Dimensionally-stable polyurethane sponge and sponge-forming prepolymer
Assignee: Hampshire Chemical Corp
•
Filing: 1981-10-26
•
Granted: 1983-03-22
•
Expires: 2001-10-26
Abstract
Abstract An MDI based polyurethane foam having cellulose foam properties is produced by mixing together an aqueous phase which can optionally contain reinforcing fibers and surfactants and a resin phase comprising a prepolymer derived from a poly(oxy C2-4 alkylene)diol, an MDI containing isocyanate product having a functionality greater than 2.0 made of a mixture of MDI and isocyanate containing derivatives of MDI, and a monomeric polyol cross-linking agent having 3 or 4 hydroxyl equivalents per mole. The preferred polyol is trimethylolpropane and the preferred diol is Carbowax 1000. The diol and the polyol, such as trimethylolpropane, are present in a mole ratio in the range of 4:1 to 8:1 while the ratio of the isocyanate equivalents to the total hydroxyl equivalents is in the range of 3:1 to 4:1. The isocyanate containing product comprises more than 50% by weight of the prepolymer and Isonate 143L is the preferred isocyanate product. The foam has a minimal swell when wet and it does not curl upon drying.
Inventors
- 👤 James L. Guthrie
- 👤 Suze E. Arquette
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:50
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/77; C08G18/78; C08G18/79; C08G18/797; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; C08G18/6677; C08G18/6681; C08G18/6688; C08G18/721; C08G18/725; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/005; C08G2110/0058; C08G2110/0083; Y; Y10; Y10S; Y10S521/00; Y10S521/901; Y10S521/905; Y10S521/914
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
172 words
A foamed sponge having minimal swell when wet and which does not curl upon drying made by mixing together and reacting an aqueous phase and a resin phase comprising a prepolymer derived from (a) a poly(oxy C 2-4 alkylene) diol having at least about 50% by weight of oxyethylene groups and a nominal number average molecular weight of about at most 1100, said diol having nominally two hydroxyl equivalents per mole, (b) a diphenylmethane diisocyanate-containing isocyanate product with a functionality of greater than 2.0 comprising a mixture of a major amount of pure diphenylmethane diisocyanate and minor amounts of carbodiimides and trifunctional cycloadducts of diphenylmethane diisocyanate, and (c) a monomeric polyol cross-linking agent having 3 or 4 hydroxyl equivalents per mole, said isocyanate product comprising more than 50% by weight of the prepolymer, said diol and polyol cross-linking agent being present in a mole ratio in the range of 4:1 to 8:1, and the ratio of the isocyanate equivalents to the total hydroxyl equivalents being in the range of 3:1 to 4:1.
Claim 2
Dependent Claim
172 words
A foamed sponge having minimal swell when wet and which does not curl upon drying made by mixing together and reacting an aqueous phase and a resin phase comprising a prepolymer derived from (a) a poly(oxy C 2-4 alkylene) diol having at least about 50% by weight of oxyethylene groups and a nominal number average molecular weight of about at most 1100, said diol having nominally two hydroxyl equivalents per mole, (b) a diphenylmethane diisocyanate-containing isocyanate product with a functionality of greater than 2.0 comprising a mixture of a major amount of pure diphenylmethane diisocyanate and minor amounts of carbodiimides and trifunctional cycloadducts of diphenylmethane diisocyanate, and (c) a monomeric polyol cross-linking agent having 3 or 4 hydroxyl equivalents per mole, said isocyanate product comprising more than 50% by weight of the prepolymer, said diol and polyol cross-linking agent being present in a mole ratio in the range of 4:1 to 8:1, and the ratio of the isocyanate equivalents to the total hydroxyl equivalents being in the range of 3:1 to 4:1.
Claim 3
Dependent Claim
38 words
A foamed sponge according to claim 1, wherein the nominal number average molecular weight of the poly(oxy C 2-4 alkylene) diol is between 600 and 1100 and the diol has at least 80% by weight of oxyethylene groups.
Claim 4
Dependent Claim
27 words
A foamed sponge according to claim 1, wherein the polyol cross-linking agent is selected from the group consisting of trimethylolpropane, trimethylolethane, glycerol, triethanolamine, pentaerythritol, and mixtures thereof.
Claim 5
Dependent Claim
14 words
A foamed sponge according to claim 3, wherein the polyol cross-linking agent is trimethylolpropane.
Claim 6
Dependent Claim
15 words
A foamed sponge according to claim 1, wherein the aqueous phase further comprises a surfactant.
Claim 7
Dependent Claim
40 words
A foamed sponge according to claim 5, wherein the surfactant is a diol made by capping poly(oxypropylene) of molecular weight of about 1750 with ethylene oxide such that the resultant liquid product contains about 20% by weight of ethylene oxide.
Claim 8
Dependent Claim
11 words
A foamed sponge according to claim 1, further comprising reinforcing fibers.
Claim 9
Dependent Claim
23 words
A foamed sponge according to claim 7, wherein the reinforcing fibers are polyester fibers of a length of about 1/2 inch or less.
Claim 10
Dependent Claim
14 words
A foamed sponge according to claim 8, further comprising a thickening or suspending agent.
Claim 11
Dependent Claim
20 words
A foamed sponge according to claim 9, wherein the thickening or suspending agent is a high molecular weight polycarboxylic acid.
Claim 12
Dependent Claim
23 words
A foamed sponge according to claim 10, wherein the polycarboxylic acid is a polyacrylic acid polymer having an approximate molecular weight of 1,250,000.
Claim 13
Dependent Claim
13 words
A foamed sponge according to claim 10, wherein the polycarboxylic acid is neutralized.
Claim 14
Dependent Claim
16 words
A foamed sponge according to claim 12, wherein the polycarboxylic acid is neutralized with ammonium hydroxide.
Claim 15
Dependent Claim
153 words
A prepolymer, for use in making a foamed sponge, comprising the reaction product of (a) a poly(oxy C 2-4 alkylene) diol having at least about 50% by weight of oxyethylene groups and a nominal number average molecular weight of about at most 1100, said diol having nominally two hydroxyl equivalents per mole, (b) a diphenylmethane diisocyanate-containing isocyanate product with a functionality of greater than 2.0 comprising a mixture of a major amount of pure diphenylmethane diisocyanate and minor amounts of carbodiimides and trifunctional cycloadducts of diphenylmethane diisocyanate, and (c) a monomeric polyol cross-linking agent having 3 or 4 hydroxyl equivalents per mole, said isocyanate product comprising more than 50% by weight of the prepolymer, said diol and polyol cross-linking agent being present in a mole ratio in the range of 4:1 to 8:1, and the ratio of the isocyanate equivalents to the total hydroxyl equivalents being in the range of 3:1 to 4:1.
Claim 16
Dependent Claim
153 words
A prepolymer, for use in making a foamed sponge, comprising the reaction product of (a) a poly(oxy C 2-4 alkylene) diol having at least about 50% by weight of oxyethylene groups and a nominal number average molecular weight of about at most 1100, said diol having nominally two hydroxyl equivalents per mole, (b) a diphenylmethane diisocyanate-containing isocyanate product with a functionality of greater than 2.0 comprising a mixture of a major amount of pure diphenylmethane diisocyanate and minor amounts of carbodiimides and trifunctional cycloadducts of diphenylmethane diisocyanate, and (c) a monomeric polyol cross-linking agent having 3 or 4 hydroxyl equivalents per mole, said isocyanate product comprising more than 50% by weight of the prepolymer, said diol and polyol cross-linking agent being present in a mole ratio in the range of 4:1 to 8:1, and the ratio of the isocyanate equivalents to the total hydroxyl equivalents being in the range of 3:1 to 4:1.
Claim 17
Dependent Claim
34 words
A prepolymer according to claim 14, wherein the molecular weight of the poly(oxy C 2-4 alkylene) diol is between 600 and 1100 and the diol has at least 80% by weight of oxyethylene groups.
Claim 18
Dependent Claim
26 words
A prepolymer according to claim 15, wherein the polyol cross-linking agent is selected from the group consisting of trimethylolpropane, trimethylolethane, glycerol, triethanolamine, pentaerythritol, and mixtures thereof.
References Cited (Backward Citations)
GB874430A
Cited
GB1209058A
Cited
US3806474A
Cited
US4160076A
Cited
US4102831A
Cited
US4201846A
Cited
US4292412A
Cited
US4309509A
Cited
US4314034A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |