Process for producing expandable thermoplastic resin beads using polypropylene as nucleus

Claim 2

A process for producing expandable thermoplastic resin beads which comprises suspending in an aqueous medium from 20 to 70% by weight of polypropylene resin particles and from 30 to 80% by weight of a vinyl aromatic monomer, polymerizing the vinyl aromatic monomer in the presence of a polymerization catalyst to graft the vinyl aromatic monomer onto the backbone of the polypropylene to form graft-copolymerized thermoplastic resin beads, and thereafter introducing a blowing agent composed of an easily volatilizable hydrocarbon or halogenated hydrocarbon into the thermoplastic resin beads.

Claim 3

The process of claim 1, wherein the amount of the polypropylene resin particles employed is from 50 to 30% by weight, and the amount of the vinyl aromatic monomer is from 50 to 70% by weight.

Claim 4

The process of claim 1, wherein the polypropylene resin particles are particles of a homopolymer of propylene, a block copolymer of polypropylene and another polyolefin containing at least 50% by weight of the polypropylene, or a mixture of at least 50% by weight of polypropylene and another polyolefin.

Claim 5

The process of claim 1, wherein the vinyl aromatic monomer is at least one monomer selected from the group consisting of styrene, α-methylstyrene, ethylstyrene, chlorostyrene, bromostyrene, vinyltoluene, vinylxylene and isopropylxylene, or a mixture of at least 50% by weight of at least one of said monomers with another monomer copolymerizable therewith.

Claim 6

The process of claim 1, wherein the polymerization is carried out in the further presence of a cross-linking agent.

Claim 7

The process of claim 1, wherein the blowing agent is introduced into the resin beads under pressure while in the aqueous suspension.

Claim 8

The process of claim 1, wherein the blowing agent is introduced into the resin beads by dipping the beads into a liquid organic blowing agent.

Claim 9

In a process for producing expandable thermoplastic resin beads which comprises suspending in an aqueous medium containing 0.01 to 5% by weight, based on water present in the aqueous medium, of a dispersing agent selected from the group consisting of polyvinyl alcohol, methyl cellulose, calcium phosphate, magnesium pyrophosphate and calcium carbonate, from 20 to 70% by weight of polypropylene resin particles and from 30 to 80% by weight of a vinyl aromatic monomer, polymerizing the vinyl aromatic monomer in the presence of a polymerization catalyst to graft the vinyl aromatic monomer onto the backbone of the polypropylene to form graft-copolymerized thermoplastic resin beads, and thereafter introducing a blowing agent composed of an easily volatilizable hydrocarbon or halogenated hydrocarbon into the thermoplastic resin beads, the improvement comprising heating the aqueous medium to a temperature at which the vinyl aromatic monomer can be polymerized before adding the vinyl aromatic monomer and the polymerization catalyst thereto, and adding said vinyl aromatic monomer and said polymerization catalyst to the heated aqueous medium.

Claim 10

In a process for producing expandable thermoplastic resin beads which comprises suspending in an aqueous medium containing 0.01 to 5% by weight, based on water present in the aqueous medium, of a dispersing agent selected from the group consisting of polyvinyl alcohol, methyl cellulose, calcium phosphate, magnesium pyrophosphate and calcium carbonate, from 20 to 70% by weight of polypropylene resin particles and from 30 to 80% by weight of a vinyl aromatic monomer, polymerizing the vinyl aromatic monomer in the presence of a polymerization catalyst to graft the vinyl aromatic monomer onto the backbone of the polypropylene to form graft-copolymerized thermoplastic resin beads, and thereafter introducing a blowing agent composed of an easily volatilizable hydrocarbon or halogenated hydrocarbon into the thermoplastic resin beads, the improvement comprising heating the aqueous medium to a temperature at which the vinyl aromatic monomer can be polymerized before adding the vinyl aromatic monomer and the polymerization catalyst thereto, and adding said vinyl aromatic monomer and said polymerization catalyst to the heated aqueous medium.

Claim 11

The process of claim 8, wherein the polymerization is carried out in the further presence of a cross-linking agent.