Additive combination for hydraulic cement compositions
Assignee: WR Grace and Co Conn
•
Filing: 1981-11-23
•
Granted: 1983-03-08
•
Expires: 2001-11-23
Abstract
Abstract The low temperature stability of an additive product for imparting desirable properties such as water repellency, set-retardation, etc., to hydraulic cement compositions and Portland masonry cements in particular, is improved by the addition of a small amount of certain low molecular weight, water soluble, non-ionic organic materials (e.g. alcohols, ketones, amides, and aldehydes) to the additive product. The use of low-temperature stabilizers within this class which also act as grinding aids for hydraulic cements (e.g. glycols) is highly preferred, since the use of such materials as the stabilizing ingredient has been found to additionally impart grinding aid properties to the additive product even at the relatively low usage rates of the stabilizing component. This additional property of the resulting product is a very desirable advantage to the user of the product since the product is customarily added to the cement during the grinding operation.
Inventors
- 👤 Bruce A. Lange
- 👤 Heyman C. Duecker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:59
CPC Classifications
C; C04; C04B; C04B24/00; C04B24/08; C04B28/00; C04B28/02; C04B28/04
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
94 words
An improved additive for hydraulic cement compositions which additive is readily dispersible in water and comprises an oil-in-water emulsion in which the solids portion is comprised of a major proportion of a water-insoluble, water-repelling acid component to impart water-repelling properties to said cement, from about 3 to about 30 percent by weight of a set-retarding component for said cement, emulsifier, and a stabilizing component comprising a low molecular weight non-ionic, water soluble organic compound, the amount of said stabilizing component being at least sufficient to maintain said emulsion stable when exposed to low temperature.
Claim 2
Dependent Claim
94 words
An improved additive for hydraulic cement compositions which additive is readily dispersible in water and comprises an oil-in-water emulsion in which the solids portion is comprised of a major proportion of a water-insoluble, water-repelling acid component to impart water-repelling properties to said cement, from about 3 to about 30 percent by weight of a set-retarding component for said cement, emulsifier, and a stabilizing component comprising a low molecular weight non-ionic, water soluble organic compound, the amount of said stabilizing component being at least sufficient to maintain said emulsion stable when exposed to low temperature.
Claim 3
Dependent Claim
14 words
The additive of claim 1 wherein said acid component is derived from tall oil.
Claim 4
Dependent Claim
21 words
The additive of claim 1 wherein said stabilizing component is comprised of an alcohol, ketone, aldehyde, amide or mixture of such.
Claim 5
Dependent Claim
141 words
An improved additive for Portland masonry cement compositions, which additive is readily dispersible in water and comprises an oil-in-water emulsion containing water and a solids portion comprised of a major proportion of a water-insoluble, water-repelling acid component selected from the group consisting of fatty acids, rosin acids and mixtures thereof, from about 3 to about 30 percent by weight of solids of a water-soluble, set-retarding component for said cement, at least about 0.5 percent by weight of an emulsifier formed by reacting said acid component with a base capable of forming a salt thereof, and a stabilizing component comprising a low-molecular weight, non-ionic, water soluble organic compound selected from the group consisting of alcohols, ketones, aldehydes, amides, and mixtures of such, the amount of said stabilizing component being at least sufficient to maintain said emulsion stable when exposed to low temperature.
Claim 6
Dependent Claim
141 words
An improved additive for Portland masonry cement compositions, which additive is readily dispersible in water and comprises an oil-in-water emulsion containing water and a solids portion comprised of a major proportion of a water-insoluble, water-repelling acid component selected from the group consisting of fatty acids, rosin acids and mixtures thereof, from about 3 to about 30 percent by weight of solids of a water-soluble, set-retarding component for said cement, at least about 0.5 percent by weight of an emulsifier formed by reacting said acid component with a base capable of forming a salt thereof, and a stabilizing component comprising a low-molecular weight, non-ionic, water soluble organic compound selected from the group consisting of alcohols, ketones, aldehydes, amides, and mixtures of such, the amount of said stabilizing component being at least sufficient to maintain said emulsion stable when exposed to low temperature.
Claim 7
Dependent Claim
24 words
The additive of claim 1 or 4 containing as an additional component other than the components recited, an air-entraining agent for said cement composition.
Claim 8
Dependent Claim
39 words
The additive of claims 1 or 4 wherein said stabilizing component also acts to impart an ability to said additive to improve the efficiency of the grinding operation when said additive is added to said cement during grinding thereof.
Claim 9
Dependent Claim
22 words
The additive of claims 1 or 4 wherein said stabilizing component is an alcohol, urea, a polyhydric alcohol, or mixture of such.
Claim 10
Dependent Claim
15 words
The additive of claims 1 or 4 wherein said stabilizing component is an alkylene glycol.
Claim 11
Dependent Claim
137 words
An improved additive for Portland masonry cement compositions, which additive is readily dispersible in water and comprises an oil-in-water emulsion containing water and a solids portion containing a major proportion of tall oil acid, from about 3 to about 35 percent by weight of a retarder of the setting time of said cement, at least about 0.5 percent by weight of a salt of said acid as an emulsifier, from 1 to about 5 percent by weight of an air-entraining agent for said cement, and from about 3 to about 25 percent by weight of said emulsion of a polyhydric alcohol, said alcohol acting to stabilize said emulsion when said emulsion is exposed to low temperature and also to improve the efficiency of the grinding operation when said additive is added to said cement during grinding thereof.
Claim 12
Dependent Claim
137 words
An improved additive for Portland masonry cement compositions, which additive is readily dispersible in water and comprises an oil-in-water emulsion containing water and a solids portion containing a major proportion of tall oil acid, from about 3 to about 35 percent by weight of a retarder of the setting time of said cement, at least about 0.5 percent by weight of a salt of said acid as an emulsifier, from 1 to about 5 percent by weight of an air-entraining agent for said cement, and from about 3 to about 25 percent by weight of said emulsion of a polyhydric alcohol, said alcohol acting to stabilize said emulsion when said emulsion is exposed to low temperature and also to improve the efficiency of the grinding operation when said additive is added to said cement during grinding thereof.
Claim 13
Dependent Claim
15 words
The additive of claims 4 or 9 wherein said salt is an alkali metal salt.
Claim 14
Dependent Claim
15 words
The additive of claims 1, 4 or 9 wherein said set-retarding agent is a carbohydrate.
Claim 15
Dependent Claim
17 words
The additive of claim 9 wherein said air-entraining agent is a condensation product of a ethylene oxide.
Claim 16
Dependent Claim
25 words
The additive of claims 4 or 9 wherein said retarder is a carbohydrate and said emulsifier is formed by reacting said acid with sodium hydroxide.
Claim 17
Dependent Claim
19 words
The method which comprises intergrinding Portland cement in the presence of an additive of claim 1, 4, or 9.
Claim 18
Dependent Claim
18 words
The method of claim 14 wherein said additive is mixed with water prior to addition to said cement.
Claim 19
Dependent Claim
31 words
The method of claim 14 wherein the amount of additive employed ranges from about 0.001 to about 0.3 percent by weight of additive solids based upon the weight of said cement.
Claim 20
Dependent Claim
29 words
The method of claim 14 wherein said cement is interground along with a material selected from the group consisting of limestone, pozzolan, chalk, talc, clay, gypsum, and mixtures thereof.
References Cited (Backward Citations)
US1772999A
Cited
US1965935A
Cited
US2060425A
Cited
US2307744A
Cited
US2573599A
Cited
US2828345A
Cited
US3008843A
Cited
US3408297A
Cited
US3507791A
Cited
US3635834A
Cited
US3865601A
Cited
US3885985A
Cited
US3998733A
Cited
US3943954A
Cited
US4010105A
Cited
US4110213A
Cited
US4097403A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-03-07 | 1986-09-06 | 1987-03-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-03-07 | 1990-09-06 | 1991-03-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-03-07 | 1994-09-06 | 1995-03-08 | $7700.00 | Window Closed / Lapsed |