Novel process for the preparation of high purity alumina from ammonium alum
Assignee: CRICERAM A CORP OF FRANCE
•
Filing: 1981-06-29
•
Granted: 1983-03-22
•
Expires: 2001-06-29
Abstract
Abstract Process for preparing high purity aluminas from ammonium alum, the process comprising separately dehydrating the alum and thereafter thermally decomposing the dehydrate, wherein the thermal decomposition is carried out by forcing a gas through a layer of the dehydrated alum so as to continuously remove the gaseous reaction products formed without removal of solids by the carrier gas, and providing improved productivity of high purity transition aluminas having specific surfaces above 125 m2/g and/or bulk densities above 0.2 g/cm3, the transition aluminas so obtained being characterized by their greater reactivity for the preparation of corundum so that corundum having a bulk density greater than 0.4 g/cm3 can be economically prepared.
Inventors
- 👤 Roland Bachelard
- 👤 Robert Barral
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:50
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/02; C01F7/30; C01F7/32; C01P; C01P2006/00; C01P2006/11; C01P2006/12; C01P2006/13
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
101 words
A process for the preparation of alumina from ammonium alum comprising first dehydrating ammonium alum at a temperature above the fusion point of the alum and below the temperature which calcines the alum to alumina and then thermally decomposing the dehydrated alum with hot gas to produce alumina, the thermal decomposition being carried out with a flow of the hot gas forced through a layer of the dehydrated alum to heat and decompose the dehydrated alum and to continuously remove the decomposition products as they are formed, the movement of the dehydrated solid alum along with the gas flow being prevented.
Claim 2
Dependent Claim
101 words
A process for the preparation of alumina from ammonium alum comprising first dehydrating ammonium alum at a temperature above the fusion point of the alum and below the temperature which calcines the alum to alumina and then thermally decomposing the dehydrated alum with hot gas to produce alumina, the thermal decomposition being carried out with a flow of the hot gas forced through a layer of the dehydrated alum to heat and decompose the dehydrated alum and to continuously remove the decomposition products as they are formed, the movement of the dehydrated solid alum along with the gas flow being prevented.
Claim 3
Dependent Claim
34 words
A process according to claim 1 wherein the dehydration is carried out under vacuum with the alum in contact with a surface heated to a temperature above the melting point of the ammonium alum.
Claim 4
Dependent Claim
30 words
A process according to claim 1 wherein the dehydration is carried out by fluidizing the alum with the gas heated to a temperature above the melting point of the alum.
Claim 5
Dependent Claim
47 words
A process according to claim 1 wherein the thermal decomposition is carried out in a fixed bed having the alum distributed in a substantially uniform layer and wherein the hot gas moves downwardly through the bed at a speed greater than the fluidization velocity of the charge.
Claim 6
Dependent Claim
43 words
A process according to claim 1 wherein the thermal decomposition is carried out by conducting the dehydrated alum downwardly through a conduit having gas permeable walls and sweeping the hot gas through the walls transversely to the downward movement of the dehydrated alum.
Claim 7
Dependent Claim
63 words
A process according to claim 5 wherein the dehydration of the alum is continuously effected by conducting the ammonium alum starting material downwardly through the conduit having porous walls and sweeping hot gas transversely to the downward movement of the alum, the gas being at a temperature to dehydrate the alum but lower than the temperature required to calcine the alum to alumina.
Claim 8
Dependent Claim
29 words
A process according to claim 1 wherein the dehydration is effected by heating the ammonium alum with microwave radiation to a temperature above the fusion point of the alum.
Claim 9
Dependent Claim
35 words
A process according to claim 1 wherein the thermal decomposition produces transition alumina and the transition alumina is thereafter heated to a temperature above the thermal decomposition temperature of the transition alumina to produce α-alumina.
Claim 10
Dependent Claim
21 words
A process according to claim 1 wherein the thermal decomposition is carried out at a temperature of at least 600° C.
Claim 11
Dependent Claim
22 words
A process according to claim 1 wherein the thermal decomposition is carried out at a temperature of from 600° to 1250° C.
Claim 12
Dependent Claim
15 words
A process according to claim 10 wherein the temperature is at least about 1100° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |