Process for manufacturing aluminum oxide
Assignee: Individual
•
Filing: 1976-06-28
•
Granted: 1978-04-18
•
Expires: 1996-06-28
Abstract
Abstract There is disclosed a two step process for manufacturing aluminum oxide of controlled particle size from aluminum sulfate by the thermal decomposition of aluminum sulfate into aluminum oxide and other gaseous by-products at a relatively low temperature, and the treatment of the aluminum oxide product of the first step at a controlled higher temperature for the purpose of increasing the average particle size by a desired amount.
Inventors
- 👤 Kenneth F. Griffiths
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:41
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/02; C01F7/30; C01F7/32; C01P; C01P2004/00; C01P2004/51; C01P2004/52
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
128 words
A method of producing aluminum oxide powder of substantially uniform particle size from aluminum sulfate comprising 1. first thermally treating said aluminum sulfate at a temperature in the range from about 800° to about 1150° C. 2. maintaining said temperature for a time sufficient to decompose all of said aluminum sulfate and to form a mass of aluminum oxide having a uniform temperature throughout, and 3. thereafter subjecting said uniformly heated mass of aluminum oxide to additional heat to raise its temperature uniformly at approximately the same rate as the heat source to a curing temperature in the range from about 1175° to about 1250° C. for an additional period of time sufficient to cure said aluminum oxide and to increase the average particle size of aluminum oxide.
Claim 2
Independent Claim
128 words
A method of producing aluminum oxide powder of substantially uniform particle size from aluminum sulfate comprising 1. first thermally treating said aluminum sulfate at a temperature in the range from about 800° to about 1150° C. 2. maintaining said temperature for a time sufficient to decompose all of said aluminum sulfate and to form a mass of aluminum oxide having a uniform temperature throughout, and 3. thereafter subjecting said uniformly heated mass of aluminum oxide to additional heat to raise its temperature uniformly at approximately the same rate as the heat source to a curing temperature in the range from about 1175° to about 1250° C. for an additional period of time sufficient to cure said aluminum oxide and to increase the average particle size of aluminum oxide.
Claim 3
Dependent Claim
20 words
A method as defined in claim 1 wherein said aluminum sulfate comprises aluminum sulfate in admixture with ammonium aluminum sulfate.
Claim 4
Dependent Claim
22 words
A method as defined in claim 1 wherein subsequent to step (3) said aluminum oxide is cooled to below about 1150° C.
Claim 5
Dependent Claim
14 words
A method as defined in claim 1 carried out in a batch-type muffle furnace.
Claim 6
Dependent Claim
13 words
A method as defined in claim 1 carried out in a continuous calciner.
Claim 7
Dependent Claim
25 words
A method as defined in claim 5 further comprising carrying out said steps (1), (2) and (3) in one vessel having two differing temperature zones.
Claim 8
Dependent Claim
13 words
A method as defined in claim 1 carried out in a rotary-type calciner.
Claim 9
Dependent Claim
28 words
A method as defined in claim 1 wherein aluminum sulfate is introduced at one end of a furnace and cured aluminum oxide is withdrawn at another end thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-17 | 1981-10-17 | 1982-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-17 | 1985-10-17 | 1986-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-17 | 1989-10-17 | 1990-04-18 | $7700.00 | Window Closed / Lapsed |