Linear hydroquinone phenoxy polymers and process
Assignee: Eastman Chemical Co
•
Filing: 1981-02-23
•
Granted: 1983-05-10
•
Expires: 2001-02-23
Abstract
Abstract This invention relates to a process for the preparation of thermoplastic polymers. Specifically it relates to a process for the preparation of a substantially linear, high molecular weight phenoxy resin from substituted hydroquinone, less than 80 mole percent of hydroquinone and optionally up to about 20 mole percent of a second aromatic diol, epichlorohydrin (or another epihalohydrin) and a base, such as sodium hydroxide. Hydroquinone phenoxy resins of this invention are characterized by low permeability to oxygen and carbon dioxide and are, therefore, useful as a gas-barrier layer in multilayer plastic film constructions used in food packaging and beverage bottle applications, for example. For use in such applications, the resin is generally in the form of a thin, uniform film prepared by extrusion, casting, or other such method. It is highly desirable that polymers used in this manner be as free as possible from chain branches or cross-links, as these lead to the formation of gel particles which cause imperfections in the polymer film. These imperfections, in turn, detract from the appearance of the film. Moreover, as is well known, increasing the amount of chain branching in a polymer results in an undesirable reduction of flexibility and toughness.
Inventors
- 👤 Eric G. Olsen
- 👤 Winston J. Jackson, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:26
CPC Classifications
C; C08; C08G; C08G65/00; C08G65/02; C08G65/26; C08G65/2603; C08G65/2606; C08G65/2612; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
92 words
Process for the preparation of high molecular weight hydroquinone phenoxy polymer from at least 21 mole percent hydroquinone substituted with one or two substituents selected from chlorine or an alkyl group containing 1-4 carbon atoms and mixtures thereof, 0 to 79% mole percent hydroquinone and an epihalohydrin, said process comprising reacting the hydroquinone compounds with about 0.95 to about 1.05 equivalents of an epihalohydrin in the presence of about 1.0 to 1.1 equivalents of a base and of about one to seven parts by weight solvent for said polymer per part polymer.
Claim 2
Dependent Claim
92 words
Process for the preparation of high molecular weight hydroquinone phenoxy polymer from at least 21 mole percent hydroquinone substituted with one or two substituents selected from chlorine or an alkyl group containing 1-4 carbon atoms and mixtures thereof, 0 to 79% mole percent hydroquinone and an epihalohydrin, said process comprising reacting the hydroquinone compounds with about 0.95 to about 1.05 equivalents of an epihalohydrin in the presence of about 1.0 to 1.1 equivalents of a base and of about one to seven parts by weight solvent for said polymer per part polymer.
Claim 3
Dependent Claim
23 words
Process of claim 1 wherein water is present in the amount of about 0.8 to 10 parts by weight water per part polymer.
Claim 4
Dependent Claim
11 words
Process of claim 2 wherein said solvent is immisible with water.
Claim 5
Dependent Claim
24 words
Process of claim 1 wherein said solvent is selected from cyclohexanone, 2-butanone, acetophenone, dichloromethane, γ-butyrolactone, sulfolane, dimethyl sulfoxide, N-methyl-2-pyrrolidone, N,N-dimethyl formamide and triethyl phosphate.
Claim 6
Dependent Claim
24 words
Process of claim 1 wherein said base is selected from sodium hydroxide, potassium hydroxide, lithium hydroxide, tetraalkylammonium hydroxides and alkali metal salts of alcohols.
Claim 7
Dependent Claim
25 words
Process of claim 1 wherein a phase transfer catalyst is present in the amount of up to about 10 mole percent of the hydroquinone compound.
Claim 8
Dependent Claim
20 words
Process of claim 6 wherein said catalyst is selected from quaternary ammonium halides, sulfates, acetates, cyclic polyethers and acyclic polyethers.
Claim 9
Dependent Claim
22 words
Process of claim 7 wherein said catalyst is present in the amount of 1 to 5 mole percent of the hydroquinone compound.
Claim 10
Dependent Claim
15 words
Process of claim 8 wherein said catalyst is selected from benzyltrimethylammonium chloride and benzyltriethylammonium chloride.
Claim 11
Dependent Claim
16 words
Process of claim 1 wherein the reaction temperature is from about 50° C. to 100° C.
Claim 12
Dependent Claim
16 words
Process of claim 1 wherein the reaction temperature is from about 80° C. to 90° C.
Claim 13
Dependent Claim
22 words
Process of claim 1 wherein said hydroquinone phenoxy polymer is modified with up to about 20 mole percent of another aromatic diol.
Claim 14
Dependent Claim
10 words
Process of claim 12 wherein said aromatic diol is resorcinol.
Claim 15
Dependent Claim
22 words
Process of claim 1 wherein said hydroquinone phenoxy polymer is modified with up to about 10 mole percent of another aromatic diol.
Claim 16
Dependent Claim
10 words
Process of claim 14 wherein said aromatic diol is resorcinol.
Claim 17
Dependent Claim
94 words
Linear hydroquinone phenoxy polymer prepared from at least 21% hydroquinone substituted with one or two substituents selected from chlorine or an alkyl group containing 1-4 carbon atoms, and mixtures thereof, 0 to 79% hydroquinone and an epihalohydrin, said polymer being characterized by an inherent viscosity of about 0.45 to 0.9 as determined at 25° C. in a 60/40 by volume mixture of phenol/tetrachloroethane solvent at a concentration of 0.5 gram/deciliter, a molecular weight distribution, as determined by gel permeation chromatography, of Mw / .sbsb.Mn ≦ about 4 and Mz / .sbsb.Mn ≦ about 10.
Claim 18
Dependent Claim
94 words
Linear hydroquinone phenoxy polymer prepared from at least 21% hydroquinone substituted with one or two substituents selected from chlorine or an alkyl group containing 1-4 carbon atoms, and mixtures thereof, 0 to 79% hydroquinone and an epihalohydrin, said polymer being characterized by an inherent viscosity of about 0.45 to 0.9 as determined at 25° C. in a 60/40 by volume mixture of phenol/tetrachloroethane solvent at a concentration of 0.5 gram/deciliter, a molecular weight distribution, as determined by gel permeation chromatography, of Mw / .sbsb.Mn ≦ about 4 and Mz / .sbsb.Mn ≦ about 10.
Claim 19
Dependent Claim
16 words
Linear hydroquinone phenoxy polymer of claim 16, wherein the inherent viscosity is about 0.5 to 0.7.
Claim 20
Dependent Claim
15 words
Linear hydroquinone phenoxy polymer of claim 16 wherein Mw / .sbsb.Mn is ≦ about 3.
Claim 21
Dependent Claim
19 words
Linear hydroquinone phenoxy polymer of claim 16 modified with up to about 20 mole percent of an aromatic diol.
Claim 22
Dependent Claim
13 words
Linear hydroquinone phenoxy polymer of claim 19 wherein said aromatic diol is resorcinol.
Claim 23
Dependent Claim
19 words
Linear hydroquinone phenoxy polymer of claim 16 modified with up to about 10 mole percent of an aromatic diol.
Claim 24
Dependent Claim
10 words
Linear hydroquinone phenoxy polymer wherein said aromatic diol is resorcinol.
Claim 25
Dependent Claim
10 words
Linear hydroquinone phenoxy polymer wherein said aromatic diol is resorcinol.
Claim 26
Dependent Claim
8 words
Shaped object of the polymer of claim 16.
Claim 27
Dependent Claim
8 words
Shaped object of the polymer of claim 19.
Claim 28
Dependent Claim
8 words
Shaped object of the polymer of claim 20.
Claim 29
Dependent Claim
8 words
Shaped object of the polymer of claim 21.
Claim 30
Dependent Claim
8 words
Shaped object of the polymer of claim 22.
References Cited (Backward Citations)
US2602075A
Cited
US3395118A
Cited
US3238087A
Cited
US3701680A
Cited
US3767618A
Cited
US4267301A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-09 | 1986-11-08 | 1987-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-09 | 1990-11-08 | 1991-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-09 | 1994-11-08 | 1995-05-10 | $7700.00 | Window Closed / Lapsed |