Abstract
Abstract A method of making a coated tip for cutting purposes having a lower degree of flank and crater wear and reduced chipping. A WC-based ultrahard alloy containing WC, at least one nitride selected from among TiN, TaN and NbN and a bonding metal is heat treated at a temperature of 800° C. to 1,300° C. in a nitrogen atmosphere for a sufficiently long period of time to cause nitride in a layer in the vicinity of the surface of the alloy to move to the surface to form a layer of nitride thereon as well as an alloy layer of WC and the bonding metal in which the nitride has been reduced. The surface of the tip is then coated with a layer of Al 2 O 3 .
Inventors
- 👤 Junichiro Suzuki
- 👤 Hiroshi Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:56
CPC Classifications
B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C; C23; C23C; C23C16/00; C23C16/02; C23C16/0209; C23C16/22; C23C16/30; C23C16/40; C23C16/403; C23C30/00; C23C30/005; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12021
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
123 words
A method of making a coated tip for cutting purposes, comprising the steps of heat treating a WC-based ultrahard alloy containing WC, at least one nitride selected from the group consisting of TiN, TaN and NbN, and a bonding metal at a temperature of 800° C. to 1,300° C. ; in an atmosphere containing nitrogen for a sufficient time to cause said nitride in a layer in the vicinity of the surface of said alloy to move to said surface to form a layer of said nitride on said surface and to form an alloy layer of said WC and said bonding metal in which said nitride has been reduced; and coating said surface with a layer of Al 2 O 3 .
Claim 2
Independent Claim
123 words
A method of making a coated tip for cutting purposes, comprising the steps of heat treating a WC-based ultrahard alloy containing WC, at least one nitride selected from the group consisting of TiN, TaN and NbN, and a bonding metal at a temperature of 800° C. to 1,300° C. ; in an atmosphere containing nitrogen for a sufficient time to cause said nitride in a layer in the vicinity of the surface of said alloy to move to said surface to form a layer of said nitride on said surface and to form an alloy layer of said WC and said bonding metal in which said nitride has been reduced; and coating said surface with a layer of Al 2 O 3 .
Claim 3
Dependent Claim
55 words
The method of making a coating tip for cutting purposes as set forth in claim 1, wherein said nitride layer has a thickness 1 to 8μ, said Al 2 O 3 layer has a thickness of 1 to 5μ, and said nitride and Alhd 2O 3 layers have a total thickness of 2 to 10μ.
Claim 4
Dependent Claim
36 words
The method of making a coating tip for cutting purposes as set forth in claim 1 or 2, wherein said step of coating said surface with a layer of Al 2 O 3 comprises CVD deposition.
Claim 5
Independent Claim
130 words
A method of making a coated tip for cutting purposes, comprising the steps of heat treating a WC-based ultrahard alloy containing WC, at least one nitride selected from the group consisting of TiN, TaN and NbN, and a bonding metal at a temperature of approximately 1,200° C. for approximately 2 hours in a nitrogen atmosphere to form a nitride layer having a thickness of 1 to 7μ on the surface of said tip; placing said tip in a reaction chamber; and heating set tip in said reaction chamber to a temperature of approximately 1,100° C. while supplying a gas mixture containing approximately 59% of H 2 , 3% of Co and Co 2 , and 8% of AlCl 3 at a pressure of approximately 20 Torr of approximately 2 hours.
Claim 6
Independent Claim
130 words
A method of making a coated tip for cutting purposes, comprising the steps of heat treating a WC-based ultrahard alloy containing WC, at least one nitride selected from the group consisting of TiN, TaN and NbN, and a bonding metal at a temperature of approximately 1,200° C. for approximately 2 hours in a nitrogen atmosphere to form a nitride layer having a thickness of 1 to 7μ on the surface of said tip; placing said tip in a reaction chamber; and heating set tip in said reaction chamber to a temperature of approximately 1,100° C. while supplying a gas mixture containing approximately 59% of H 2 , 3% of Co and Co 2 , and 8% of AlCl 3 at a pressure of approximately 20 Torr of approximately 2 hours.
References Cited (Backward Citations)
DE2253745A1
Cited
USRE29420E
Cited
US3955038A
Cited
US3994692A
Cited
US4018631A
Cited
US4212671A
Cited
US4180400A
Cited
US4282289A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-21 | 1986-08-23 | 1987-02-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-21 | 1990-08-23 | 1991-02-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-21 | 1994-08-23 | 1995-02-22 | $7700.00 | Window Closed / Lapsed |