Rubber compositions of ethylene-propylene elastomers
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1981-02-27
•
Granted: 1983-03-08
•
Expires: 2001-02-27
Abstract
Abstract The invention provides a novel rubber composition based on an ethylene-propylene copolymeric rubbery elastomer and curable by hot air vulcanization under atmospheric pressure giving great advantages over conventional ones vulcanizable only under pressure. The inventive rubber composition comprises, in addition to the ethylene-propylene copolymeric rubbery elastomer, an oganopolysiloxane gum having alkenyl or mercapto groups in the molecule, a reinforcing silica filler, an organic compound having at least two maleimido groups in a molecule and a curing agent which is an organic peroxide or an organic sulfur compound.
Inventors
- 👤 Kunio Itoh
- 👤 Toshimichi Oshima
- 👤 Nobuyuki Uesugi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:46
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/16; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C08K3/34; C08K3/36; C08K5/00; C08K5/04; C08K5/09; C08K5/16; C08K5/20; C08K5/34; C08K5/3412; C08K5/3415; C08L83/00; C08L83/04; C08L91/00
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
109 words
A curable rubber composition which comprises (a) 100 parts by weight of a mixture composed of (a-1) from 40 to 99% by weight of an ethylene-propylene copolymeric elastomer, and (a-2) from 60 to 1% by weight of an organopolysiloxane gum having an average degree of polymerization of at least 1000 and containing at least one alkenyl group in a molecule, (b) from 10 to 150 parts by weight of a reinforcing silica filler having a specific area of at least 50 m 2 /g, (c) from 0.5 to 10 parts by weight of N,N'-m-phenylene bismaleimide or N,N'-(2,4-tolylene)dimaleimide, (d) from 0.1 to 10 parts by weight of a curing agent.
Claim 2
Dependent Claim
109 words
A curable rubber composition which comprises (a) 100 parts by weight of a mixture composed of (a-1) from 40 to 99% by weight of an ethylene-propylene copolymeric elastomer, and (a-2) from 60 to 1% by weight of an organopolysiloxane gum having an average degree of polymerization of at least 1000 and containing at least one alkenyl group in a molecule, (b) from 10 to 150 parts by weight of a reinforcing silica filler having a specific area of at least 50 m 2 /g, (c) from 0.5 to 10 parts by weight of N,N'-m-phenylene bismaleimide or N,N'-(2,4-tolylene)dimaleimide, (d) from 0.1 to 10 parts by weight of a curing agent.
Claim 3
Dependent Claim
29 words
The curable rubber composition as claimed in claim 1 wherein the propylene content in the ethylene-propylene copolymeric rubbery elastomer is in the range from 10 to 70% by moles.
Claim 4
Dependent Claim
27 words
The curable rubber composition as claimed in claim 1 wherein the curing agent is selected from the class consisting of sulfur, organic sulfur compounds and organic peroxides.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-07 | 1986-09-06 | 1987-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-07 | 1990-09-06 | 1991-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-07 | 1994-09-06 | 1995-03-08 | $7700.00 | Window Closed / Lapsed |