Method for producing catalysts for gas phase oxidation of saturated and/or unsaturated C4 -hydrocarbons to maleic anhydride
Assignee: Huels AG
•
Filing: 1981-03-16
•
Granted: 1983-05-10
•
Expires: 2001-03-16
Abstract
Abstract A method for producing catalysts for gas phase oxidation of saturated or unsaturated hydrocarbons to maleic anhydride is disclosed comprising: (a) mixing a vanadium compound containing pentavalent vanadium with orthophosphoric acid in an alcohol from the series of monohydric lower aliphatic alcohols having 2-8 C-atoms in the optional presence of promoters, and a reducing agent combination of H 3 PO 3 +alcohol wherein the sum of H 3 PO 3 and H 3 PO 4 is so controlled that an atomic ratio of P to V of 1.0 to 1.2 is attained and wherein said H 3 PO 3 is used in such sub-stoichiometric amounts that it is sufficient to reduce the vanadium to an oxidation state only of 4.2 to 4.4, and then said reducing agent combination is used to further reduce the vanadium to an oxidation state between 3.9 to 4.0, any water if present being distilled off as an azeotrope with the alcohol by heating; (b) adding titanium dioxide obtained through high temperature pyrolysis of titanium tetrahalide and optional additional promoters Ni, Fe, Li, Mg; (c) forming precipitated catalyst in a known manner; and (d) activating the catalyst in an oxidation reactor at temperatures of about 450° to 510° C. for about 12 to 72 hours in the presence of an air-hydrocarbon stream.
Inventors
- 👤 Kurt Neubold
- 👤 Klaus-Dieter Gollmer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:40
CPC Classifications
C; C07; C07C; C07C51/00; C07C51/16; C07C51/21; C07C51/25; C07C51/252; B; B01; B01J; B01J23/00; B01J23/002; B01J23/16; B01J23/20; B01J23/22; B01J27/00; B01J27/14; B01J27/186; B01J27/195; B01J27/198; C07C51/215; B01J2523/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
209 words
A method for producing catalysts for gas phase oxidation of saturated or unsaturated hydrocarbons to maleic anhydride, comprising: (a) mixing a vanadium compound containing pentavalent vanadium with orthophosphoric acid in an alcohol from the series of monohydric lower aliphatic alcohols having 2-8 C-atoms, and a reducing agent combination of H 3 PO 3 +alcohol wherein the sum of H 3 PO 3 and H 3 PO 4 is so controlled that an atomic atomic ratio of P to V of 1.0 to 1.2 is attained and wherein said H 3 PO 3 is used in such sub-stoichiometric amounts that it is sufficient to reduce the vanadium to an oxidation state only of 4.2 to 4.4, and then said reducing agent combination is used to further reduce the vanadium to an oxidation state between 3.9 and 4.0, any water if present being distilled off as an azeotrope with the alcohol by heating; (b) adding titanium dioxide obtained through high temperature pyrolysis of titanium tetrahalide and optional additional promoters Ni, Fe, Li, Mg; (c) forming precipitated catalyst in a known manner; and (d) activating thhe catalyst in an oxidation reactor at temperatures of about 450° to 510° C. for about 12 to 72 hours in the presence of an air-hydrocarbon stream.
Claim 2
Independent Claim
209 words
A method for producing catalysts for gas phase oxidation of saturated or unsaturated hydrocarbons to maleic anhydride, comprising: (a) mixing a vanadium compound containing pentavalent vanadium with orthophosphoric acid in an alcohol from the series of monohydric lower aliphatic alcohols having 2-8 C-atoms, and a reducing agent combination of H 3 PO 3 +alcohol wherein the sum of H 3 PO 3 and H 3 PO 4 is so controlled that an atomic atomic ratio of P to V of 1.0 to 1.2 is attained and wherein said H 3 PO 3 is used in such sub-stoichiometric amounts that it is sufficient to reduce the vanadium to an oxidation state only of 4.2 to 4.4, and then said reducing agent combination is used to further reduce the vanadium to an oxidation state between 3.9 and 4.0, any water if present being distilled off as an azeotrope with the alcohol by heating; (b) adding titanium dioxide obtained through high temperature pyrolysis of titanium tetrahalide and optional additional promoters Ni, Fe, Li, Mg; (c) forming precipitated catalyst in a known manner; and (d) activating thhe catalyst in an oxidation reactor at temperatures of about 450° to 510° C. for about 12 to 72 hours in the presence of an air-hydrocarbon stream.
Claim 3
Dependent Claim
38 words
The method according to claim 1, wherein said titanium dioxide has a surface area of about 50 to 80 m 2 /g, in an amount to make the atomic ratio of Ti to V between 0.05 and 0.4.
Claim 4
Dependent Claim
44 words
The method according to claim 1 wherein nickel and iron, individually or in combination and optionally combined with lithium or magnesium, are used as additional promoters in the form of oxides of these elements obtained through heating salts of these elements at 500°-600° C.
Claim 5
Dependent Claim
40 words
The method according to claim 1 or 3 wherein the atomic ratios of Ni or Fe to vanadium or Ni+Fe to vanadium are between 0.01 and 0.05 and those of Li or Mg to vanadium are between 0.001 and 0.02.
Claim 6
Dependent Claim
55 words
The method according to claim 1 wherein the catalyst is heated in an air stream to temperatures between 300° and 350° C. before it is activated, and the air in this temperature range is replaced by a mixture of air and an unsaturated or saturated C 4 -hydrocarbon, and the activation temperature is 450°-510° C.
Claim 7
Dependent Claim
22 words
The method according to claim 1 wherein the catalyst is activated at a hydrocarbon throughput of 10-20 g of hydrocarbon/cm 2 .hr.
Claim 8
Dependent Claim
26 words
The method according to claim 1 wherein activation is carried out with an air-hydrocarbon mixture in which the weight ratio of air to hydrocarbon is 25-50:1.
Claim 9
Dependent Claim
18 words
A process according to any one of the claims 1-4, 6-7 wherein in step (a) promoters are present.
References Cited (Backward Citations)
US3915892A
Cited
US3985775A
Cited
US4111963A
Cited
US4132670A
Cited
US4062873A
Cited
US4064070A
Cited
US4149992A
Cited
US4147661A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-09 | 1986-11-08 | 1987-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-09 | 1990-11-08 | 1991-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-09 | 1994-11-08 | 1995-05-10 | $7700.00 | Window Closed / Lapsed |