Method of preparing a sizing composition for treating glass fibers

Claim 2

A stable aqueous emulsion for incorporation into a sizing composition for treating glass fibers, comprising: about 0.1 to about 10 parts per hundred parts of resin of unhydrolyzed amino-functional silane, one hundred parts of a polyester resin having free carboxyl functionality and having ethylenic unsaturation and where the polyester and silane are combined to favor the acid-base salt reaction between the free carboxyl groups of the polyester resin and the amine group of the silane over the formation of silane dimers by combination of hydrolyzed silanes, and an amount of water to produce an emulsion having a total solids content in the range of about 5 to about 20 weight percent.

Claim 5

The method of claim 2 wherein the polyester resin having the carboxyl functionality is a polyester resin with terminal carboxyl functionality.

Claim 6

Method of claim 2 wherein the polyester resin with carboxyl functionality is a polyester resin having pendant carboxyl functionality.

Claim 7

Method of claim 2 wherein the polyester resin with carboxyl functionality is a polyester resin having pendant and terminal carboxyl functionality.

Claim 8

Method of claim 2 wherein the unhydrolyzed amino-silane is gamma aminopropyltrimethoxysilane.

Claim 9

Method of claim 2 wherein the dilution is performed by adding water.

Claim 10

Method of claim 2 wherein the dilution is performed by adding an aqueous medium containing emulsifying agent and plasticizer.

Claim 11

Method of claim 2 wherein the polyester resin is a combination of two polyester resins one having pendant carboxyl functionality and the other having terminal carboxyl functionality.

Claim 12

Method according to claim 9 wherein 25 percent of the unhydrolyzed amino-functional silane is added to the polyester resin with terminal carboxyl functionality while 75 percent of the unhydrolyzed amino-functional silane is added to the polyester resin with pendant carboxyl functionality.

Claim 13

Method according to claim 9 wherein 50 percent of the unhydrolyzed amino-silane is added to the polyester resin with terminal carboxyl functionality while 50 percent of the unhydrolyzed amino-functional silane is added to the polyester resin with the pendant carboxyl functionality.

Claim 14

Method according to claim 9 wherein 75 percent of the unhydrolyzed amino-functional silane is added to the polyester resin with terminal carboxyl functionality while 25 percent of the unhydrolyzed amino-functional silane is added to the polyester resin with pendant carboxyl functionality.

Claim 15

Method according to claim 2 or 9 wherein the stable emulsion is incorporated in a sizing composition.

Claim 16

A sizing composition for treating glass fibers, comprising: a solubilized, condensed, crosslinkable, first unsaturated polyester resin having pendant carboxyl groups, said polyester resin substantially insoluble in aromatic solvents when crosslinked; a second unsaturated water dispersible and insoluble polyester resin, said second polyester resin being insoluble in said first polyester resin in a water solution; a plasticizer; a first silane coupling agent that is an amino-functional silane in the unhydrolyzed state, which is combined with the first polyester resin to favor the acid-base salt reaction between the pendant carboxyl groups and the amine of the silane over the formation of silane dimers by combination of hydrolyzed amino silanes; a thermoplastic polymer being of sufficiently low molecular weight to impart pressure sensitive adhesive characteristics to said sizing composition; and a major amount of water to give a total solids content in the range of about 5 to about 17 weight percent.

Claim 17

A sizing composition for treating glass fibers, comprising: a solubilized, condensed, crosslinkable, first unsaturated polyester resin having pendant carboxyl groups, said polyester resin substantially insoluble in aromatic solvents when crosslinked; a second unsaturated water dispersible and insoluble polyester resin, said second polyester resin being insoluble in said first polyester resin in a water solution; a plasticizer; a first silane coupling agent that is an amino-functional silane in the unhydrolyzed state, which is combined with the first polyester resin to favor the acid-base salt reaction between the pendant carboxyl groups and the amine of the silane over the formation of silane dimers by combination of hydrolyzed amino silanes; a thermoplastic polymer being of sufficiently low molecular weight to impart pressure sensitive adhesive characteristics to said sizing composition; and a major amount of water to give a total solids content in the range of about 5 to about 17 weight percent.

Claim 18

The emulsion of claim 1 wherein the unhydrolyzed amino-silane has been hydrolyzed to a partially hydrolyzed amino-silane or mixture of unhydrolyzed and partially hydrolyzed silane.

Claim 19

Method according to claim 2 wherein the unhydrolyzed amino-silane has been hydrolyzed to a partially hydrolyzed amino-silane or mixture of unhydrolyzed and partially hydrolyzed amino-silane.

Claim 20

Sizing composition according to claim 14 wherein the amino-functional silane has been hydrolyzed to a partially hydrolyzed silane or a mixture of unhydrolyzed and partially hydrolyzed silanes.

Claim 21

The method of claim 2 or 16 wherein the unhydrolyzed, partially hydrolyzed or mixture of unhydrolyzed and partially hydrolyzed amino-silane is combined with the polyester resin having free carboxyl functionality wherein the polyester resin has less than 90 percent water.

Claim 22

The emulsion of claim 1 wherein the polyester resin is in bulk form and is melted before the addition of the amino-functional silane.

Claim 23

The method of claim 2 wherein the polyester resin with free carboxyl or acid, saturated dicarboxylic acid and polyhydric alcohol.

Claim 24

The method of claim 2 wherein the amino-functional silane is a gamma-aminopropyltriethoxy silane.

Claim 25

Glass fiber strands treated with the sizing composition made by the method of claim 13.

Claim 26

Emulsion of claim 15 wherein the amino-silane is partially hydrolyzed more than unhydrolyzed and the polyester resin with free carboxyl functionality is present in aqueous solution at a concentration of at least 30 weight percent solids.

Claim 27

Method of claim 16 wherein the partially hydrolyzed or mixture of unhydrolyzed and partially hydrolyzed silane results from the combining of gamma-aminopropyltriethoxysilane to the polyester resin with less than 90 percent water.

Claim 28

The sizing composition of claim 14 or 19 wherein the unhydrolyzed or partially hydrolyzed amino-functional silane is combined with the second unsaturated polyester resin having less than 90 percent water.

Claim 29

A polymer acid-base salt interaction product of a polyester polymer having free carboxyl functionality and having unsaturation and of an unhydrolyzed, amino-silane is prepared by: combining the unhydrolyzed amino-functional silane with the polyester resin having free carboxyl groups in the presence of less than 90 percent water at a temperature in the range of about 18° C. to about 50° C. and at atmospheric pressure.

Claim 30

A polymer acid-base salt interaction product of a polyester polymer having free carboxyl functionality and having unsaturation and of an unhydrolyzed, amino-silane is prepared by: combining the unhydrolyzed amino-functional silane with the polyester resin having free carboxyl groups in the presence of less than 90 percent water at a temperature in the range of about 18° C. to about 50° C. and at atmospheric pressure.

Claim 31

The polymer acid-base salt interaction product of claim 26 wherein the unhydrolyzed amino-functional silane is partially hydrolyzed to partially hydrolyzed amino-silane or mixture of unhydrolyzed and partially hydrolyzed amino-silane and where said amino-functional silane is combined with the polyester resin with free carboxyl functionality that is present in aqueous solution at a concentration of at least 30 weight percent solids.

Claim 32

A polymer acid-base salt interaction product of a polyester polymer having free carboxyl functionality and having unsaturation, and of an unhydrolyzed, partially hydrolyzed amino-silane or mixture thereof prepared by: (a) melting the polyester polymer with free carboxyl functionality, and (b) combining the melted polymer with unhydrolyzed or partially hydrolyzed amino-silane or mixture thereof at a temperature in the range of about 18° C. to about 50° C. and at atmospheric pressure.

Claim 33

A polymer acid-base salt interaction product of a polyester polymer having free carboxyl functionality and having unsaturation, and of an unhydrolyzed, partially hydrolyzed amino-silane or mixture thereof prepared by: (a) melting the polyester polymer with free carboxyl functionality, and (b) combining the melted polymer with unhydrolyzed or partially hydrolyzed amino-silane or mixture thereof at a temperature in the range of about 18° C. to about 50° C. and at atmospheric pressure.

Claim 34

Sizing composition in accordance with claim 14 which includes a second silane coupling agent having a reactive moiety that is free radically polymerizable.

Claim 35

Sizing composition of claim 29 wherein the second silane coupling agent is gamma-methacryloxypropyltriethoxysilane.

Claim 36

Emulsion of claim 1 wherein the polyester resin is a combination of two polyester resins, one having pendant carboxyl functionality and the other having terminal carboxyl functionality.

Claim 39

Method of claim 32 wherein the polyester resin with free carboxyl functionality is prepared from a trimellitic acid or anhydride.

Claim 40

Method of preparing a more stable aqueous sizing composition that contains two unsaturated polyester resins, the first unsaturated polyester resin having pendant carboxyl groups and the second unsaturated polyester resin having terminal carboxyl groups and an amino silane, comprising: a. combining the amino silane in a state of unhydrolyzation, partial hydrolyzation, or mixture thereof with the second unsaturated polyester resin in the presence of less than 90 percent water, to produce an acid-base salt reaction product between the unhydrolyzed and/or partially hydrolyzed amino silane and carboxyl functionality of the polyester, b. adding a plasticizer and emulsifier and water to the mixture of step (a); c. adding the first unsaturated polyester resin with pendant carboxyl groups to the emulsion to produce an acid-base salt reaction product with the unhydrolyzed and/or partially hydrolyzed amino silane in the emulsion, d. hydrolyzing a vinyl-containing silane coupling agent with acetic acid and adding to the emulsion, e. diluting a thermoplastic polymeric additive in water and adding to the emulsion, and f. diluting the mixture to the desired solids in the range of about 5 to about 17 weight percent.

Claim 41

Method of preparing a more stable aqueous sizing composition that contains two unsaturated polyester resins, the first unsaturated polyester resin having pendant carboxyl groups and the second unsaturated polyester resin having terminal carboxyl groups and an amino silane, comprising: a. combining the amino silane in a state of unhydrolyzation, partial hydrolyzation, or mixture thereof with the second unsaturated polyester resin in the presence of less than 90 percent water, to produce an acid-base salt reaction product between the unhydrolyzed and/or partially hydrolyzed amino silane and carboxyl functionality of the polyester, b. adding a plasticizer and emulsifier and water to the mixture of step (a); c. adding the first unsaturated polyester resin with pendant carboxyl groups to the emulsion to produce an acid-base salt reaction product with the unhydrolyzed and/or partially hydrolyzed amino silane in the emulsion, d. hydrolyzing a vinyl-containing silane coupling agent with acetic acid and adding to the emulsion, e. diluting a thermoplastic polymeric additive in water and adding to the emulsion, and f. diluting the mixture to the desired solids in the range of about 5 to about 17 weight percent.

Claim 42

Method of claims 32 or 34 wherein a portion of the amine silane that is unhydrolyzed, partially hydrolyzed, or a mixture of unhydrolyzed and partially hydrolyzed is added to the first unsaturated polyester resin with pendant carboxyl groups while the other portion is added to the second unsaturated polyester resin with terminal carboxyl groups.

Claim 43

Method according to claims 9 or 16 wherein the amino-functional silane selected from the group consisting of unhydrolyzed or partially hydrolyzed or a mixture of partially hydrolyzed and unhydrolyzed amino silane is added to the polyester resin having terminal carboxyl functionality, and the combination is combined with the polyester resin having pendant carboxyl functionality.

Claim 44

Method according to claims 9 or 16 wherein the amino-functional silane selected from the group consisting of unhydrolyzed, partially hydrolyzed or a mixture of unhydrolyzed and partially hydrolyzed amino-functional silane is added to the polyester resin with pendant carboxyl functionality, and the combination is combined with the polyester resin having terminal carboxyl functionality.

Claim 45

The method of claim 2 wherein the polyester resin is in bulk form and is melted before the addition of the aminofunctional silane.

Claim 46

The sizing composition of claim 14 wherein the polyester resin with free carboxyl functionality is prepared with trimellitic acid or anhydride, maleic anhydride or acid, saturated dicarboxylic acid and polyhydric alcohol.

Claim 47

Sizing composition of claim 14 wherein the amino-functional silane is a gamma-aminopropyltriethoxy silane.

Claim 48

Glass fiber strands treated with the sizing composition of claim 14.

Claim 49

Method of claim 16 wherein the amino silane is partially hydrolyzed more than unhydrolyzed and the polyester resin with free carboxyl functionality is present in aqueous solution at a concentration of at least 30 weight percent solids.

Claim 50

The emulsion of claim 1 wherein the polyester resin having carboxyl functionality is a polyester resin with terminal carboxyl functionality.

Claim 51

Emulsion of claim 1 wherein the polyester resin with carboxyl functionality is a polyester resin having pendant carboxyl functionality.

Claim 52

Emulsion of claim 1 wherein the polyester resin with carboxyl functionality is a polyester resin having pendant and terminal carboxyl functionality.