Slide member
Assignee: Toyota Motor Corp
•
Filing: 1980-06-28
•
Granted: 1983-06-07
•
Expires: 2000-06-28
Abstract
Abstract The present invention relates to a slide member which has excellent wear, seizing, and scuffing resistances, and excellent adherence property, and which can be used even under high-temperature conditions, and which is suited for being applied to slide surfaces of piston rings, cylinder liners and slide surfaces of the air compressors for internal combustion engines. For this purpose, according to the present invention, the slide surface has a layer which is formed by plasma spray-coating of a powdery mixture consisting of 5 to 80% by weight of an Fe/Ni alloy and 95 to 20% by weight of an Fe/high-Cr alloy.
Inventors
- 👤 Katsumi Kondo
- 👤 Yoshio Fuwa
- 👤 Shoji Miyazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:54
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/14; B; B22; B22F; B22F1/00; B22F1/09; C; C23; C23C; C23C4/00; C23C4/04; C23C4/06; C23C4/08; F16N; F16N15/00; F16C2223/00; F16C2223/30; F16C2223/42; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/937; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12931; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
69 words
A slide member, comprising: a spray-coated layer on a base material, said spray-coated layer being provided by the plasma spray coating of a mixture consisting of from 5 to 80% by weight of a first powder of Fe/Ni alloy and from 95 to 20% by weight of a second powder of an iron-chromium alloy consisting of 55 to 70% Cr and 3 to 9% C with the balance Fe.
Claim 2
Dependent Claim
69 words
A slide member, comprising: a spray-coated layer on a base material, said spray-coated layer being provided by the plasma spray coating of a mixture consisting of from 5 to 80% by weight of a first powder of Fe/Ni alloy and from 95 to 20% by weight of a second powder of an iron-chromium alloy consisting of 55 to 70% Cr and 3 to 9% C with the balance Fe.
Claim 3
Dependent Claim
38 words
The slide member of claim 1, wherein said Fe/Ni alloy powder consists of 35 to 55% Ni; 0 to 8% Cr, 4 to 10% Si, 0 to 2% C and 0 to 3% B with the balance Fe.
Claim 4
Dependent Claim
16 words
The slide member of claim 1, wherein said layer ranges from 0.2 to 0.4 mm thick.
Claim 5
Dependent Claim
28 words
The slide member of claim 1, wherein said powder mixture consists of 10% to 70% of said Fe/Ni powder and 90% to 30% of said iron-chromium alloy powder.
Claim 6
Dependent Claim
47 words
The slide member of claim 1, wherein said Fe/Ni alloy powder consists of 42% Ni, 4.8% Cr, 1% B, 8.8% Si, and 0.9% C with the remainder iron and wherein said iron-chromium powder alloy consists of 65% Cr, 8.2% C and 1.5% Si with the balance iron.
Claim 7
Dependent Claim
77 words
A slide member, comprising: a spray-coated layer containing from 1.75-44% nickel and from 11-74.1% Cr on a base material, said spray-coated layer being provided by the plasma spray coating of a mixture consisting of from 5 to 80% by weight of a first powder of Fe/Ni alloy and from 95 to 20% by weight of a second powder of an iron-chromium alloy consisting of 55 to 70% Cr and 3 to 9% C with the balance Fe.
Claim 8
Dependent Claim
77 words
A slide member, comprising: a spray-coated layer containing from 1.75-44% nickel and from 11-74.1% Cr on a base material, said spray-coated layer being provided by the plasma spray coating of a mixture consisting of from 5 to 80% by weight of a first powder of Fe/Ni alloy and from 95 to 20% by weight of a second powder of an iron-chromium alloy consisting of 55 to 70% Cr and 3 to 9% C with the balance Fe.
References Cited (Backward Citations)
US3184331A
Cited
US3606359A
Cited
US3725017A
Cited
US3740212A
Cited
JPS5425232A
Cited
DE2849745A1
Cited
DE2816520A1
Cited
US4275090A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-06-06 | 1986-12-06 | 1987-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-06-06 | 1990-12-06 | 1991-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-06-06 | 1994-12-06 | 1995-06-07 | $7700.00 | Window Closed / Lapsed |