Method and apparatus for shaping moving glass sheets by sagging followed by roll pressing
Assignee: PPG Industries Ohio Inc
•
Filing: 1982-01-25
•
Granted: 1983-05-03
•
Expires: 2002-01-25
Abstract
Abstract This invention relates to shaping glass sheets by roll forming to either simple or complex curvatures about a single axis of bending or to compound curvatures comprising components of curvature about mutually perpendicular axes of bending by a controlled, repeatable program of roll forming without causing the glass sheets to stop their forward movement during their shaping. The apparatus used to perform this process has a minimum of moving parts, thus minimizing maintenance problems and reducing downtime for maintenance and repair.
Inventors
- 👤 Stephen J. Schultz
- 👤 Terry L. Wolfe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:54
CPC Classifications
C; C03; C03B; C03B27/00; C03B27/04; C03B27/0404; C03B23/00; C03B23/02; C03B23/023; C03B23/025; C03B23/0252; C03B23/0254; C03B23/03; C03B23/033; C03B27/044; C03B27/0442; C03B27/0445; C03B35/00; C03B35/14; C03B35/16; C03B35/161; C03B35/165; C03B35/18; C03B35/186; C03B35/187; C03B35/189
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
152 words
A method of shaping a glass sheet comprising heating the sheet to its deformation temperature in a furnace, conveying said sheet along a path of travel beyond said furance while said sheet remains hot over a series of rotating forming rolls shaped to transverse elevational shape to sag the sheet by gravity to conform approximately to the transverse elevational shape of the last forming roll in said series, and inhibiting the formation of tip curl in the vicinity of the transverse side edge portions of said gravity sagged sheet by pressing said sheet between a plurality of pairs of additional rotating forming rolls of complementary transverse elevational shape arranged with diminishing space between the rolls of each successive pair of said additional rotating forming rolls along said path of travel wherein the space between the last of said pairs of additional rotating forming rolls barely exceeds the thickness of said glass sheet.
Claim 2
Independent Claim
152 words
A method of shaping a glass sheet comprising heating the sheet to its deformation temperature in a furnace, conveying said sheet along a path of travel beyond said furance while said sheet remains hot over a series of rotating forming rolls shaped to transverse elevational shape to sag the sheet by gravity to conform approximately to the transverse elevational shape of the last forming roll in said series, and inhibiting the formation of tip curl in the vicinity of the transverse side edge portions of said gravity sagged sheet by pressing said sheet between a plurality of pairs of additional rotating forming rolls of complementary transverse elevational shape arranged with diminishing space between the rolls of each successive pair of said additional rotating forming rolls along said path of travel wherein the space between the last of said pairs of additional rotating forming rolls barely exceeds the thickness of said glass sheet.
Claim 3
Dependent Claim
57 words
The method as in claim 1, followed by cooling said glass sheet immediately after it leaves the space between said last pair of additional rotating forming rolls at a rapid rate sufficient to impart at least a partial temper to said glass sheet while conveying said glass sheet on curved support rolls disposed along a cooling section.
Claim 4
Dependent Claim
49 words
The method as in claim 2, wherein said glass sheet is cooled differentially by applying cold tempering medium against the opposite major surfaces of said glass sheet at sufficiently different rates to warp said glass sheet from the shape developed by said gravity sagging followed by said roll pressing.
Claim 5
Dependent Claim
28 words
The method as in claim 2 or claim 3, wherein said glass sheet is conveyed along the length of said furnace during its heating to its deformation temperature.
Claim 6
Dependent Claim
78 words
The method according to claim 4, comprising conveying said glass sheet on rotating conveyor rolls of cylindrical configuration through said furnace and providing said conveyor rolls with a peripheral speed approximating the peripheral speed of said rotating forming rolls, said additional rotating forming rolls and said curved support rolls in said cooling section to maintain said glass sheet along a path of movement while avoiding misalignment and skewing of said glass sheet relative to said path of movement.
Claim 7
Dependent Claim
58 words
The method according to claim 4, wherein said glass sheet is conveyed between said furnace and said additional conveyor rolls in said cooling section in facing relation to heat reflecting means to minimize temperature loss of said glass sheet during its conveyance over said rotating forming rolls and between said plurality of pairs of additional rotating forming rolls.
Claim 8
Dependent Claim
30 words
The method according to claim 1 or 2 or 3, wherein said glass sheet is oriented in an essentially horizontal orientation for movement along an essentially horizontal path of movement.
Claim 9
Dependent Claim
40 words
The method according to claim 7, wherein said essentially horizontal path of movement is along an essentially straight line defined by supporting said rotating forming rolls and the lower of said pairs of additional forming rolls along a straight line.
Claim 10
Dependent Claim
39 words
The method according to claim 7, wherein said essentially horizontal path of movement is along an arcuate path defined by supporting said rotating forming rolls and the lower of said pairs of additional forming rolls along an arcuate line.
Claim 11
Dependent Claim
37 words
The method according to claim 7, comprising imparting a transverse elevational shape of concave elevation by engaging said glass sheet with said rotating forming rolls and said pairs of additional rotating forming rolls of concave transverse elevation.
Claim 12
Dependent Claim
37 words
The method according to claim 7, comprising imparting a transverse elevational shape of convex elevation by engaging said glass sheet with said rotating forming rolls and said pairs of additional rotating formig rolls of convex transverse elvation.
Claim 13
Independent Claim
23 words
The method according to any one of claims 8 to 11, wherein said glass sheet is one of a series of glass sheets.
Claim 14
Independent Claim
64 words
A method of shaping a glass sheet while at deformation temperature comprising passing said sheet between pairs of rotating forming rolls of complementary transverse elevational shape arranged with diminishing space between the rolls of each successive pair along a path of travel including a downstream pair of rolls spaced from one another by a distance that barely exceeds the thickness of said glass sheet.
Claim 15
Independent Claim
64 words
A method of shaping a glass sheet while at deformation temperature comprising passing said sheet between pairs of rotating forming rolls of complementary transverse elevational shape arranged with diminishing space between the rolls of each successive pair along a path of travel including a downstream pair of rolls spaced from one another by a distance that barely exceeds the thickness of said glass sheet.
Claim 16
Dependent Claim
18 words
A method as in claim 13, wherein said glass sheet is one of a series of glass sheets.
Claim 17
Dependent Claim
79 words
Apparatus for shaping a glass sheet comprising a furnace and a roll forming section, said roll forming section comprising an upstream portion having a plurality of rotatable forming rolls shaped in transverse elevation and a downstream portion comprising a plurality of pairs of closely spaced, rotatable forming rolls of complementary shape arranged along a path of travel, the space between the rotatable forming rolls of said plurality of pairs diminishing in a downstream direction along said path of travel.
Claim 18
Dependent Claim
79 words
Apparatus for shaping a glass sheet comprising a furnace and a roll forming section, said roll forming section comprising an upstream portion having a plurality of rotatable forming rolls shaped in transverse elevation and a downstream portion comprising a plurality of pairs of closely spaced, rotatable forming rolls of complementary shape arranged along a path of travel, the space between the rotatable forming rolls of said plurality of pairs diminishing in a downstream direction along said path of travel.
Claim 19
Dependent Claim
33 words
Apparatus as in claim 15, comprising means to support the last of said plurality of pairs of forming rolls at a spacing from one another barely exceeding the thickness of said glass sheet.
Claim 20
Dependent Claim
26 words
Apparatus as in claim 15 or 16, wherein said uptream portion comprises a plurality of rotatable forming rolls of gradually increasing severity of transverse elevational shape.
Claim 21
Dependent Claim
31 words
Apparatus as in claim 15 or 16, wherein said upstream portion comprises a plurality of rotatable conveyor rolls of cylindrical shape alternating with said rotatable forming rolls shaped in transverse elevation.
Claim 22
Dependent Claim
34 words
Apparatus as in claim 15 or 16, wherein said rotatable forming rolls and said additional rotatable forming rolls are supported along a straight line of support in the direction of said path of travel.
Claim 23
Dependent Claim
34 words
Apparatus as in claim 15 or 16, wherein said rotatable forming rolls and said additional rotatable forming rolls are supported along an arcuate line of support in the direction of said path of travel.
Claim 24
Dependent Claim
25 words
Apparatus as in claim 15 or 16, wherein said rotatable forming rolls and said additional rotatable forming rolls are shaped to have transverse concave elevation.
Claim 25
Dependent Claim
25 words
Apparatus as in claim 15 or 16, wherein said rotatable forming rolls and said additional rotatable forming rolls are shaped to have transverse convex elevation.
Claim 26
Dependent Claim
55 words
Apparatus as in claim 15 or 16, further including a cooling section located downstream of said downstream portion of said roll forming section along said path of travel, further comprising heat-reflecting surface means in facing relation to said rotatable forming rolls and said additional rotatable forming rolls along the length of said roll forming section.
Claim 27
Dependent Claim
30 words
Apparatus as in claim 23, wherein at least a portion of said heat-reflecting surface means in the downstream portion of said roll forming section is oriented obliquely downward and upstream.
References Cited (Backward Citations)
US409047A
Cited
US1147713A
Cited
US1946240A
Cited
US2348887A
Cited
US3245771A
Cited
US3248198A
Cited
US3262768A
Cited
US3226219A
Cited
US3284182A
Cited
US3342573A
Cited
US3332761A
Cited
US3245772A
Cited
US3223499A
Cited
US3396000A
Cited
US3420650A
Cited
US3545951A
Cited
US3372016A
Cited
US3522029A
Cited
US3497340A
Cited
US3801298A
Cited
US3832153A
Cited
US3820969A
Cited
US3701644A
Cited
US3831239A
Cited
US3856499A
Cited
US3869269A
Cited
US3871855A
Cited
US3881906A
Cited
US3934996A
Cited
US3891420A
Cited
US3929441A
Cited
US4054438A
Cited
US3992181A
Cited
US4028086A
Cited
US4054437A
Cited
US4043783A
Cited
US4139359A
Cited
US4123246A
Cited
US4226608A
Cited
US4305746A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-05-02 | 1986-11-01 | 1987-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-05-02 | 1990-11-01 | 1991-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-05-02 | 1994-11-01 | 1995-05-03 | $7700.00 | Window Closed / Lapsed |