Electroplating baths, additives therefor and methods for the electrodeposition of metals

Claim 2

An aqueous acidic electroplating bath composition comprising (a) at least one bath soluble divalent or polyvalent metal salt, and (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR8## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 3

The electroplating bath of claim 1 wherein the metal of (a) is tin, lead, copper, zinc, cadmium or tin/lead mixtures.

Claim 4

The electroplating bath of claim 1 wherein the metal is tin or a tin/lead mixture.

Claim 5

The electroplating bath of claim 1 wherein the metal is zinc.

Claim 6

The electroplating bath of claim 1 wherein the metal is cadmium.

Claim 7

The electroplating bath of claim 1 wherein the metal is copper.

Claim 8

An aqueous acidic plating bath for electrodeposition of tin, lead or tin/lead alloy comprising (a) at least one bath soluble metal salt selected from the group consisting of a stannous salt, a lead salt, or a mixture of lead and stannous salts, and (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR9## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 9

An aqueous acidic plating bath for electrodeposition of tin, lead or tin/lead alloy comprising (a) at least one bath soluble metal salt selected from the group consisting of a stannous salt, a lead salt, or a mixture of lead and stannous salts, and (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR9## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 10

The plating bath of claim 7 wherein the bath contains fluoborate, fluosilicate, sulfate or sulfonate groups or mixtures thereof.

Claim 11

The plating bath of claim 7 wherein the bath further contains an additional component (c) comprising at least one carbonyl compound.

Claim 12

The plating bath of claim 9 wherein the carbonyl compound of component (c) is an aldehyde, ketone or carboxylic acid.

Claim 13

The plating bath of claim 9 wherein the carbonyl compound is an aromatic aldehyde or ketone.

Claim 14

The plating bath of claim 7 wherein the bath also contains (d) at least one aromatic amine.

Claim 15

An aqueous acid plating bath for electrodeposition of a tin, lead or a tin/lead alloy comprising from about 5 to about 350 grams per liter of (a) at least one metal ion selected from the group consisting of stannous ions, lead ions and mixtures thereof, from about 50 to about 500 grams per liter of at least one radical selected from the group consisting of fluoborates, fluosilicates, sulfates, sulfamates and mixtures thereof, (b) from about 0.5 to about 15 grams per liter of at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR10## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20, (c) from 0 to about 10 grams per liter of at least one aromatic aldehyde, and (d) from 0 to about 15 grams per liter of an aromatic amine.

Claim 16

An aqueous acid plating bath for electrodeposition of a tin, lead or a tin/lead alloy comprising from about 5 to about 350 grams per liter of (a) at least one metal ion selected from the group consisting of stannous ions, lead ions and mixtures thereof, from about 50 to about 500 grams per liter of at least one radical selected from the group consisting of fluoborates, fluosilicates, sulfates, sulfamates and mixtures thereof, (b) from about 0.5 to about 15 grams per liter of at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR10## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20, (c) from 0 to about 10 grams per liter of at least one aromatic aldehyde, and (d) from 0 to about 15 grams per liter of an aromatic amine.

Claim 17

An aqueous acidic zinc electroplating bath which comprises zinc ions, and from about 0.5 to about 15 grams per liter of (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR11## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 18

An aqueous acidic zinc electroplating bath which comprises zinc ions, and from about 0.5 to about 15 grams per liter of (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR11## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 19

The electroplating bath of claim 14 wherein the bath also contains chloride ions and boric acid.

Claim 20

The electroplating bath of claim 14 wherein the bath also contains an additional component (c) comprising at least one carbonyl-containing compound.

Claim 21

The electroplating bath of claim 16 wherein the carbonyl compound is an aromatic carbonyl compound.

Claim 22

The electroplating bath of claim 17 wherein the aromatic carbonyl compound is an aromatic aldehyde, ketone or carboxylic acid or bath-soluble salt of a carboxylic acid.

Claim 23

The electroplating bath of claim 16 wherein the bath also contains (e) at least one nonionic or cationic wetting agent.

Claim 24

An aqueous acid zinc electroplating bath comprising (a) from about 5 to about 75 grams per liter of zinc ion, from about 10 to about 75 grams per liter of boric acid, from about 50 to about 300 grams per liter of ammonium, sodium or potassium fluoride, (b) from about 1 to about 15 grams per liter of at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR12## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20, (c) from about 0 to about 30 grams per liter of an aromatic carbonyl-containing compound selected from a group consisting of aldehydes, ketones, acids and mixtures thereof, and (e) from 0 to about 25 grams per liter of a non-ionic or cationic wetting agent.

Claim 25

An aqueous acid zinc electroplating bath comprising (a) from about 5 to about 75 grams per liter of zinc ion, from about 10 to about 75 grams per liter of boric acid, from about 50 to about 300 grams per liter of ammonium, sodium or potassium fluoride, (b) from about 1 to about 15 grams per liter of at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR12## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20, (c) from about 0 to about 30 grams per liter of an aromatic carbonyl-containing compound selected from a group consisting of aldehydes, ketones, acids and mixtures thereof, and (e) from 0 to about 25 grams per liter of a non-ionic or cationic wetting agent.

Claim 26

An aqueous electroplating bath for the electrodeposition of cadmium comprising (a) cadmium ions and a free acid, and (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR13## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 27

An aqueous electroplating bath for the electrodeposition of cadmium comprising (a) cadmium ions and a free acid, and (b) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR13## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 28

The plating bath of claim 21 wherein the bath also contains (c) at least one organic brightener compound selected from the group consisting of pyridines and aromatic carbonyl-containing compounds.

Claim 29

The electroplating bath of claim 21 wherein the free acid is sulfuric acid, fluoboric acid or mixtures thereof.

Claim 30

The plating bath of claim 21 wherein the bath also contains (d) a condensed naphthalene sulfonic acid.

Claim 31

An aqueous acidic copper electroplating bath containing one or more bath-soluble copper salts, free acid, and at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR14## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 32

An aqueous acidic copper electroplating bath containing one or more bath-soluble copper salts, free acid, and at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR14## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20.

Claim 33

The plating bath of claim 25 wherein the bath also contains chloride ions.

Claim 34

The plating bath of claim 25 wherein the bath further contains an additional component (i) which comprises at least one wetting agent.

Claim 35

The plating bath of claim 27 wherein the wetting agent (i) is a polyalkylene glycol, a polyalkylene glycol ether, a composition prepared by addition of propylene oxide to ethylene diamine followed by the addition of ethylene oxide, or mixtures thereof.

Claim 36

The copper plating bath of claim 28 wherein the wetting agent (i) is a polyethylene oxide having a molecular weight of from about 400 to about 6000.

Claim 38

An additive composition for aqueous acid metal electroplating baths comprising a mixture of (a) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR15## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20, (b) an additional component which comprises at least one brightener composition which is a pyridine or a carbonyl-containing compound, and (c) a solvent.

Claim 39

An additive composition for aqueous acid metal electroplating baths comprising a mixture of (a) at least one surfactant of the formula ROCH.sub.2 CH(CH.sub.3)OCH.sub.2 CH(CH.sub.3)N(H)CH.sub.2 CH.sub.2 COOH (I) or ##STR15## wherein R is an alkyl group containing 10 to 12 carbon atoms; x and y are integers, the sum of which is from 2 to about 20, (b) an additional component which comprises at least one brightener composition which is a pyridine or a carbonyl-containing compound, and (c) a solvent.

Claim 40

The additive composition of claim 31 wherein the carbonyl compound is an aromatic carbonyl-containing compound.

Claim 41

The additive composition of claim 31 wherein the composition also contains an additional component (d) comprising at least one wetting agent.