Pre-foamed particles of polypropylene resin and process for production thereof
Assignee: JAPA STYRENE PAPER Corp
•
Filing: 1981-11-19
•
Granted: 1983-04-12
•
Expires: 2001-11-19
Abstract
Abstract Substantially non-crosslinked pre-foamed particles of a polypropylene resin, characterized by the fact that they are composed of an ethylene/propylene random copolymer or a mixture of an ethylene/propylene random copolymer with low density polyethylene and/or an ethylene/vinyl acetate copolymer as a base resin; and a process for producing pre-foamed particles of a polypropylene resin, which comprises dispersing substantially non-crosslinked particles of the polypropylene resin composed of an ethylene/propylene random copolymer or a mixture of an ethylene/propylene random copolymer with low-density polyethylene and/or an ethylene/vinyl acetate copolymer and a volatile blowing agent in water in the presence of a dispersing agent within a closed vessel; heating the dispersion to a temperature above a temperature at which the resin particles soften, thereby to impregnated the blowing agent in the resin particles; and while maintaining the pressure of the inside of the vessel higher than the vapor pressure of the blowing agent, opening one end of the vessel to release the resin particles and water simultaneously into an atmosphere kept at a lower pressure than the inside of the vessel.
Inventors
- 👤 Kuninori Hirosawa
- 👤 Sumio Shimada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:20
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0061; C08J9/16; C08J9/18; C08J2323/00; C08J2323/02; C08J2323/16; C08J2423/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
56 words
Substantially non-crosslinked pre-foamed particles of a propylene copolymer resin selected from the group consisting of an ethylene/propylene random copolymer or a mixture of an ethylene/propylene random copolymer with low density polyethylene and/or an ethylene/vinyl acetate copolymer as a base resin, provided that the ethylene/propylene random copolymer has an ethylene contents of 1 to 20% by weight.
Claim 2
Dependent Claim
56 words
Substantially non-crosslinked pre-foamed particles of a propylene copolymer resin selected from the group consisting of an ethylene/propylene random copolymer or a mixture of an ethylene/propylene random copolymer with low density polyethylene and/or an ethylene/vinyl acetate copolymer as a base resin, provided that the ethylene/propylene random copolymer has an ethylene contents of 1 to 20% by weight.
Claim 3
Dependent Claim
28 words
The pre-foamed particles of claim 1 wherein the content of the low-density polyethylene and/or the ethylene/vinyl acetate copolymer in the mixture is not more than 45% by weight.
Claim 4
Dependent Claim
154 words
A process for producing pre-foamed particles of a propylene copolymer resin, which comprises dispersing substantially non-crosslinked particles of a propylene copolymer resin selected from the group consisting of an ethylene/propylene random copolymer or a mixture of an ethylene/propylene random copolymer with low-density polyethylene and/or an ethylene/vinyl acetate copolymer provided that the ethylene/propylene random copolymer has an ethylene content 1 to 20% by weight and a volatile blowing agent in water in the presence of a dispersing agent within a closed vessel; heating the dispersion to a temperature above a temperature at which the resin particles soften, thereby to impregnate the blowing agent in the resin particles; and while maintaining the pressure of the inside of the vessel higher than the vapor pressure of the blowing agent, opening one end of the vessel to release the resin particles and water simultaneously into an atmosphere kept at a lower pressure than the inside of the vessel.
Claim 5
Dependent Claim
154 words
A process for producing pre-foamed particles of a propylene copolymer resin, which comprises dispersing substantially non-crosslinked particles of a propylene copolymer resin selected from the group consisting of an ethylene/propylene random copolymer or a mixture of an ethylene/propylene random copolymer with low-density polyethylene and/or an ethylene/vinyl acetate copolymer provided that the ethylene/propylene random copolymer has an ethylene content 1 to 20% by weight and a volatile blowing agent in water in the presence of a dispersing agent within a closed vessel; heating the dispersion to a temperature above a temperature at which the resin particles soften, thereby to impregnate the blowing agent in the resin particles; and while maintaining the pressure of the inside of the vessel higher than the vapor pressure of the blowing agent, opening one end of the vessel to release the resin particles and water simultaneously into an atmosphere kept at a lower pressure than the inside of the vessel.
Claim 6
Dependent Claim
28 words
The process of claim 3 wherein the volatile blowing agent is at least one member selected from the group consisting of aliphatic hydrocarbons, alicyclic hydrocarbons and halogenated hydrocarbons.
Claim 7
Dependent Claim
30 words
The process of claim 3 wherein the blowing agent is used in an amount of 10 to 40 parts by weight per 100 parts by weight of the polypropylene resin.
Claim 8
Dependent Claim
29 words
The process of claim 3 wherein the dispersing agent is at least one member selected from the group consisting of basic magnesium carbonate, basic zinc carbonate and calcium carbonate.
Claim 9
Dependent Claim
30 words
The process of claim 3 wherein the dispersing agent is used in an amount of 0.1 to 10 parts by weight per 100 parts by weight of the polypropylene resin.
Claim 10
Dependent Claim
13 words
The process of claim 7 wherein the dispersing agent is basic magnesium carbonate.
Claim 11
Dependent Claim
28 words
The process of claim 3 wherein the content of the low density polyethylene and/or the ethylene/vinyl acetate copolymer in the mixture is not more than 45% by weight.
References Cited (Backward Citations)
US3616365A
Cited
US3743611A
Cited
US3709806A
Cited
US4168353A
Cited
US4303757A
Cited
US4303756A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-11 | 1986-10-11 | 1987-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-11 | 1990-10-11 | 1991-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-11 | 1994-10-11 | 1995-04-12 | $7700.00 | Window Closed / Lapsed |