Process for the preparation of low temperature flexible polyurethane elastomers
Assignee: BASF SE
•
Filing: 1981-11-06
•
Granted: 1983-05-10
•
Expires: 2001-11-06
Abstract
Abstract Low temperature flexible polyurethane elastomers are prepared by reacting organic polyisocyanates with polyester polyols which have glass transition temperatures of -10° to -80° C. and incorporating therein alkoxylated esters of fatty acids and/or alkoxylated terpene alcohols.
Inventors
- 👤 Dietmar Nissen
- 👤 Hans U. Schmidt
- 👤 Wolfgang Straehle
- 👤 Uwe Schuett
- 👤 Matthias Marx
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 02:46
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/487; C08G18/30; C08G18/36; C08G18/4009; C08G18/4018; C08G18/4891; C08G18/65; C08G18/66; C08G18/6629; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/0058; C08G2110/0066; C08G2110/0083; Y; Y10; Y10S; Y10S521/00; Y10S521/904
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
86 words
A process for the preparation of low temperature flexible polyurethane elastomers by reacting organic polyisocyanates, polyols, alkoxylated fatty acid esters and/or alkoxylated terpene alcohols in the presence of catalysts and optionally chain extenders, blowing agents, stabilizers, pigments, surface active agents and flame retardants wherein said polyols are selected from the group consisting of polyester polyols having a hydroxyl number of 40 to 120 and a glass transition temperature range of -10° C. to -80° C. and polytetrafuran polyols having a hydroxyl number of 20 to 250.
Claim 2
Dependent Claim
86 words
A process for the preparation of low temperature flexible polyurethane elastomers by reacting organic polyisocyanates, polyols, alkoxylated fatty acid esters and/or alkoxylated terpene alcohols in the presence of catalysts and optionally chain extenders, blowing agents, stabilizers, pigments, surface active agents and flame retardants wherein said polyols are selected from the group consisting of polyester polyols having a hydroxyl number of 40 to 120 and a glass transition temperature range of -10° C. to -80° C. and polytetrafuran polyols having a hydroxyl number of 20 to 250.
Claim 3
Dependent Claim
38 words
The process of claim 1 wherein the concentration of alkoxylated fatty acid esters and/or alkoxylated terpene alcohols is from 0.1 to 6 parts by weight based on 100 parts by weight of polyol and optionally chain extending agents.
Claim 4
Dependent Claim
37 words
The process of claim 1 wherein said alkoxylated fatty acid esters contain 8 to 26 carbon atoms in the fatty acid radical and 1 to 30 moles of ethylene oxide and/or propylene oxide in the alkoxy radical.
Claim 5
Dependent Claim
16 words
The process of claim 1 wherein said fatty acid esters are mono-, di-, and/or triglyceride esters.
Claim 6
Dependent Claim
38 words
The process of claim 1 wherein said alkoxylated terpene alcohols consist of alcohols containing 10 to 25 carbon atoms in the alcohol radical and 1 to 30 moles of ethylene oxide and/or propylene oxide per mole of alcohol.
Claim 7
Dependent Claim
33 words
The process of claim 1 wherein a prepolymer with an NCO content of 10 to 25 percent by weight based on the weight of polyisocyanate is employed for the preparation of the elastomers.
Claim 8
Dependent Claim
25 words
The process of claim 5 wherein the polyisocyanate is selected from the group consisting of 4,4'-diphenylmethane diisocyanate, and carbodiimide and/or allophanate group containing 4,4'-diphenylmethane diisocyanate.
Claim 9
Dependent Claim
45 words
The process of claim 4 wherein the ratio of reactive hydrogen atoms of the polyols, alkoxylated fatty acid esters, and/or alkoxylated terpene alcohols and optionally chain extenders or cross-linking agents to NCO groups of the polyisocyanates or NCO group containing prepolymers, is 0.90:1 to 1.15:1.
Claim 10
Dependent Claim
156 words
A process for the preparation of low temperature flexible elastomers wherein (a) polyester polyol prepolymers with NCO contents of 10 to 20 percent by weight based on the weight of polyisocyanate, (b) polyesterdiols having OH numbers of 40 to 120 and glass transition temperatures of -10° C. to -80° C., (c) alkoxylated fatty acid esters produced by alkoxylation of fatty acid esters having 8 to 26 carbon atoms in the fatty acid radical with ethylene and/or propylene oxide in a mole ratio of 1:1 to 1:30 and (d) optionally chain extenders or cross-linking agents are reacted in the presence of catalysts, blowing agents and additives in quantities of 0.1 to 6 parts by weight of component (c) per 100 parts by weight of component (b) and optionally (d), wherein the mole ratios of reactive hydrogen atoms of the components (b), (c) and optionally (d) to the NCO groups of components (a) range from 0.90:1 to 1.15:1.
Claim 11
Dependent Claim
156 words
A process for the preparation of low temperature flexible elastomers wherein (a) polyester polyol prepolymers with NCO contents of 10 to 20 percent by weight based on the weight of polyisocyanate, (b) polyesterdiols having OH numbers of 40 to 120 and glass transition temperatures of -10° C. to -80° C., (c) alkoxylated fatty acid esters produced by alkoxylation of fatty acid esters having 8 to 26 carbon atoms in the fatty acid radical with ethylene and/or propylene oxide in a mole ratio of 1:1 to 1:30 and (d) optionally chain extenders or cross-linking agents are reacted in the presence of catalysts, blowing agents and additives in quantities of 0.1 to 6 parts by weight of component (c) per 100 parts by weight of component (b) and optionally (d), wherein the mole ratios of reactive hydrogen atoms of the components (b), (c) and optionally (d) to the NCO groups of components (a) range from 0.90:1 to 1.15:1.
Claim 12
Dependent Claim
5 words
The product of claim 1.
Claim 13
Dependent Claim
5 words
The product of claim 2.
Claim 14
Dependent Claim
5 words
The product of claim 3.
Claim 15
Dependent Claim
5 words
The product of claim 4.
Claim 16
Dependent Claim
5 words
The product of claim 5.
Claim 17
Dependent Claim
5 words
The product of claim 6.
Claim 18
Dependent Claim
5 words
The product of claim 7.
Claim 19
Dependent Claim
5 words
The product of claim 8.
Claim 20
Dependent Claim
5 words
The product of claim 9.
References Cited (Backward Citations)
US2936293A
Cited
US2954369A
Cited
US2953539A
Cited
GB874766A
Cited
US3094510A
Cited
US3248348A
Cited
US3201359A
Cited
US3423339A
Cited
US4201847A
Cited
US3929732A
Cited
US4130698A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-09 | 1986-11-08 | 1987-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-09 | 1990-11-08 | 1991-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-09 | 1994-11-08 | 1995-05-10 | $7700.00 | Window Closed / Lapsed |