US4387359A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Titania oxygen sensor with chrome oxide compensator
Assignee: Bendix Corp
•
Filing: 1981-01-21
•
Granted: 1983-06-07
•
Expires: 2001-01-21
Abstract
Abstract An oxygen sensor utilizes a chrome oxide compensating resistor (5) in series with a titania sensing resistor (3). The chrome oxide resistor (5) not only compensates for the effects of temperature on the titania sensing (3) resistor, but since it exhibits (p) type behavior while the titania exhibits (n) type behavior in the presence of gaseous oxygen, the sensitivity of the sensor is increased. The resistors (3, 5) can be applied as a film to a substrate (7) or they can be formed as discrete chips. Substantial quantities of alumina and glass can be added to the chrome oxide without affecting oxygen sensitivity although the electrical resistance rises substantially.
Inventors
- 👤 Tseng-Ying Tien
- 👤 David C. Weber
- 👤 Philip R. Woodruff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:00
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/02; G01N27/04; G01N27/12
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
187 words
A titania oxygen sensor with a chrome oxide compensator for detecting the oxygen content in an exhaust gas, said sensor comprising a first resistor comprised of titania, the resistance of which varies as a function of both the temperature of the exhaust gas to which it is exposed and the partial pressure of oxygen in the exhaust gas, and a second resistor consisting essentially of a calcine of chromium oxide and a modifier selected from a group consisting of aluminum oxide, zirconium oxide, platinum and glass, the resistance of which varies as a function of temperature in the same sense as the titania but varies as a function of the partial pressure of oxygen in the exhaust gas in the opposite sense to that of the titania, said first and second resistors being connected in series with a common junction such that with a source voltage connected across the two series connected resistors the voltage generated at said common junction is a function of the partial pressure of the exhaust gas to which the two resistors are exposed despite variations in the temperature of the exhaust gases.
Claim 2
Dependent Claim
187 words
A titania oxygen sensor with a chrome oxide compensator for detecting the oxygen content in an exhaust gas, said sensor comprising a first resistor comprised of titania, the resistance of which varies as a function of both the temperature of the exhaust gas to which it is exposed and the partial pressure of oxygen in the exhaust gas, and a second resistor consisting essentially of a calcine of chromium oxide and a modifier selected from a group consisting of aluminum oxide, zirconium oxide, platinum and glass, the resistance of which varies as a function of temperature in the same sense as the titania but varies as a function of the partial pressure of oxygen in the exhaust gas in the opposite sense to that of the titania, said first and second resistors being connected in series with a common junction such that with a source voltage connected across the two series connected resistors the voltage generated at said common junction is a function of the partial pressure of the exhaust gas to which the two resistors are exposed despite variations in the temperature of the exhaust gases.
Claim 3
Dependent Claim
55 words
The oxygen sensor of claim 1 wherein said first resistor comprises about 80% by weight titanium oxide and 20% platinum, the second resistor comprises a calcine of 65% by weight chromium oxide and 35% aluminum oxide, and wherein said first and second resistors are applied as a film to substantially equal areas on a substrate.
Claim 4
Dependent Claim
24 words
The oxygen sensor of claim 1 wherein said calcined and chromium oxide consists essentially of 65-79% by weight chromium oxide and 21-35% aluminum oxide.
Claim 5
Dependent Claim
27 words
The oxygen sensor of claim 1 wherein said second resistor consists essentially of a calcine of chromium oxide and up to about 35% by weight aluminum oxide.
Claim 6
Dependent Claim
30 words
The oxygen sensor of claim 1 wherein said second resistor comprises about 60% to 90% by weight of said calcine and from about 30% to 10% by weight of glass.
Claim 7
Dependent Claim
26 words
The oxygen sensor of claim 1 wherein said second resistor consists of a calcine of chromium oxide and up to about 10% by weight of glass.
Claim 8
Dependent Claim
46 words
The oxygen sensor of claims 5 wherein the ingredients in said first and second resistors are mixed with an organic vehicle and the resultant mixture is applied to a substrate, dried and fired in air to a temperature of about 850° C. for about one-half hour.
Claim 9
Dependent Claim
22 words
The sensor of claim 1 wherein said second resistor consists essentially of a calcine of chromium oxide and up to 60% glass.
Claim 10
Dependent Claim
28 words
The oxygen sensor of claim 1 wherein said second resistor consists essentially of a calcine of 50% by weight chromium oxide and 50% by weight of zirconium oxide.
Claim 11
Dependent Claim
38 words
The oxygen sensor of claim 1 wherein said second resistor comprises about 80% by weight of said calcine, 10% by weight of glass and 10% by weight of platinum, said platinum being in the form of a paste.
Claim 12
Dependent Claim
76 words
The oxygen sensor of claim 1 wherein said second resistor further includes a binder, plasticizer and a solvent which are combined with said chrome oxide and selected modifier to form a mixture which is applied to a tape, said tape being cut into desired shapes, several pieces of said tape being laminated together and electrical leads being connected to said second resistor and fired at a temperature of about 2300° F. to produce a unitray structure.
Claim 13
Dependent Claim
46 words
The oxygen sensor of claim 6 wherein the ingredients in said first and second resistors are mixed with an organic vehicle and the resultant mixture is applied to a substrate, dried and fired in air to a temperature of about 850° C. for about one-half hour.
References Cited (Backward Citations)
US3695848A
Cited
US3900815A
Cited
US4007435A
Cited
US4001756A
Cited
DE2817873A1
Cited
US4147513A
Cited
GB2005026B
Cited
US4225842A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-06 | 1986-12-06 | 1987-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-06 | 1990-12-06 | 1991-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-06 | 1994-12-06 | 1995-06-07 | $7700.00 | Window Closed / Lapsed |