Catalytic supports with controlled pore properties
Assignee: Chevron USA Inc
•
Filing: 1981-08-03
•
Granted: 1983-03-08
•
Expires: 2001-08-03
Abstract
Abstract A catalyst support suitable for use in a cracking process or hydrotreating process having outstanding thermal stability comprising (I) a selected Group IIB metal compound, combinations thereof, and combinations of Group IIB and Group IIA metal compounds, (II) alumina and (III) aluminum phosphate.
Inventors
- 👤 Roger F. Vogel
- 👤 George Marcelin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:09
CPC Classifications
B; B01; B01J; B01J27/00; B01J27/14; B01J27/16; B01J35/00; B01J35/60; B01J35/61; B01J35/615; B01J35/63; B01J35/635; B01J35/64; B01J35/647
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
176 words
A catalyst support comprising (A)(I) a Group IIB metal compound selected from the group consisting of zinc and cadmium compounds, (II) a combination of said zinc and cadmium compounds or (III) a combination of at least one of said Group IIB metals compounds with at least one Group IIA metal compound selected from the group consisting of magnesium, calcium, strontium and barium compounds; (B) alumina and (C) aluminum phosphate matrix, characterized after calcination at 500° C. for about 10 hours as amorphous, and having an average pore radius of from about 10 A to about 300 A, a surface area ranging from about 80 m 2 /g to about 350 m 2 /g, a pore volume of from about 0.3 cc/g to about 1.5 cc/g and wherein component (A) is present in an amount ranging from about 0.5 to about 75 mole percent, component (B) is present in an amount ranging from about two to about 90 mole percent and component (C) is present in an amount ranging from about three to about 95 mole percent.
Claim 2
Dependent Claim
176 words
A catalyst support comprising (A)(I) a Group IIB metal compound selected from the group consisting of zinc and cadmium compounds, (II) a combination of said zinc and cadmium compounds or (III) a combination of at least one of said Group IIB metals compounds with at least one Group IIA metal compound selected from the group consisting of magnesium, calcium, strontium and barium compounds; (B) alumina and (C) aluminum phosphate matrix, characterized after calcination at 500° C. for about 10 hours as amorphous, and having an average pore radius of from about 10 A to about 300 A, a surface area ranging from about 80 m 2 /g to about 350 m 2 /g, a pore volume of from about 0.3 cc/g to about 1.5 cc/g and wherein component (A) is present in an amount ranging from about 0.5 to about 75 mole percent, component (B) is present in an amount ranging from about two to about 90 mole percent and component (C) is present in an amount ranging from about three to about 95 mole percent.
Claim 3
Dependent Claim
102 words
The catalyst support of claim 1 wherein said matrix has an average pore radius of from about 75 A to about 200 A, a surface area of from about 125 m 2 /g to about 250 m 2 /g, a pore volume of from about 0.5 cc/g to about 1.2 cc/g and wherein component (A) is present in an amount ranging from about two to about 70 mole percent, component (B) is present in an amount ranging from about eight to about 80 mole percent and component (C) is present in an amount ranging from about five to about 80 mole percent.
Claim 4
Dependent Claim
12 words
The catalyst support of claim 1 wherein component (A) is zinc oxide.
Claim 5
Dependent Claim
12 words
The catalyst support of claim 2 wherein component (A) is zinc oxide.
Claim 6
Dependent Claim
12 words
The catalyst support of claim 1 wherein component (A) is cadmium oxide.
Claim 7
Dependent Claim
12 words
The catalyst support of claim 2 wherein component (A) is cadmium oxide.
Claim 8
Dependent Claim
17 words
The catalyst support of claim 1 wherein component (A) is composed of zinc oxide and cadmium oxide.
Claim 9
Dependent Claim
17 words
The catalyst support of claim 2 wherein component (A) is composed of zinc oxide and cadmium oxide.
Claim 10
Dependent Claim
17 words
The catalyst support of claim 1 wherein component (A) is composed of zinc oxide and magnesium oxide.
Claim 11
Dependent Claim
17 words
The catalyst support of claim 2 wherein component (A) is composed of zinc oxide and magnesium oxide.
Claim 12
Dependent Claim
17 words
The catalyst support of claim 1 wherein component (A) is composed of zinc oxide and calcium oxide.
Claim 13
Dependent Claim
17 words
The catalyst support of claim 2 wherein component (A) is composed of zinc oxide and calcium oxide.
References Cited (Backward Citations)
US4210560A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-07 | 1986-09-06 | 1987-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-07 | 1990-09-06 | 1991-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-07 | 1994-09-06 | 1995-03-08 | $7700.00 | Window Closed / Lapsed |