Method for making low barrier Schottky devices of the electron beam evaporation of reactive metals
Assignee: International Business Machines Corp
•
Filing: 1981-08-31
•
Granted: 1983-04-12
•
Expires: 2001-08-31
Abstract
Abstract A method for making low barrier Schottky devices by the electron beam evaporation of a reactive metal such as tantalum, titanium, hafnium, tungsten, molybdenum, and niobium which is selectively deposited at a semiconductor surface such as n-type silicon using a photoresist mask. The method includes a series of steps during the deposition of the barrier metal for degassing the semiconductor substrate, photoresist mask, reactive metal charge and deposition chamber. More particularly, the method includes steps for preliminarily degassing the substrate, mask and surrounding chamber by infra red heating under vacuum followed by steps for preliminarily degassing the charge and surrounding chamber, while the substrate and mask are shielded by electron beam heating the charge while under vacuum. Thereafter, and prior to deposition, the substrate and mask are finally degassed by irradiation with X-rays produced by electron beam heating the charge to a temperature below evaporation for a predetermined time under vacuum. Upon further heating of the charge, the barrier metal is evaporated and deposited at the semiconductor substrate surface.
Inventors
- 👤 Hormazdyar M. Dalal
- 👤 John J. Lowney
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:20
CPC Classifications
H; H10; H10P; H10P76/00; H10P76/20; H10P76/204; H10P76/2047; C; C23; C23C; C23C14/00; C23C14/04; H10D; H10D64/00; H10D64/01; H10D64/012; H10D64/0121; H10P76/202; Y; Y10; Y10S; Y10S438/00; Y10S438/974
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
150 words
An improved lift-off mask method for applying a reactive metal layer to a major surface of a semiconductor substrate, the method including forming a compound layer of photoresist materials at the semiconductor surface; selectively exposing the photoresist layer to radiation which the photoresist is reactive to; removing portions of the photoresist layer to expose select regions of the substrate surface; depositing at least a first layer of reactive metal at the selectively exposed substrate surface and the photoresist by electron beam evaporation of the reactive metal; and removing the photoresist and reactive metal layer on the photoresist layer; the improvement comprising irradiating the photoresist layer with x-rays generated by heating a charge of reactive metal from which the metal to be deposited is supplied to a temperature below the evaporation temperature of the metal while under vacuum with an electron beam for a predetermined time before depositing the reactive metal.
Claim 2
Dependent Claim
150 words
An improved lift-off mask method for applying a reactive metal layer to a major surface of a semiconductor substrate, the method including forming a compound layer of photoresist materials at the semiconductor surface; selectively exposing the photoresist layer to radiation which the photoresist is reactive to; removing portions of the photoresist layer to expose select regions of the substrate surface; depositing at least a first layer of reactive metal at the selectively exposed substrate surface and the photoresist by electron beam evaporation of the reactive metal; and removing the photoresist and reactive metal layer on the photoresist layer; the improvement comprising irradiating the photoresist layer with x-rays generated by heating a charge of reactive metal from which the metal to be deposited is supplied to a temperature below the evaporation temperature of the metal while under vacuum with an electron beam for a predetermined time before depositing the reactive metal.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein additionally the semiconductor substrate, photoresist layer and surrounding vacuum chamber are degassed by infrared heating under vacuum before X-ray irradiation.
Claim 4
Dependent Claim
32 words
The method of claim 2 wherein additionally the reactive metal charge and surrounding vacuum chamber are degassed by electron beam heating the charge while under vacuum, before X-ray irradiation of the photoresist.
Claim 5
Dependent Claim
88 words
The method of claim 3 wherein the reactive metal charge and surrounding chamber are degassed with the substrate and photoresist layer shielded by heating the source while under vacuum with an electron beam to a first temperature substantially below the metal evaporation temperature for a predetermined time, thereafter further heating the source to a second temperature approximately equal to the metal evaporation temperature for a predetermined time and thereafter yet further heating the source to a third temperature substantially above the metal evaporation temperature for a predetermined time.
Claim 6
Dependent Claim
15 words
The method of claim 4 wherein the degas steps are repeated one or more times.
Claim 7
Dependent Claim
67 words
The method of claim 4 or 5 wherein the reactive metal for deposition at the semiconductor substrate is generated following X-ray irradiation by heating the charge while under vacuum with an electron beam to a temperature approximately equal to the source evaporation temperature for a predetermined time and to thereafter further heat the charge to a temperature substantially above the charge evaporation temperature for a predetermined time.
Claim 8
Independent Claim
163 words
A method for depositing a reactive metal film at a surface of a semiconductor substrate, the surface being selectively exposed by a photoresist mask thereon, the method comprising: a. placing the semiconductor substrate and photoresist mask thereon in a vacuum chamber together with a charge of reactive metal and drawing a vacuum; b. degassing the semiconductor substrate photoresist mask thereon and surrounding vacuum chamber by infrared heating; c. degassing the reactive metal charge and surrounding vacuum chamber by electron beam heating and charge under vacuum while the semiconductor substrate and photoresist layer thereon are shielded; d. further degassing the semiconductor substrate and photoresist mask thereon by irradiating them under vacuum with X-rays generated by electron beam heating the reactive metal charge to a temperature below the charge evaporation temperature for a predetermined time; e. and depositing a reactive metal film at the exposed semiconductor surface by heating the charge under vacuum with an electron beam to a temperature sufficient to evaporate the charge.
Claim 9
Independent Claim
163 words
A method for depositing a reactive metal film at a surface of a semiconductor substrate, the surface being selectively exposed by a photoresist mask thereon, the method comprising: a. placing the semiconductor substrate and photoresist mask thereon in a vacuum chamber together with a charge of reactive metal and drawing a vacuum; b. degassing the semiconductor substrate photoresist mask thereon and surrounding vacuum chamber by infrared heating; c. degassing the reactive metal charge and surrounding vacuum chamber by electron beam heating and charge under vacuum while the semiconductor substrate and photoresist layer thereon are shielded; d. further degassing the semiconductor substrate and photoresist mask thereon by irradiating them under vacuum with X-rays generated by electron beam heating the reactive metal charge to a temperature below the charge evaporation temperature for a predetermined time; e. and depositing a reactive metal film at the exposed semiconductor surface by heating the charge under vacuum with an electron beam to a temperature sufficient to evaporate the charge.
Claim 10
Dependent Claim
76 words
The method of claim 7 wherein the charge and surrounding vacuum chamber are degassed by heating the charge under vacuum with an electron beam to a first temperature substantially below the charge evaporation temperature for a predetermined time, thereafter heating the charge to a second temperature approximately equal to the charge evaporation temperature for a predetermined time and thereafter heating the charge to a third temperature substantially above the charge evaporation temperature for a predetermined time.
Claim 11
Dependent Claim
15 words
The method of claim 8 wherein the degas steps are repeated one or more times.
Claim 12
Dependent Claim
58 words
The method of claim 8 or 9 wherein the reactive metal is deposited by heating the charge while under vacuum with an electron beam to a temperature approximately equal to the charge evaporation temperature for a predetermined time and to thereafter further heat the charge to a temperature substantially above the charge evaporation temperature for a predetermined time.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-04-11 | 1986-10-11 | 1987-04-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-04-11 | 1990-10-11 | 1991-04-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-04-11 | 1994-10-11 | 1995-04-12 | $7700.00 | Window Closed / Lapsed |