US4386189A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the post-chlorination of vinyl chloride polymers
Assignee: OCCIDENTIAL ELECTROCHEMICALS Corp
•
Filing: 1981-05-05
•
Granted: 1983-05-31
•
Expires: 2001-05-05
Abstract
Abstract A simple and practical method for making post-chlorinated polymers based upon vinyl chloride is provided based upon conducting the chlorination reaction on a granular polymer suspended in aqueous hydrochloric acid in the presence of a stoichiometric excess of liquid chlorine and in the absence of any significant amount or organic solvent/swelling agent. Use of photo-radiation techniques is also avoided since the reaction is activated by means of a minor fraction of a percent based upon weight of said polymer of an organic peroxy compound which decomposes to form free radicals at the temperatures involved in the reaction.
Inventors
- 👤 Alfred J. Ackerman
- 👤 David L. Lull
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:03
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/18; C08F8/20; C08F8/22
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
178 words
A process for the post-chlorination of a granular, microporous solid polymer of which about 75 to about 100 percent by weight is derived from vinyl chloride so as to increase the chlorine content thereof by at least about 5 percent by weight, said process comprising (a) establishing a reaction mass having a stoichiometric excess of liquified chlorine, providing a distinct liquid chlorine phase, (b) permitting reaction of granular polymer contained in said reaction mass at a temperature of between about 30° and about 75° C. and in the presence of a minor fraction of a percent by weight based on said polymer of organic peroxy catalyst which generates organic free radicals at said temperature, and (c) maintaining said liquid chlorine phase of the reaction mass through the major portion of chlorination while also maintaining reactants as a thorough intermixture in a pool of aqueous hydrochloric acid which is at least equal to the weight of said polymer and in the presence of less than 1 percent by weight, based on said polymer, of organic solvents or swelling agents.
Claim 2
Dependent Claim
178 words
A process for the post-chlorination of a granular, microporous solid polymer of which about 75 to about 100 percent by weight is derived from vinyl chloride so as to increase the chlorine content thereof by at least about 5 percent by weight, said process comprising (a) establishing a reaction mass having a stoichiometric excess of liquified chlorine, providing a distinct liquid chlorine phase, (b) permitting reaction of granular polymer contained in said reaction mass at a temperature of between about 30° and about 75° C. and in the presence of a minor fraction of a percent by weight based on said polymer of organic peroxy catalyst which generates organic free radicals at said temperature, and (c) maintaining said liquid chlorine phase of the reaction mass through the major portion of chlorination while also maintaining reactants as a thorough intermixture in a pool of aqueous hydrochloric acid which is at least equal to the weight of said polymer and in the presence of less than 1 percent by weight, based on said polymer, of organic solvents or swelling agents.
Claim 3
Dependent Claim
19 words
A process as in claim 1 which is conducted in the substantial absence of actinic radiation or molecular oxygen.
Claim 4
Dependent Claim
22 words
A process as in claim 1 wherein said granular polymer is largely between about 10 and about 500 microns in particle size.
Claim 5
Dependent Claim
33 words
A process as in claim 1 wherein said aqueous hydrochloric acid is at least about twice the weight of said polymer and contains from about 10 to about 30 percent HCl by weight.
Claim 6
Dependent Claim
48 words
A process as in any of the previous claims wherein the amount of liquefied chlorine introduced is at least about 35 percent by weight of said granular polymer, and the amount of said organic peroxy catalyst is between about 0.01 percent and about 0.3 percent thereof by weight.
Claim 7
Dependent Claim
88 words
A process as in claim 1 or 2 wherein the weight average molecular weight of the starting granular polymer is not substantially less than about 100,000; the vinyl chloride content of the same is at least about 85 percent by weight; said organic peroxy catalyst is chosen from peroxy carboxylic acid esters, diorganoperoxycarbonates, diacyl peroxides, mixed anhydrides of organic sulfoperacids with carboxylic acids and mixtures thereof; and the total concentration of said catalyst is between about 0.02 percent and about 0.2 percent by weight of said starting polymer.
Claim 8
Dependent Claim
31 words
A process as in claim 6 wherein the pressure is maintained above the vapor pressure of liquid chlorine until at least the major part of the ultimate chlorination has been accomplished.
Claim 9
Dependent Claim
37 words
A process as in claim 6 wherein the chlorination is accomplished within a period of about 1 to about 5 hours, and the pressure is above the vapor pressure of liquid chlorine throughout substantially the entire chlorination.
Claim 10
Dependent Claim
38 words
A process as in claim 6 wherein a major portion of the total catalyst is added at the beginning but at least one addition of same is made after a major part of the ultimate chlorination has occurred.
Claim 11
Dependent Claim
25 words
A process as in claim 1 wherein the amount of liquefied chlorine charged does not substantially exceed the amount by weight of said granular polymer.
References Cited (Backward Citations)
GB609693A
Cited
US2590651A
Cited
US2996489A
Cited
US3100762A
Cited
US3287336A
Cited
GB976001A
Cited
US3328371A
Cited
GB1120769A
Cited
US3506637A
Cited
GB1200711A
Cited
US3598708A
Cited
US3700632A
Cited
GB1378364A
Cited
US4049517A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-30 | 1986-11-29 | 1987-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-30 | 1990-11-29 | 1991-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-30 | 1994-11-29 | 1995-05-31 | $7700.00 | Window Closed / Lapsed |