Particle board process using polymeric isocyanate/release agent
Assignee: Quaker Oats Co
•
Filing: 1981-06-15
•
Granted: 1983-03-08
•
Expires: 2001-06-15
Abstract
Abstract A binder system is disclosed which incorporates an internal release agent and comprises a mixture of polyisocyanate resin, furfural and an ester of phosphoric acid. In the process of the invention the ester of phosphoric acid is placed into solution with furfural and subsequently blended with the polyisocyanate. Increased stability of the binder system is observed as well as providing for increased mold releasing capabilities.
Inventors
- 👤 Ben R. Bogner
- 👤 Francis C. Grant-Acquah
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 08:09
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/49; C08K5/51; C08K5/52; C08K5/521; B; B27; B27N; B27N3/00; B29; B29C; B29C33/00; B29C33/56; B29C33/60; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/64; C08G18/6484; C08G18/70; C08L; C08L97/00; C08L97/02; C08G2125/00; C08L2205/00; C08L2205/06; C08L75/00; C08L75/04
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
69 words
A process for the preparation of a particle board comprising the steps of mixing furfural and a phosphate to form a stable release agent solution, blending a polyisocyanate with said release agent solution to form a binder system, mixing said binder system with wood chip particles and molding said mixture of said binder system and cellulosic material under heat to form a board of good strength and water resistance.
Claim 2
Dependent Claim
69 words
A process for the preparation of a particle board comprising the steps of mixing furfural and a phosphate to form a stable release agent solution, blending a polyisocyanate with said release agent solution to form a binder system, mixing said binder system with wood chip particles and molding said mixture of said binder system and cellulosic material under heat to form a board of good strength and water resistance.
Claim 3
Dependent Claim
25 words
The process of claim 1 wherein said binder system and said wood chip particles are molded at 350° F. for 41/2 minutes at 500 psi.
Claim 4
Dependent Claim
44 words
The process of claim 1 wherein said release agent solution is blended with said polyisocyanate to form a solution having a furfural content of from 0-50 percent by weight, and a content of phosphate from 0.1-5 percent by weight of the isocyanate resin solids.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-07 | 1986-09-06 | 1987-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-07 | 1990-09-06 | 1991-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-07 | 1994-09-06 | 1995-03-08 | $7700.00 | Window Closed / Lapsed |