Integrated carbon/insulator structure and method for fabricating same
Assignee: Yardney Technical Products Inc
•
Filing: 1981-04-06
•
Granted: 1983-03-22
•
Expires: 2001-04-06
Abstract
Abstract A thin, integrated carbon/insulator structure, and a method for fabricating same, for use in a primary electrochemical cell. A quantity of a wet carbon slurry material including a mixture of carbon black, water and/or isopropyl alcohol, and a binder such as finely-divided "Teflon" in suspension, is deposited onto a porous fiberglass substrate and rolled to a prescribed thickness. The rolling operation causes a portion of the slurry material to diffuse into the surface of the porous fiberglass substrate and permanently adhere to and unite with a surface portion of the fiberglass substrate in an integrated, interlocking fashion. The fiberglass substrate having the layer of carbon slurry material integrated therewith is then dried to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque having a network of cracks produced therethrough in a random pattern as a result of the shrinkage during drying. The layer of carbon plaque at this stage represents an aggregation of porous carbon globules. The layer of carbon plaque is re-rolled to close cracks at the upper surface of the layer while simultaneously establishing a desired thickness for the layer. After curing the above arrangement to increase adherence of the carbon globules to each other and to the fiberglass substrate, an integrated carbon/insulator structure of a desired size and configuration for use in a primary electrochemical cell can be cut out from the abovedescribed arrangement.
Inventors
- 👤 John E. Barnes
- 👤 Franz Goebel
- 👤 William T. McHugh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:37
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/64; H01M4/86; H01M4/96; H01M6/00; H01M6/14; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108; Y10T29/49115
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
211 words
A method for fabricating an integrated carbon/insulator structure for an electrochemical cell, comprising the steps of: depositing a quantity of a wet carbon slurry material onto a porous sheet of an electrically-nonconductive substrate material; physically working the quantity of wet carbon slurry material as deposited onto the sheet of electrically-nonconductive substrate material in the previous step across the porous sheet of electrically-nonconductive substrate material to achieve a layer of desired thickness for the carbon slurry material and to cause a portion of the carbon slurry material to diffuse into the surface of the porous sheet of substrate material and permanently adhere to and unite with a portion of the sheet of substrate material in an integrated, interlocking fashion; drying the sheet of substrate material having the layer of carbon slurry material integrated therewith to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque comprising an aggregation of porous carbon globules and having a network of cracks produced therethrough in a random pattern as a result of the shrinkage during drying; and physically reworking the layer of carbon plaque to close cracks at the upper surface of the layer of carbon plaque while simultaneously maintaining a desired thickness for said layer.
Claim 2
Independent Claim
211 words
A method for fabricating an integrated carbon/insulator structure for an electrochemical cell, comprising the steps of: depositing a quantity of a wet carbon slurry material onto a porous sheet of an electrically-nonconductive substrate material; physically working the quantity of wet carbon slurry material as deposited onto the sheet of electrically-nonconductive substrate material in the previous step across the porous sheet of electrically-nonconductive substrate material to achieve a layer of desired thickness for the carbon slurry material and to cause a portion of the carbon slurry material to diffuse into the surface of the porous sheet of substrate material and permanently adhere to and unite with a portion of the sheet of substrate material in an integrated, interlocking fashion; drying the sheet of substrate material having the layer of carbon slurry material integrated therewith to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque comprising an aggregation of porous carbon globules and having a network of cracks produced therethrough in a random pattern as a result of the shrinkage during drying; and physically reworking the layer of carbon plaque to close cracks at the upper surface of the layer of carbon plaque while simultaneously maintaining a desired thickness for said layer.
Claim 3
Dependent Claim
38 words
A method in accordance with claim 1 further comprising the step of: cutting from the sheet of substrate material having the reworked layer of carbon plaque interlocked therewith an integrated carbon/insulator structure of a desired size and configuration.
Claim 4
Dependent Claim
17 words
A method in accordance with claim 1 wherein: the sheet of electrically-nonconductive substrate material is of fiberglass.
Claim 5
Dependent Claim
21 words
A method in accordance with claim 1 wherein: the carbon slurry material includes a mixture of carbon black and a liquid.
Claim 6
Dependent Claim
20 words
A method in accordance with claim 4 wherein: the liquid of the carbon slurry material includes water and isopropyl alcohol.
Claim 7
Dependent Claim
107 words
A method in accordance with claim 1 wherein: the wet carbon slurry material includes a mixture of carbon black and a liquid; and the step of drying the sheet of substrate material having the layer of wet carbon slurry material integrated therewith comprises the steps of: blotting the sheet of substrate material having the layer of wet carbon slurry material integrated therewith to remove excess liquid; and drying the aforesaid arrangement at an elevated temperature to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque having a network of cracks produced therethrough in a random pattern.
Claim 8
Dependent Claim
20 words
A method in accordance with claim 6 wherein: the liquid of the carbon slurry material includes water and isopropyl alcohol.
Claim 9
Dependent Claim
40 words
A method in accordance with claim 1 wherein: each of the steps of working the quantity of wet carbon slurry material onto and across the sheet of substrate material and reworking the layer of carbon plaque includes a rolling operation.
Claim 10
Dependent Claim
99 words
A method in accordance with claim 1 wherein: the wet carbon slurry material includes a mixture of carbon black, a liquid, and a curable binder material in suspension for increasing the adherence of the carbon globules of the carbon plaque to each other and to the sheet of substrate material; and wherein the method further comprises the additional step, following the reworking step, of: curing the sheet of substrate material having the layer of carbon plaque integrated therewith to cause increased adherence of the carbon globules of the plaque to each other and to the sheet of substrate material.
Claim 11
Independent Claim
240 words
A method for fabricating an integrated carbon/insulator structure for a primary electrochemical cell, comprising the steps of: depositing a quantity of a wet carbon slurry material including carbon black and a liquid onto a porous fiberglass substrate, said porous fiberglass substrate having a thickness in a range of 0.001 to 0.007 inch; rolling the quantity of carbon slurry material onto and across the porous fiberglass substrate to achieve a layer of the carbon slurry material having a thickness in the range of 0.003 to 0.020 inch and to cause a portion of the carbon slurry material to diffuse into the surface of the porous fiberglass substrate and permanently adhere to and unite with a surface portion of the porous fiberglass substrate in an integrated, interlocking fashion; drying the porous fiberglass substrate and the layer of carbon slurry material integrated therewith to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque comprising an aggregation of porous carbon globules and having a network of cracks produced therethrough in a random pattern as a result of the shrinkage during drying: re-rolling the layer of carbon plaque to close cracks at the upper surface of the layer while simultaneously establishing a desired final thickness for the layer; and cutting from the porous fiberglass substrate having the re-rolled layer of carbon plaque interlocked therewith an integrated carbon/insulator structure of a desired size and configuration.
Claim 12
Independent Claim
240 words
A method for fabricating an integrated carbon/insulator structure for a primary electrochemical cell, comprising the steps of: depositing a quantity of a wet carbon slurry material including carbon black and a liquid onto a porous fiberglass substrate, said porous fiberglass substrate having a thickness in a range of 0.001 to 0.007 inch; rolling the quantity of carbon slurry material onto and across the porous fiberglass substrate to achieve a layer of the carbon slurry material having a thickness in the range of 0.003 to 0.020 inch and to cause a portion of the carbon slurry material to diffuse into the surface of the porous fiberglass substrate and permanently adhere to and unite with a surface portion of the porous fiberglass substrate in an integrated, interlocking fashion; drying the porous fiberglass substrate and the layer of carbon slurry material integrated therewith to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque comprising an aggregation of porous carbon globules and having a network of cracks produced therethrough in a random pattern as a result of the shrinkage during drying: re-rolling the layer of carbon plaque to close cracks at the upper surface of the layer while simultaneously establishing a desired final thickness for the layer; and cutting from the porous fiberglass substrate having the re-rolled layer of carbon plaque interlocked therewith an integrated carbon/insulator structure of a desired size and configuration.
Claim 13
Dependent Claim
20 words
A method in accordance with claim 10 wherein: the liquid of the carbon slurry material includes water and isopropyl alcohol.
Claim 14
Dependent Claim
102 words
A method in accordance with claim 10 wherein: the wet carbon slurry material includes a mixture of carbon black, a liquid, and a curable binder material in suspension for increasing the adherence of the porous carbon globules of the carbon plaque to each other and to the porous fiberglass substrate; and wherein the method further comprises the additional step, intermediate to the re-rolling and cutting steps, of: curing the porous fiberglass substrate having the layer of carbon plaque integrated therewith to cause increased adherence of the porous carbon globules of the carbon plaque to each other and to the porous fiberglass substrate.
Claim 15
Dependent Claim
90 words
A method in accordance with claim 12 wherein: the step of drying the porous fiberglass substrate having the layer of wet carbon slurry material integrated therewith comprises the steps of: blotting the porous fiberglass substrate having the layer of wet carbon slurry material integrated therewith to remove excess liquid; and drying the aforesaid arrangement at an elevated temperature to cause the layer of carbon slurry material to dry and shrink to the form of a layer of carbon plaque having a network of cracks produced therethrough in a random pattern.
Claim 16
Dependent Claim
24 words
A method in accordance with claim 13 wherein: the drying step at the elevated temperature takes place at a temperature of about 100° C.
Claim 17
Dependent Claim
20 words
A method in accordance with claim 14 wherein: the curing step takes place at a temperature of about 270° C.
References Cited (Backward Citations)
US2721154A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-21 | 1986-09-20 | 1987-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-21 | 1990-09-20 | 1991-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-21 | 1994-09-20 | 1995-03-22 | $7700.00 | Window Closed / Lapsed |