Ductile alloy and process for preparing composite superconducting wire
Assignee: United States Department of Energy
•
Filing: 1979-03-12
•
Granted: 1983-03-29
•
Expires: 1999-03-12
Abstract
Abstract An alloy for the commercial production of ductile superconducting wire is prepared by melting together copper and at least 15 weight percent niobium under non-oxygen-contaminating conditions, and rapidly cooling the melt to form a ductile composite consisting of discrete, randomly distributed and orientated dendritic-shaped particles of niobium in a copper matrix. As the wire is worked, the dendritric particles are realigned parallel to the longitudinal axis and when drawn form a plurality of very fine ductile superconductors in a ductile copper matrix. The drawn wire may be tin coated and wound into magnets or the like before diffusing the tin into the wire to react with the niobium. Impurities such as aluminum or gallium may be added to improve upper critical field characteristics.
Inventors
- 👤 John D. Verhoeven
- 👤 Douglas K. Finnemore
- 👤 Edwin D. Gibson
- 👤 Jerome E. Ostenson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:17
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/80; H10N60/85; C; C22; C22C; C22C9/00; C22F; C22F1/00; C22F1/08; H10N60/01; Y; Y10; Y10S; Y10S505/00; Y10S505/825; Y10S505/917; Y10S505/918; Y10S505/919; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
54 words
A ductile alloy for preparing composite superconducting wire comprising copper and from 20 to 60 weight percent niobium, the niobium being present in the copper as discrete, randomly distributed and oriented, elongated dendritic-shaped particles having a diameter from about 1 μm to about 25 μm and an aspect ratio of between 50 to 100.
Claim 2
Dependent Claim
54 words
A ductile alloy for preparing composite superconducting wire comprising copper and from 20 to 60 weight percent niobium, the niobium being present in the copper as discrete, randomly distributed and oriented, elongated dendritic-shaped particles having a diameter from about 1 μm to about 25 μm and an aspect ratio of between 50 to 100.
Claim 3
Dependent Claim
31 words
The ductile alloy of claim 1 wherein the alloy also contains from 1 to about 10 weight percent of an impurity selected from the group consisting of gallium, aluminum and indium.
Claim 4
Independent Claim
82 words
A method of forming a ductile alloy of copper and niobium where the niobium is present in the copper as discrete, randomly distributed and oriented, elongated dendritic-shaped particles comprising the steps of: a. melting together under a non-oxygen containing atmosphere in non-oxygen releasing crucibles, a mixture of copper and at least 15 weight percent niobium to form a melt, and b. rapidly cooling the melt so that the melt freezes upwardly from one end to promote dendritic growth within the copper matrix.
Claim 5
Independent Claim
82 words
A method of forming a ductile alloy of copper and niobium where the niobium is present in the copper as discrete, randomly distributed and oriented, elongated dendritic-shaped particles comprising the steps of: a. melting together under a non-oxygen containing atmosphere in non-oxygen releasing crucibles, a mixture of copper and at least 15 weight percent niobium to form a melt, and b. rapidly cooling the melt so that the melt freezes upwardly from one end to promote dendritic growth within the copper matrix.
Claim 6
Dependent Claim
34 words
The method of claim 3 wherein the mixture is heated under an inert atmosphere in a crucible made of material selected from the group consisting of yttria, thoria, graphite, and zirconia stabilized with yttria.
Claim 7
Dependent Claim
19 words
The method of claim 4 wherein the melt is rapidly cooled by casting it into a copper chill mold.
Claim 8
Dependent Claim
16 words
The method of claim 5 wherein the mixture contains from 20 to 60 weight percent niobium.
Claim 9
Dependent Claim
24 words
The method of claim 6 wherein the copper chill mold contains a thin liner of graphite to slow the cooling rate of the melt.
References Cited (Backward Citations)
US3290186A
Cited
US3818578A
Cited
US3905839A
Cited
US3817746A
Cited
GB1445723A
Cited
US3907550A
Cited
US4000014A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-28 | 1986-09-27 | 1987-03-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-28 | 1990-09-27 | 1991-03-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-28 | 1994-09-27 | 1995-03-29 | $7700.00 | Window Closed / Lapsed |