Assignee: Hylsa SA de CV
•
Filing: 1981-08-04
•
Granted: 1983-06-14
•
Expires: 2001-08-04
Abstract
Abstract Sponge iron pellets are protected against re-oxidation by pre-wetting them with water or steam, coating them with a pulverulent passivating agent which is a mixture of iron oxide particles and hydraulic cement particles, then drying the treated pellets. Especially good results are achieved by using a hydraulic cement such as Portland cement and an iron oxide/cement ratio of 40:60 to 70:30.
Inventors
- 👤 David H. Carrillo-Cantu
- 👤 Asdrubal Trevino-Alanis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:36
CPC Classifications
C; C22; C22B; C22B1/00; C22B1/14; C22B1/24; C22B1/2406; C21; C21B; C21B13/00; C21B13/0086; C22B1/2413; Y; Y02; Y02P; Y02P10/00; Y02P10/10; Y02P10/134; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
58 words
A method of passivating sponge iron pellets comprising the steps of wetting said sponge iron pellets, applying to the wetted pellets a passivating amount of a pulverulent mixture of about 40% to 70% by weight of iron oxide particles and about 60% to 30% by weight of hydraulic cement particles and drying the thus treated sponge iron pellets.
Claim 2
Independent Claim
58 words
A method of passivating sponge iron pellets comprising the steps of wetting said sponge iron pellets, applying to the wetted pellets a passivating amount of a pulverulent mixture of about 40% to 70% by weight of iron oxide particles and about 60% to 30% by weight of hydraulic cement particles and drying the thus treated sponge iron pellets.
Claim 3
Dependent Claim
42 words
A method of passivating sponge iron pellets according to claim 1 wherein the wetted pellets are coated with said pulverulent mixture of iron oxide and cement particles to form a coating comprising about 0.1% to 1.0% by weight of the coated pellets.
Claim 4
Dependent Claim
23 words
A method of passivating sponge iron pellets according to claim 1 wherein said coating comprises about 0.5% by weight of said coated pellets.
Claim 5
Dependent Claim
28 words
A method of passivating sponge iron pellets according to claim 1 wherein the pellets are wetted with steam or liquid water before application of said pulverulent mixture thereto.
Claim 6
Dependent Claim
50 words
A method of passivating sponge iron pellets according to claim 1 wherein said hydraulic cement comprises by weight about 60% to 67% calcium oxide, 19% to 24% silicon dioxide, 4% to 9% aluminum oxide, up to 5% magnesium oxide, up to 3% sulfur trioxide, and 1.6 to 6% ferric oxide.
Claim 7
Dependent Claim
25 words
A method of passivating sponge iron pellets according to claim 1 wherein the treated pellets are dried with an inert gas at an elevated temperature.
Claim 8
Dependent Claim
51 words
A method of passivating sponge iron pellets according to claim 1 wherein the pellets are treated with an excess of said pulverulent mixture to form a coating thereon, the coated pellets are separated from excess pulverulent mixture and the excess mixture is used to treat a further quantity of untreated pellets.
Claim 9
Independent Claim
85 words
A method for the passivation of sponge iron pellets comprising the steps of wetting the sponge iron pellets, contacting the wetted pellets with an effective amount of a pulverulent passivating material comprising iron oxide particles in admixture with a hydraulic cement consisting essentially of a major amount of calcium oxide and minor but substantial amounts of silicon dioxide and aluminum oxide to coat said pellets with said passivating material, separating any excess passivating material from said coated sponge iron pellets and drying the coated pellets.
Claim 10
Independent Claim
85 words
A method for the passivation of sponge iron pellets comprising the steps of wetting the sponge iron pellets, contacting the wetted pellets with an effective amount of a pulverulent passivating material comprising iron oxide particles in admixture with a hydraulic cement consisting essentially of a major amount of calcium oxide and minor but substantial amounts of silicon dioxide and aluminum oxide to coat said pellets with said passivating material, separating any excess passivating material from said coated sponge iron pellets and drying the coated pellets.
Claim 11
Dependent Claim
35 words
A method according to claim 8 wherein the hydraulic cement contains by weight from about 60% to 67% calcium oxide, from about 19% to 24% silicon dioxide and from about 4% to 9% aluminum oxide.
Claim 12
Dependent Claim
20 words
A method according to claim 8 wherein said cement has an average particle size of about 0.02 to 0.05 mm.
Claim 13
Dependent Claim
20 words
A method according to claim 8 wherein said passivating material contains from 40% to 70% by weight of iron oxide.
Claim 14
Dependent Claim
21 words
A method according to claim 8 wherein separated excess passivating material is used to contact a further quantity of untreated pellets.
Claim 15
Dependent Claim
21 words
A method according to claim 8 wherein said coating comprises from about 0.1 to 1.0% by weight of the coated material.
Claim 16
Independent Claim
102 words
A method for the passivation of sponge iron particles comprising the steps of wetting said sponge iron particles, contacting said sponge iron particles with an effective amount of a pulverulent passivating material comprising iron oxide fines in admixture with hydraulic cement containing by weight 60 to 67% calcium oxide, 19 to 24% silicon dioxide, 4 to 9% aluminum oxide, up to 5% magnesium oxide, up to 3% sulfur trioxide and 1.6 to 6% ferric oxide to coat said sponge iron particles with said passivating material, separating any excess passivating material from said coated sponge iron, and drying the coated sponge iron particles.
Claim 17
Independent Claim
102 words
A method for the passivation of sponge iron particles comprising the steps of wetting said sponge iron particles, contacting said sponge iron particles with an effective amount of a pulverulent passivating material comprising iron oxide fines in admixture with hydraulic cement containing by weight 60 to 67% calcium oxide, 19 to 24% silicon dioxide, 4 to 9% aluminum oxide, up to 5% magnesium oxide, up to 3% sulfur trioxide and 1.6 to 6% ferric oxide to coat said sponge iron particles with said passivating material, separating any excess passivating material from said coated sponge iron, and drying the coated sponge iron particles.
Claim 18
Independent Claim
44 words
A method of passivating sponge iron pellets comprising the steps of wetting said sponge iron pellets, applying to the wetted pellets a passivating amount of a pulverulent mixture of hydraulic cement particles and iron oxide particles and drying the thus treated sponge iron pellets.
Claim 19
Independent Claim
44 words
A method of passivating sponge iron pellets comprising the steps of wetting said sponge iron pellets, applying to the wetted pellets a passivating amount of a pulverulent mixture of hydraulic cement particles and iron oxide particles and drying the thus treated sponge iron pellets.
Claim 20
Dependent Claim
36 words
A passivating agent for inhibiting re-oxidation of sponge iron pellets consisting essentially of a pulverulent mixture of 40% to 70% by weight or iron oxide particles and 60% to 30% by weight of hydraulic cement particles.
Claim 21
Dependent Claim
36 words
A passivating agent for inhibiting re-oxidation of sponge iron pellets consisting essentially of a pulverulent mixture of 40% to 70% by weight or iron oxide particles and 60% to 30% by weight of hydraulic cement particles.
Claim 22
Dependent Claim
25 words
A passivating agent according to claim 16 wherein said mixture contains 50% to 60% of iron oxide particles and 40% to 50% of cement particles.
Claim 23
Dependent Claim
26 words
A method according to claim 1 wherein said mixture contains from 50% to 60% of iron oxide particles and from 40% to 50% of cement particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-13 | 1986-12-13 | 1987-06-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-13 | 1990-12-13 | 1991-06-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-13 | 1994-12-13 | 1995-06-14 | $7700.00 | Window Closed / Lapsed |