Ceramic fiber foam and method for making same
Assignee: RM Engineered Products Inc
•
Filing: 1980-12-23
•
Granted: 1983-02-15
•
Expires: 2000-12-23
Abstract
Abstract Ceramic fiber is co-dispersed in a liquid medium together with a heat curable organic binder, and the mixture is beaten preferably with small amounts of a crystallizable salt and fillers. Upon beating, the mixture is foamed, and the foam is then heated to cure the binder, evaporate the liquid, and stabilize the foam. The foam may be used as is, but is preferably further heated to decompose most of the organic binder and to cause bonding between intersecting fibers by the salt, thereby resulting in a stable foam that has excellent high temperature properties.
Inventors
- 👤 Jerry Zucker
- 👤 Beth W. Porlier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 17:03
CPC Classifications
G; G21; G21C; G21C11/00; G21C11/08; C; C04; C04B; C04B26/00; C04B26/02; C04B26/04; C04B28/00; C04B30/00; C04B30/02; C08; C08J; C08J9/00; C08J9/0085; C08J9/30; C08J9/35; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
76 words
A light weight heat resistant body, said body comprising from about 50 to about 95 percent ceramic fiber, exclusive of glass and asbestos fiber, in the form of a porous elastic foam, said fiber being selected from the group containing at least one of aluminum oxide and calcium oxide, said body having a bulk density of from about 0.3 to about 6 pounds per cubic foot and being resistant to temperatures in excess of 1900° F.
Claim 2
Dependent Claim
76 words
A light weight heat resistant body, said body comprising from about 50 to about 95 percent ceramic fiber, exclusive of glass and asbestos fiber, in the form of a porous elastic foam, said fiber being selected from the group containing at least one of aluminum oxide and calcium oxide, said body having a bulk density of from about 0.3 to about 6 pounds per cubic foot and being resistant to temperatures in excess of 1900° F.
Claim 3
Dependent Claim
17 words
The product of claim 1 wherein the body contains from zero to about 30 percent inorganic fillers.
Claim 4
Dependent Claim
17 words
The product of claim 2 wherein said inorganic fillers comprise mica, vermiculite, glass microspheres, and mixtures thereof.
Claim 5
Dependent Claim
13 words
The product of claim 1 wherein the body additionally comprises a crystallizable salt.
Claim 6
Independent Claim
87 words
A method for making a low density inorganic foam material comprising the steps of co-dispersing solids comprising ceramic fibers having a melting point in excess of 1900° F. and an organic binder in an aqueous medium together with a surfactant, said solids comprising less than 15% by weight of the aqueous dispersion, beating the dispersion into a foam, and heating the foam to cure the binder while drying the foam to a porous elastic body having a bulk density of less than 6 pounds per cubic foot.
Claim 7
Independent Claim
87 words
A method for making a low density inorganic foam material comprising the steps of co-dispersing solids comprising ceramic fibers having a melting point in excess of 1900° F. and an organic binder in an aqueous medium together with a surfactant, said solids comprising less than 15% by weight of the aqueous dispersion, beating the dispersion into a foam, and heating the foam to cure the binder while drying the foam to a porous elastic body having a bulk density of less than 6 pounds per cubic foot.
Claim 8
Dependent Claim
23 words
The method of claim 5 wherein the foam containing the cured binder is then heated above the decomposition temperature of the organic binder.
Claim 9
Dependent Claim
12 words
The method of claim 5 wherein the organic binder is an elastomer.
Claim 10
Independent Claim
94 words
A method for making a ceramic fiber foam comprising the steps of forming an aqueous mixture of less than 15% solids and water, said solids comprising from about 50 to about 95 percent ceramic fiber, from about 3 to about 20 percent water dispersion of a heat curable elastomer, from zero to about 30 percent inorganic fillers, from zero to one percent metallic salt and from one to about 20 percent surfactant, beating the mixture for a time sufficient to form a wet foam, and heating the wet foam sufficiently to cure the elastomer.
Claim 11
Independent Claim
94 words
A method for making a ceramic fiber foam comprising the steps of forming an aqueous mixture of less than 15% solids and water, said solids comprising from about 50 to about 95 percent ceramic fiber, from about 3 to about 20 percent water dispersion of a heat curable elastomer, from zero to about 30 percent inorganic fillers, from zero to one percent metallic salt and from one to about 20 percent surfactant, beating the mixture for a time sufficient to form a wet foam, and heating the wet foam sufficiently to cure the elastomer.
Claim 12
Dependent Claim
23 words
The method of claim 8 wherein the foam containing the cured elastomer is then further heated above the decomposition temperature of the elastomer.
Claim 13
Dependent Claim
31 words
The method of claim 8 wherein the ceramic fiber is treated with a coupling agent selected from the group consisting of silanes and titanates prior to formation of the aqueous mixture.
References Cited (Backward Citations)
US3007806A
Cited
GB1033560A
Cited
US3461191A
Cited
US3510323A
Cited
US3756839A
Cited
US4286999A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-02-14 | 1986-08-16 | 1987-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-02-14 | 1990-08-16 | 1991-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-02-14 | 1994-08-16 | 1995-02-15 | $7700.00 | Window Closed / Lapsed |