Process for treating hydrocarbon feedstocks with CO and H2 O in the presence of steam stable catalysts

Claim 2

A process for treating hydrocarbon feeds to remove contaminants comprising sulfur, nitrogen, oxygen, metals or combinations thereof comprising contacting the feed and a treating gas comprising water and carbon monoxide under reaction conditions in the presence of a catalyst comprising (1) a metallic component having shift and hydrogenating activity, (2) a support component comprising activated alumina and (3) a steam-stabilizing phosphorus component.

Claim 3

The process of claim 1 wherein the metallic component having shift and hydrogenating activity comprises at least one Group VIII non-noble metal.

Claim 4

The process of claim 2 wherein reaction conditions comprise a temperature of about 500° to about 850° F., pressure of about 100 to about 3000 psig, space velocity of about 0.1 to about 10 pounds feed per pound of catalyst per hour and the treating gas is employed in an amount effective to provide a hydrogen addition rate of about 200 to about 10,000 SCFB.

Claim 5

The process of claim 3 wherein the treating gas contains sufficient water and carbon monoxide to satisfy at least about 20 vol% of the hydrogen addition rate.

Claim 6

The process of claim 4 wherein steam is present in the treating gas in at least a stoichiometric amount relative to carbon monoxide.

Claim 7

The process of claim 2 wherein the steam stabilizing phosphorus component is present in an amount ranging from about 0.5 to about 20 wt% expressed as P 2 O 5 and based on total catalyst weight.

Claim 8

The process of claim 2 wherein the metallic component (1) comprises, in addition to said Group VIII non-noble metal, at least one hydrogenation-promoting component or at least one shift promoting component or a combination of said hydrogenation and shift-promoting components.

Claim 9

The process of claim 2 wherein the steam-stabilizing phosphorus component is incorporated into the catalyst through the use of at least one precursor to the phosphorus component during preparation of the support component.

Claim 10

The process of claim 2 wherein the steam-stabilizing phosphorus component is incorporated into the catalyst by treatment of the support component with at least one precursor to the phosphorus component prior to incorporation of metallic component into the catalyst.

Claim 11

The process of claim 2 wherein the steam-stabilizing phosphorus component is incorporated into the catalyst by impregnation of the support component with at least one solution of at least one precursor to the metallic component in at least one precursor to the phosphorus component.

Claim 12

The process of claim 2 wherein the steam-stabilizing phosphorus component is incorporated into the catalyst by treatment of preformed catalyst with at least one precursor to the phosphorus component.

Claim 13

The process of any of claims 8-11 wherein the precursor to the phosphorus component comprises phosphoric acid.

Claim 14

A process for desulfurization of hydrocarbon feeds containing at least about 1.5 wt% sulfur comprising contacting the feed with treating gas comprising hydrogen, steam and carbon monoxide wherein the molar ratio of steam to carbon monoxide is greater than about 1:1, such treating gas being present in an amount effective to provide a hydrogen addition rate of about 350 to about 8000 SCFB, of which at least 20 vol% is provided by reaction of said water and carbon monoxide, at a temperature of about 600° to about 800° F., pressure of about 200 to about 2500 psig and space velocity of about 0.2 to about 8 lb/lb/hr in the presence of a catalyst comprising (1) a metallic component comprising nickel having shift and hydrogenating activity, (2) a support component comprising activated alumina and (3) a steam-stabilizing phosphorus component.

Claim 15

A process for desulfurization of hydrocarbon feeds containing at least about 1.5 wt% sulfur comprising contacting the feed with treating gas comprising hydrogen, steam and carbon monoxide wherein the molar ratio of steam to carbon monoxide is greater than about 1:1, such treating gas being present in an amount effective to provide a hydrogen addition rate of about 350 to about 8000 SCFB, of which at least 20 vol% is provided by reaction of said water and carbon monoxide, at a temperature of about 600° to about 800° F., pressure of about 200 to about 2500 psig and space velocity of about 0.2 to about 8 lb/lb/hr in the presence of a catalyst comprising (1) a metallic component comprising nickel having shift and hydrogenating activity, (2) a support component comprising activated alumina and (3) a steam-stabilizing phosphorus component.

Claim 16

The process of claim 13 wherein the catalyst comprises about 1 to about 8 wt% nickel oxide or cobalt oxide and about 2 to about 15 wt% phosphorus expressed as P 2 O 5 , such weight percentages being based on total catalyst weight.

Claim 17

The process of claim 13 wherein the feed comprises a petroleum or synthetic crude oil distillate, gas oil or residue and reaction conditions comprise a temperature of about 600° to about 800° F., pressure of about 300 to about 2500 psig, weight hourly space velocity of about 0.2 to about 4 lb/lb/hr and the treating gas is present in an amount effective to provide a hydrogen consumption rate of about 400 to about 8000 SCFB.

Claim 18

The process of claim 15 wherein the catalyst comprises about 2 to about 6 wt% nickel oxide, about 8 to about 18 wt% molybdenum oxide, at least about 75 wt% activated alumina and about 2 to about 8 wt% phosphorus expressed as P 2 O 5 , such weight percentages being based on total catalyst weight.