Containment of nuclear waste
Assignee: Westinghouse Electric Corp
•
Filing: 1980-06-25
•
Granted: 1983-03-08
•
Expires: 2000-06-25
Abstract
Abstract Disclosed is a method of immobilizing nuclear waste in glass. A composition is prepared of about 30 to about 85% of a hydrolyzed glass-forming silicon compound, about 5 to about 30% of a glass-forming sodium compound, up to about 30% of a glass-forming aluminum compound, and about 5 to about 30% of a glass-forming boron, calcium, or magnesium compound. Up to an equal amount of nuclear waste is mixed into the composition and the mixture is heated at up to 500 DEG C. until dry. The mixture is then melted at 800 DEG to 1300 DEG C., and can be poured into ingots and cooled. The mixture can also be melted in situ with a laser.
Inventors
- 👤 James M. Pope
- 👤 Don E. Harrison
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:08
CPC Classifications
G; G21; G21F; G21F9/00; G21F9/04; G21F9/06; G21F9/16; C; C03; C03C; C03C1/00; C03C1/002; B; B09; B09B; B09B3/00; B09B3/20; B09B3/25; B09B3/29; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C3/076; C03C3/089; C03C3/091; G21F9/28; G21F9/30; G21F9/301; G21F9/302; G21F9/305
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
334 words
A method of immobilizing nuclear waste comprising: (A) preparing a composition which comprises (1) about 30% to about 85% by weight, calculated as SiO 2 , of a silicon compound having the general formula SiR m (OR') n X p or Si(OSiR 3 ) 4 where each R is independently selected from alkyl to C 10 and alkenyl to C 10 , each R' is independently selected from R and aryl, each X is independently selected from chlorine and bromine, m is 0 to 3, n is 0 to 4, p is 0 to 1, and m+n+p equals 4; (2) about 5% to about 30% by weight, calculated as Na 2 O, of a sodium compound having the general formula NaOR" or NaZR' 3 , where each R" is independently selected from R and hydrogen, and Z is carbon or boron; (3) up to about 30% by weight, calculated as Al 2 O 3 , of an aluminum compound having the general formula AlR' q (OR") r X s or Mg(Al(OR) 4 ) 2 , q is 0 to 3, r is 0 to 3, s is 0 to 1, and q+r+s equals 3; (4) about 5% to about 30% by weight, calculated as the corresponding oxide, of a compound selected from the group consisting of boron compounds having the general formula BR' q (OR") r X s , where q+r+s equals 3, alkaline earth metal compounds having the general formula MR t (OR") u X v where M is calcium or magnesium, t is 0 to 2, u is 0 to 2, v is 0 to 1, and t+u+v equals 2, lithium compounds having the general formula LiOR, and mixtures thereof, said composition being at least partially hydrolyzed; (B) mixing into said composition up to about to an equal amount by weight of said nuclear waste at up to 500° C. until the mixture is dry and organics have been removed; and (C) melting said mixture at about 800° C. to 1300° C.
Claim 2
Independent Claim
334 words
A method of immobilizing nuclear waste comprising: (A) preparing a composition which comprises (1) about 30% to about 85% by weight, calculated as SiO 2 , of a silicon compound having the general formula SiR m (OR') n X p or Si(OSiR 3 ) 4 where each R is independently selected from alkyl to C 10 and alkenyl to C 10 , each R' is independently selected from R and aryl, each X is independently selected from chlorine and bromine, m is 0 to 3, n is 0 to 4, p is 0 to 1, and m+n+p equals 4; (2) about 5% to about 30% by weight, calculated as Na 2 O, of a sodium compound having the general formula NaOR" or NaZR' 3 , where each R" is independently selected from R and hydrogen, and Z is carbon or boron; (3) up to about 30% by weight, calculated as Al 2 O 3 , of an aluminum compound having the general formula AlR' q (OR") r X s or Mg(Al(OR) 4 ) 2 , q is 0 to 3, r is 0 to 3, s is 0 to 1, and q+r+s equals 3; (4) about 5% to about 30% by weight, calculated as the corresponding oxide, of a compound selected from the group consisting of boron compounds having the general formula BR' q (OR") r X s , where q+r+s equals 3, alkaline earth metal compounds having the general formula MR t (OR") u X v where M is calcium or magnesium, t is 0 to 2, u is 0 to 2, v is 0 to 1, and t+u+v equals 2, lithium compounds having the general formula LiOR, and mixtures thereof, said composition being at least partially hydrolyzed; (B) mixing into said composition up to about to an equal amount by weight of said nuclear waste at up to 500° C. until the mixture is dry and organics have been removed; and (C) melting said mixture at about 800° C. to 1300° C.
Claim 3
Dependent Claim
20 words
A method according to claim 1 including the additional last step of pouring said melted mixture into ingots and cooling.
Claim 4
Dependent Claim
16 words
A method according to claim 1 wherein said melting is accomplished in situ with a laser.
Claim 5
Dependent Claim
57 words
A method according to claim 1 wherein said nuclear waste is up to about 10% by weight sulfate, phosphate, and nitrate, up to about 85% by weight water, and the remainder is selected from the group consisting of oxides, hydroxides, and mixtures thereof of silicon, aluminum, manganese, iron, calcium, uranium, sodium, potassium, cesium, ruthenium, mercury, and nickel.
Claim 6
Dependent Claim
120 words
A method according to claim 1 wherein said silicon compound has the general formula SiR m (OR') n X p where R' is alkyl to C 4 and n=4, said sodium compound has the general formula NaOR" where R" is alkyl to C 4 , said aluminum compound has the general formula AlR' q (OR") r X s where R" is alkyl to C 4 and r is 3, said boron compound has the general formula BR' q (OR") r X s where R" is alkyl to C 4 and r is 3, and said alkaline earth metal compound has the general formula MR t (OR") u X v where R" is alkyl to C 4 and u is 2.
Claim 7
Dependent Claim
43 words
A method according to claim 1 wherein said silicon compound is tetraethylorthosilicate, said sodium compound is sodium methylate, said aluminum compound is aluminum secondary butoxide, and said boron compound is selected from the group consisting of trimethyl borate, triethyl borate, and mixtures thereof.
Claim 8
Dependent Claim
46 words
A method according to claim 1 wherein said silicon compound is hydrolyzed in alcohol at a molar ratio of silicon compound to alcohol of about 0.2 to about 2, with water at a molar ratio of silicon compound to water of about 0.1 to about 5.
Claim 9
Dependent Claim
22 words
A method according to claim 1 wherein said silicon compound is at least partially hydrolyzed prior to its addition to said composition.
Claim 10
Dependent Claim
12 words
Glass immobilized nuclear waste made according to the method of claim 1.
References Cited (Backward Citations)
US3597252A
Cited
US3759683A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-07 | 1986-09-06 | 1987-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-07 | 1990-09-06 | 1991-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-07 | 1994-09-06 | 1995-03-08 | $7700.00 | Window Closed / Lapsed |