Method of planarizing silicon dioxide in semiconductor devices
Assignee: International Business Machines Corp
•
Filing: 1980-12-16
•
Granted: 1983-06-21
•
Expires: 2000-12-16
Abstract
Abstract The present invention provides a method for planarizing a non-uniform thickness of oxide, for example silicon dioxide as is formed over oxide-filled trenches used in deep dielectric isolation in integrated circuits. The oxide is removed by a planarizing resist-etching process so that etching in thicker resist areas proceeds at a rate slower than etching in thinner resist areas. A referred etchant is HF gas and etching is preferably at an elevated temperature.
Inventors
- 👤 Narasipur G. Anantha
- 👤 Harsaran S. Bhatia
- 👤 John S. Lechaton
- 👤 James L. Walsh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:34
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10P95/062; H10P95/064; H10P14/00; H10P14/60; H10P14/68; H10P14/683; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
257 words
A method for planarizing a non-level silicon dioxide layer which comprises at least one area (a) where a relatively high amount of silicon dioxide is to be removed and at least one area (b) where a relatively low amount of silicon dioxide is to be removed, said at least one area (a) and said at least one area (b) being non-level with respect to each other, said method comprising: forming a first layer of a patterned HF permeable positive photoresist and a second layer of a negative HF permeable photoresist on said silicon dioxide, said combination of HF permeable photoresists providing a relatively rapid etch rate at said at least one area (a) and a relatively slow etch rate at said at least one area (b); and exposing said layers of said HF permeable photoresists and said silicon dioxide layer to HF gas at a pressure in the range of from about 2 to about 18 torr and at a temperature in the range of from about 150° C. to about 200° C., thereby etching and planarizing said silicon dioxide layer as said HF gas penetrates said HF permeable photoresists to relatively rapidly etch said at least one area (a) and relatively slowly etch said at least one area (b), said exposing to said HF gas and said etching continuing until said at least one area (b) and said at least one area (b) have both been etched so as to be substantially planar with respect to each other, wherein etching is completed prior to photoresist removal.
Claim 2
Independent Claim
257 words
A method for planarizing a non-level silicon dioxide layer which comprises at least one area (a) where a relatively high amount of silicon dioxide is to be removed and at least one area (b) where a relatively low amount of silicon dioxide is to be removed, said at least one area (a) and said at least one area (b) being non-level with respect to each other, said method comprising: forming a first layer of a patterned HF permeable positive photoresist and a second layer of a negative HF permeable photoresist on said silicon dioxide, said combination of HF permeable photoresists providing a relatively rapid etch rate at said at least one area (a) and a relatively slow etch rate at said at least one area (b); and exposing said layers of said HF permeable photoresists and said silicon dioxide layer to HF gas at a pressure in the range of from about 2 to about 18 torr and at a temperature in the range of from about 150° C. to about 200° C., thereby etching and planarizing said silicon dioxide layer as said HF gas penetrates said HF permeable photoresists to relatively rapidly etch said at least one area (a) and relatively slowly etch said at least one area (b), said exposing to said HF gas and said etching continuing until said at least one area (b) and said at least one area (b) have both been etched so as to be substantially planar with respect to each other, wherein etching is completed prior to photoresist removal.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said silicon dioxide has a thickness of 1.5 to 3.0 microns.
Claim 4
Dependent Claim
13 words
The method of claim 1, wherein said temperature is 165° to 190° C.
Claim 5
Dependent Claim
41 words
The method of claim 1, wherein said patterned HF permeable positive photoresist covers only said at least one area (b) and said negative HF permeable photoresist covers both said at least one area (a) and said at least one area (b).
Claim 6
Dependent Claim
27 words
The method of claim 4, wherein said patterned HF permeable positive photoresist and said HF permeable negative photoresist have different etch rates with respect to silicon dioxide.
Claim 7
Independent Claim
46 words
The method of any one of claims 1, 2, 3, 4, or 5, wherein said at least one area (a) is in a deep wide trench and said at least one area (b) is in a deep narrow trench and wherein said silicon dioxide is conformal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-20 | 1986-12-20 | 1987-06-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-20 | 1990-12-20 | 1991-06-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-20 | 1994-12-20 | 1995-06-21 | $7700.00 | Window Closed / Lapsed |