radicals, and a sufficient amount of a titanium-containing composition to yield from 0.1 to 10 parts by weight of chelated titanium compound based upon 100 parts by weight of the hydroxyl endblocked polydiorganosiloxane, said elastomeric composition being stable under conditions excluding moisture and curable by exposure to moisture, where said tatanium-containing composition comprise the product obtained by mixing, under conditions which substantially exclude moisture, (a) a chelated titanium compound having a formula ##STR14## in which R 3 is a monovalent hydrocarbon radical having from 1 to 18 inclusive carbon atoms, R 4 is a monovalent radical selected from the group consisting of hydrocarbon radicals having from 1 to 18 carbon atoms, and hydrogen, R 5 is a monovalent radical selected from the group consisting of hydrocarbon radicals and aliphatic hydrocarbonoxy radicals each having from 1 to 18 inclusive carbon atoms, and Z is a radical selected from the group consisting of monovalent aliphatic hydrocarbonoxy radicals and monovalent acyloxy radicals, each having from 1 to 18 inclusive carbon atoms; hydroxyl radical; divalent oxygen atoms forming a TiOTi linkage; and when taken together form an alkanedioxy radical of the formula ##STR15## in which R 6 is a radical selected from the group consisting of hydrogen atom and monovalent aliphatic hydrocarbon radicals having not more than 8 carbon atoms, the total number of carbon atoms in the alkanedioxy radical is not more than 18, and (b) from 1 to 100 parts by weight based on 100 parts by weight of (a), of an additive soluble in the chelated titanium compound and being selected from the group consisting of (1) an ester of thioalkanoic acid of the formula ##STR16## wherein R 8 is an alkyl group containing from 1 to 15 inclusive carbon atoms and a is an integer of from 1 to 4 inclusive, (2) di-tertiary-butyl phenol containing compounds selected from the group consisting of 2,6-di-tert-butyl-4-methylphenol, tetrakis[methylene-3-(3',5'-di-tert-butyl4'-hydroxyphenyl)propionate]methane, octadecyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate, 4,4'-methylenebis(2,6-di-tert-butylphenol), 1,6-hexamethylene-bis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), and thiodiethylenebis-(3,5-di-tert-butyl-4-hydroxy hydrocinnamate), (3) an organic phosphite selected from the group consisting of the formula (R.sup.10 O).sub.b P(OR.sup.11).sub.3-b wherein R 10 and R 11 are selected from the group consisting of linear or branched alkyl radicals of from 1 to 18 carbon atoms, and phenyl radical, wherein b is 0 or 1, and the formula ##STR17## wherein R 12 is a linear or branched alkyl radical of from 1 to 18 carbon atoms, and (4) a mixture of (2) and (3), the composition having a color of less than 13 as determined by the Gardner Color Scale and being stored under conditions substantially excluding moisture.

Claim 12

A method of producing a silicone elastomeric composition which is stable under conditions excluding moisture but which will cure upon exposure to moisture comprising mixing under conditions which substantially exclude moisture (i) a hydroxyl endblocked polydiorganosiloxane having a viscosity of at least 0.025 Pa·s at 25° C. having the average formula ##EQU4## in which z has an average value from 1 to 1.01 inclusive, y has an average value from 1.99 to 2 inclusive, and the sum of y+z is 3, R is selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and monovalent cyanoalkyl radicals, all of from 1 to 18 inclusive carbon atoms, and n is an integer, (ii) at least one silane or silane mixture of the average formula R.sub.m Si(OR.sup.1).sub.4-m in which R is as defined above, R 1 is selected from the group consisting of monovalent haloaliphatic hydrocarbon radicals having no halogen alpha to the oxygen and monovalent aliphatic hydrocarbon radicals, both of less than 5 carbon atoms, m is from 0 to 3 and has an average value of from 0 to 1.99, and (ii) being present in an amount of at least 1.0 mole of silane per mole of silicon-bonded hydroxyl in (i), and (iii) a sufficient amount of a titanium-containing composition, to yield from 0.1 to 10 parts by weight of chelated titanium compound based on 100 parts by weight of (i) and placing said silicone elastomerc composition into a moisture impermeable container where said titanium-containing composition comprises the product obtained by mixing, under conditions which substantially exclude moisture, (a) a chelated titanium compound having a formula ##STR18## in which R 3 is a monovalent hydrocarbon radical having from 1 to 18 inclusive carbon atoms, R 4 is a monovalent radical selected from the group consisting of hydrocarbon radicals having from 1 to 18 carbon atoms, and hydrogen, R 5 is a monovalent radical selected from the group consisting of hydrocarbon radicals and aliphatic hydrocarbonoxy radicals each having from 1 to 18 inclusive carbon atoms, and Z is a radical selected from the group consisting of monovalent aliphatic hydrocarbonoxy radicals and monovalent acyloxy radicals, each having from 1 to 18 inclusive carbon atoms; hydroxyl radical; divalent oxygen atoms forming a TiOTi linkage; and when taken together form an alkanedioxy radical of the formula ##STR19## in which R 6 is a radical selected from the group consisting of hydrogen atom and monovalent aliphatic hydrocarbon radicals having not more than 8 carbon atoms, the total number of carbon atoms in the alkanedioxy radical is not more than 18, and (b) from 1 to 100 parts by weight based on 100 parts by weight of (a), of an additive soluble in the chelated titanium compound and being selected from the group consisting of (1) an ester of thioalkanoic acid of the formula ##STR20## wherein R 8 is an alkyl group containing from 1 to 15 inclusive carbon atoms and a is an integer of from 1 to 4 inclusive, (2) di-tertiary-butyl phenol containing compounds selected from the group consisting of 2,6-di-tert-butyl-4-methylphenol, tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]methane, octadecyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate, 4,4'-methylenebis(2,6-di-tert-butylphenol), 1,6-hexamethylene-bis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), and thiodiethylenebis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), (3) an organic phosphite selected from the group consisting of the formula (R.sup.10 O).sub.b P(OR.sup.11).sub.3-b wherein R 10 and R 11 are selected from the group consisting of linear or branched alkyl radicals of from 1 to 18 carbon atoms, and phenyl radical, wherein b is 0 or 1, and the formula ##STR21## wherein R 12 is a linear or branched alkyl radical of from 1 to 18 carbon atoms, and (4) a mixture of (2) and (3), the composition having a color of less than 13 as determined by the Gardner Color Scale.

Claim 13

A method of producing a silicone elastomeric composition which is stable under conditions excluding moisture but which will cure upon exposure to moisture comprising mixing under conditions which substantially exclude moisture (i) a hydroxyl endblocked polydiorganosiloxane having a viscosity of at least 0.025 Pa·s at 25° C. having the average formula ##EQU4## in which z has an average value from 1 to 1.01 inclusive, y has an average value from 1.99 to 2 inclusive, and the sum of y+z is 3, R is selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and monovalent cyanoalkyl radicals, all of from 1 to 18 inclusive carbon atoms, and n is an integer, (ii) at least one silane or silane mixture of the average formula R.sub.m Si(OR.sup.1).sub.4-m in which R is as defined above, R 1 is selected from the group consisting of monovalent haloaliphatic hydrocarbon radicals having no halogen alpha to the oxygen and monovalent aliphatic hydrocarbon radicals, both of less than 5 carbon atoms, m is from 0 to 3 and has an average value of from 0 to 1.99, and (ii) being present in an amount of at least 1.0 mole of silane per mole of silicon-bonded hydroxyl in (i), and (iii) a sufficient amount of a titanium-containing composition, to yield from 0.1 to 10 parts by weight of chelated titanium compound based on 100 parts by weight of (i) and placing said silicone elastomerc composition into a moisture impermeable container where said titanium-containing composition comprises the product obtained by mixing, under conditions which substantially exclude moisture, (a) a chelated titanium compound having a formula ##STR18## in which R 3 is a monovalent hydrocarbon radical having from 1 to 18 inclusive carbon atoms, R 4 is a monovalent radical selected from the group consisting of hydrocarbon radicals having from 1 to 18 carbon atoms, and hydrogen, R 5 is a monovalent radical selected from the group consisting of hydrocarbon radicals and aliphatic hydrocarbonoxy radicals each having from 1 to 18 inclusive carbon atoms, and Z is a radical selected from the group consisting of monovalent aliphatic hydrocarbonoxy radicals and monovalent acyloxy radicals, each having from 1 to 18 inclusive carbon atoms; hydroxyl radical; divalent oxygen atoms forming a TiOTi linkage; and when taken together form an alkanedioxy radical of the formula ##STR19## in which R 6 is a radical selected from the group consisting of hydrogen atom and monovalent aliphatic hydrocarbon radicals having not more than 8 carbon atoms, the total number of carbon atoms in the alkanedioxy radical is not more than 18, and (b) from 1 to 100 parts by weight based on 100 parts by weight of (a), of an additive soluble in the chelated titanium compound and being selected from the group consisting of (1) an ester of thioalkanoic acid of the formula ##STR20## wherein R 8 is an alkyl group containing from 1 to 15 inclusive carbon atoms and a is an integer of from 1 to 4 inclusive, (2) di-tertiary-butyl phenol containing compounds selected from the group consisting of 2,6-di-tert-butyl-4-methylphenol, tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate]methane, octadecyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate, 4,4'-methylenebis(2,6-di-tert-butylphenol), 1,6-hexamethylene-bis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), and thiodiethylenebis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), (3) an organic phosphite selected from the group consisting of the formula (R.sup.10 O).sub.b P(OR.sup.11).sub.3-b wherein R 10 and R 11 are selected from the group consisting of linear or branched alkyl radicals of from 1 to 18 carbon atoms, and phenyl radical, wherein b is 0 or 1, and the formula ##STR21## wherein R 12 is a linear or branched alkyl radical of from 1 to 18 carbon atoms, and (4) a mixture of (2) and (3), the composition having a color of less than 13 as determined by the Gardner Color Scale.

Claim 14

A method of producing a silicone elastomeric composition which is stable under conditions excluding moisture but which will cure upon exposure to moisture comprising mixing under conditions which substantially exclude moisture (i) 100 parts by weight of a hydroxyl endblocked polydiorganosiloxane having a viscosity of at least 0.025 Pa.s at 25° C. and having the average formula ##EQU5## in which z has an average value from 1 to 1.01 inclusive, y has an average value from 1.99 to 2 inclusive, and the sum of y+z is 3, R is selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and monovalent cyanoalkyl radicals, all of from 1 to 18 inclusive carbon atoms, and n is an integer, (ii) at least one silane or silane mixture of the average formula R.sub.m Si(OR.sup.1).sub.4-m in which R is as defined above, R 1 is selected from the group consisting of monovalent haloaliphatic hydrocarbon radicals having no halogen alpha to the oxygen and monovalent aliphatic hydrocarbon radicals, both of less than 5 carbon atoms, m is from 0 to 3 and has an average value of from 0 to 1.99, and (ii) being present in an amount of at least 1.0 mole of silane per mole of silicon-bonded hydroxyl in (i), and (a) at least 0.1 part by weight based on the weight of (i) of a chelated titanium compound having a formula ##STR22## in which R 3 is a monovalent hydrocarbon radical having from 1 to 18 inclusive carbon atoms, R 4 is a monovalent radical selected from the group consisting of hydrocarbon radicals having from 1 to 18 carbon atoms, and hydrogen, R 5 is a monovalent radical selected from the group consisting of hydrocarbon radicals and aliphatic hydrocarbonoxy radicals each having from 1 to 18 inclusive carbon atoms, and Z is a radical selected from the group consisting of monovalent aliphatic hydrocarbonoxy radicals and monovalent acyloxy radicals, each having from 1 to 18 inclusive carbon atoms; hydroxyl radical; divalent oxygen atoms forming a TiOTi linkage; and when taken together form an alkanedioxy radical of the formula ##STR23## in which R 6 is a radical selected from the group consisting of hydrogen atom and monovalent aliphatic hydrocarbn radicals having not more than 8 carbon atoms, the total number of carbon atoms in the alkanedioxy radical is not more than 18, and (b) an additive selected from the group consisting of (1) at least 0.05 part by weight of an ester of thioalkanoic acid of the formula ##STR24## wherein R 8 is an alkyl group containing from 1 to 15 inclusive carbon atoms and a is an integer of from 1 to 4 inclusive, (2) from 0.015 part to 5 parts by weight of di-tertiary-butyl phenol containing compounds selected from the group consisting of 2,6-di-tert-butyl-4-methylphenol, tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)-propionate[methane, octadecyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate, 4,4'-methylene-bis(2,6-di-tert-butylphenol), 1,6-hexamethylene-bis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), and thiodiethylenebis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), (3) from 0.001 part to 1 part by weight of an organic phosphite selected from the group consisting of the formula (R.sup.10 O).sub.b P(OR.sup.11).sub.3-b wherein R 10 and R 11 are selected from the group consisting of linear or branched alkyl radicals of from 1 to 18 carbon atoms, and phenyl radical, wherein b is 0 or 1, and the formula ##STR25## wherein R 12 is a linear or branched alkyl radical of from 1 to 18 carbon atoms; and (4) a mixture of di-tertiary-butyl phenol of (2) and an organic phosphite of (3), the composition having a color of 5 or less as determined by the Gardner Color Scale.

Claim 15

A method of producing a silicone elastomeric composition which is stable under conditions excluding moisture but which will cure upon exposure to moisture comprising mixing under conditions which substantially exclude moisture (i) 100 parts by weight of a hydroxyl endblocked polydiorganosiloxane having a viscosity of at least 0.025 Pa.s at 25° C. and having the average formula ##EQU5## in which z has an average value from 1 to 1.01 inclusive, y has an average value from 1.99 to 2 inclusive, and the sum of y+z is 3, R is selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and monovalent cyanoalkyl radicals, all of from 1 to 18 inclusive carbon atoms, and n is an integer, (ii) at least one silane or silane mixture of the average formula R.sub.m Si(OR.sup.1).sub.4-m in which R is as defined above, R 1 is selected from the group consisting of monovalent haloaliphatic hydrocarbon radicals having no halogen alpha to the oxygen and monovalent aliphatic hydrocarbon radicals, both of less than 5 carbon atoms, m is from 0 to 3 and has an average value of from 0 to 1.99, and (ii) being present in an amount of at least 1.0 mole of silane per mole of silicon-bonded hydroxyl in (i), and (a) at least 0.1 part by weight based on the weight of (i) of a chelated titanium compound having a formula ##STR22## in which R 3 is a monovalent hydrocarbon radical having from 1 to 18 inclusive carbon atoms, R 4 is a monovalent radical selected from the group consisting of hydrocarbon radicals having from 1 to 18 carbon atoms, and hydrogen, R 5 is a monovalent radical selected from the group consisting of hydrocarbon radicals and aliphatic hydrocarbonoxy radicals each having from 1 to 18 inclusive carbon atoms, and Z is a radical selected from the group consisting of monovalent aliphatic hydrocarbonoxy radicals and monovalent acyloxy radicals, each having from 1 to 18 inclusive carbon atoms; hydroxyl radical; divalent oxygen atoms forming a TiOTi linkage; and when taken together form an alkanedioxy radical of the formula ##STR23## in which R 6 is a radical selected from the group consisting of hydrogen atom and monovalent aliphatic hydrocarbn radicals having not more than 8 carbon atoms, the total number of carbon atoms in the alkanedioxy radical is not more than 18, and (b) an additive selected from the group consisting of (1) at least 0.05 part by weight of an ester of thioalkanoic acid of the formula ##STR24## wherein R 8 is an alkyl group containing from 1 to 15 inclusive carbon atoms and a is an integer of from 1 to 4 inclusive, (2) from 0.015 part to 5 parts by weight of di-tertiary-butyl phenol containing compounds selected from the group consisting of 2,6-di-tert-butyl-4-methylphenol, tetrakis[methylene-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)-propionate[methane, octadecyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate, 4,4'-methylene-bis(2,6-di-tert-butylphenol), 1,6-hexamethylene-bis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), and thiodiethylenebis-(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), (3) from 0.001 part to 1 part by weight of an organic phosphite selected from the group consisting of the formula (R.sup.10 O).sub.b P(OR.sup.11).sub.3-b wherein R 10 and R 11 are selected from the group consisting of linear or branched alkyl radicals of from 1 to 18 carbon atoms, and phenyl radical, wherein b is 0 or 1, and the formula ##STR25## wherein R 12 is a linear or branched alkyl radical of from 1 to 18 carbon atoms; and (4) a mixture of di-tertiary-butyl phenol of (2) and an organic phosphite of (3), the composition having a color of 5 or less as determined by the Gardner Color Scale.