US4391858A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Coating process
Assignee: BASF Corp
•
Filing: 1981-11-20
•
Granted: 1983-07-05
•
Expires: 2001-11-20
Abstract
Abstract A process for the production of a multilayer protective and/or decorative coating upon the surface of a substrate (1) A basecoat composition is applied comprising: (A) a film-forming polymer; (B) a volatile organic liquid diluent in which the polymer is dissolved; (C) polymer microparticles which are insoluble in the solution of the polymer (A) in the liquid diluent (B) and are stably dispersed by steric stabilization therein in a non-flocculated state in an amount of from 3% to 8% of the aggregate weight of the film-forming polymer A and the microparticles; (D) pigment particles also dispersed in the solution of the film-forming polymer in the liquid diluent. (2) A polymer film is formed upon the surface from the composition applied in (1). (3) A transparent topcoat is applied to the basecoat film from a composition comprising: (E) a film-forming polymer; and (F) a volatile carrier liquid for the polymer. (4) A second polymer film is formed upon the basecoat film from the composition applied in (1).
Inventors
- 👤 Wolfgang Batzill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:57
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/53; B05D5/00; B05D5/06; B05D5/067; B05D5/068
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
181 words
A process for the production of a multilayer protective and/or decorative coating upon the surface of a substrate, which comprises the steps of: (1) applying to the surface a basecoat composition comprising: (A) a film-forming polymer; (B) a volatile organic liquid diluent in which the polymer is dissolved; (C) polymer microparticles of diameter 0.01 to 10 microns which are insoluble in the solution of the polymer (A) in the liquid diluent (B) and are stably dispersed by steric stabilization therein in a nonflocculated state in an amount of from 3% to 8% of the aggregate weight of said film-forming polymer of (A) and said microparticles; (D) pigment particles also dispersed in the solution of the film-forming polymer in the liquid diluent; (2 ) forming a polymer film upon the surface from the composition applied in step (1); (3) applying to the basecoat film so obtained a transparent topcoat composition comprising: (E) a film-forming polymer; and (F) a volatile carrier liquid for the polymer; and (4) forming a second polymer film upon the basecoat film from the composition applied in step (1).
Claim 2
Dependent Claim
181 words
A process for the production of a multilayer protective and/or decorative coating upon the surface of a substrate, which comprises the steps of: (1) applying to the surface a basecoat composition comprising: (A) a film-forming polymer; (B) a volatile organic liquid diluent in which the polymer is dissolved; (C) polymer microparticles of diameter 0.01 to 10 microns which are insoluble in the solution of the polymer (A) in the liquid diluent (B) and are stably dispersed by steric stabilization therein in a nonflocculated state in an amount of from 3% to 8% of the aggregate weight of said film-forming polymer of (A) and said microparticles; (D) pigment particles also dispersed in the solution of the film-forming polymer in the liquid diluent; (2 ) forming a polymer film upon the surface from the composition applied in step (1); (3) applying to the basecoat film so obtained a transparent topcoat composition comprising: (E) a film-forming polymer; and (F) a volatile carrier liquid for the polymer; and (4) forming a second polymer film upon the basecoat film from the composition applied in step (1).
Claim 3
Dependent Claim
30 words
A process as claimed in claim 1, wherein the film-forming polymer constituent (A) is a polymer or copolymer of one or more alkyl esters of acrylic acid or methacrylic acid.
Claim 4
Dependent Claim
20 words
A process as claimed in claim 1, wherein the film-forming polymer constituent (A) is an alkyd resin or a polyester.
Claim 5
Dependent Claim
30 words
A process as claimed in claim 1, wherein the polymer microparticles (C) consist of a polymer or copolymer of one or more alkyl esters of acrylic acid or methacrylic acid.
Claim 6
Dependent Claim
43 words
A process as claimed in claim 1, wherein the polymer microparticles have been produced by a process of dispersion polymerization of monomers, in an organic liquid in which the resulting polymer is insoluble, in the presence of a steric stabilizer for the particles.
Claim 7
Dependent Claim
69 words
A process as claimed in claim 5, wherein the steric stabilizer is a graft copolymer of which one type of polymeric component is a polymer backbone which is solvatable by the organic liquid and of which another type of polymeric component consists of a plurality of polymer chains, pendant from the backbone, which are not solvatable by the organic liquid and which are capable of associating with the microparticles.
Claim 8
Dependent Claim
61 words
A process as claimed in claim 5, wherein the microparticles are brought into association with the auxiliary polymer by following up the dispersion polymerization process, whereby the microparticles are obtained, immediately with the polymerization of further monomer, from which the auxiliary polymer is to be derived, in the original inert liquid medium and in the presence of the original stabilizing agent.
Claim 9
Dependent Claim
46 words
A process as claimed in claim 1, wherein the microparticles are further associated with a polymer, hereinafter referred to as auxiliary polymer, which is soluble in the volatile organic liquid constituent (B) of the base-coat composition and is also compatible with the film-forming polymer constituent (A).
Claim 10
Dependent Claim
20 words
A process as claimed in claim 1, wherein said pigment particles (D) have a size from 1 to 50 microns.
Claim 11
Dependent Claim
19 words
A process as claimed in claim 9, wherein said polymer microparticles have a diameter of 0.03 to 3 microns.
Claim 12
Dependent Claim
13 words
A process as claimed in claim 9, wherein said pigment particles are non-metallic.
Claim 13
Dependent Claim
22 words
A process as claimed in claim 1, wherein the pigment particles (D) in the base-coat composition consist of a metallic flake pigment.
Claim 14
Dependent Claim
21 words
A process as claimed in claim 1, wherein the film-forming polymer (E) of the top-coat composition is a thermosetting acrylic polymer.
References Cited (Backward Citations)
US1765748A
Cited
US3136651A
Cited
US3666521A
Cited
US4098928A
Cited
US4268542A
Cited
US4278483A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-07-04 | 1987-01-03 | 1987-07-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-07-04 | 1991-01-03 | 1991-07-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-07-04 | 1995-01-03 | 1995-07-05 | $7700.00 | Window Closed / Lapsed |